Aluminum alloy plate for battery lid for forming integral explosion-proof valve and method for producing same

A technology of aluminum alloy plate and manufacturing method, which is applied in the direction of battery cover/end cover, metal rolling, lithium battery, etc., can solve the problem of valve automatic fracture, etc., achieve small working pressure deviation, excellent resistance to repeated fatigue, and softening during processing excellent effect

Inactive Publication Date: 2020-05-29
NIPPON LIGHT METAL CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The explosion-proof valve must work reliably, and the valve will automatically break when the internal pressure of the container exceeds the specified pressure, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy plate for battery lid for forming integral explosion-proof valve and method for producing same
  • Aluminum alloy plate for battery lid for forming integral explosion-proof valve and method for producing same
  • Aluminum alloy plate for battery lid for forming integral explosion-proof valve and method for producing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0104]

[0105] 〔Preparation of test materials〕

[0106] 5 kg of ingots with component compositions of 16 levels (Examples 1-6, Comparative Examples 1-10) were inserted into No. 20 crucibles, and the crucibles were heated in a small electric furnace to melt the ingots. Next, insert a spray gun into the melt, and feed N at a flow rate of 1.0 L / min. 2 The gas was degassed for 5 minutes. Thereafter, it was allowed to rest for 30 minutes, and dross floating to the surface of the melt was removed with a stirring bar. Then, the crucible was taken out from the small electric furnace, the melt was poured into a mold with an inner size of 250×200×30 mm to make an ingot, and the melts of Examples 1 to 6 and Comparative Examples 1 to 10 were obtained from the melt in each crucible. Each test material. The disc samples of these test materials were analyzed for composition by emission spectroscopic analysis. The results are shown in Table 1.

[0107] [Table 1]

[0108]

[0109] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention provide an aluminum alloy plate for a battery lid that is excellent in heat dissipation property, formability and work-softening property, and allows for forming of an integral explosion-proof valve having less variations in working pressures and being excellent in characteristics of resistance to repeated fatigue, and a method for producing the aluminum alloy plate for a battery lid. The aluminum alloy plate for battery lid for forming an integral explosion-proof valve has a component composition containing Fe:1.05-1.50 mass%, Mn:0.15-0.70 mass%, Ti:0.002-0.10 mass% and B: lessthan 0.03 mass%, and the balance Al with impurities; with Fe / Mn ratio controlled to 1.8-7.0; Si controlled to less than 0.40 mass%; Cu controlled to less than 0.03 mass%, Mg controlled to less than 0.05 mass% and V controlled to less than 0.03 mass% as impurities, has a conductivity of 53.0% IACS or more and a value of elongation of 40% or more, has a re-crystallized structure, has a value of (TS95-TS70) of less than -1 MPa when TS70 denotes a tensile strength of the aluminum alloy plate for battery lid for forming an integral explosion-proof valve after being cold-rolled at a reduction of 70%and TS95 denotes the tensile strength after being cold-rolled at a reduction of 95%, and has a value of elongation after being cold-rolled at a reduction of 90% of 5.0% or more. Furthermore, an average crystal particle size of re-crystallized particles of the re-crystallized structure is preferably 15-30 [mu]m.

Description

technical field [0001] The present invention relates to an aluminum alloy plate for a battery cover for forming an integrated explosion-proof valve used in square, cylindrical and other lithium-ion batteries and having a small working pressure deviation. Background technique [0002] In recent years, countries have imposed stricter regulations on automobile exhaust, and the production of electric vehicles, which are environmentally friendly vehicles, is rapidly expanding. Currently, the mainstream of secondary batteries used in electric vehicles is lithium-ion batteries. Lithium-ion battery casings come in various types such as square, cylindrical, and sheet-shaped. In the case of square and cylindrical shapes, aluminum alloy plates that can achieve weight reduction are drawn and processed. Or a shell obtained by thinning and deep drawing processing (also called DI processing). [0003] Thus, as a material for a battery case, development of an aluminum alloy plate having e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C22F1/04H01M2/04H01M2/12C22F1/00H01M50/147
CPCC22F1/04C22C21/00Y02E60/10C21D8/0226C21D8/0236C21D8/0273C21D1/26H01M50/159H01M50/3425H01M10/052B22D11/049B22D11/1206B22D11/1213H01M50/147B21B1/38B21B3/00B21B37/58B21B2003/001
Inventor 玉置雄一金森圭治下坂大辅穴见敏也
Owner NIPPON LIGHT METAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com