A kind of high plasticity light alloy for three-dimensional printing and preparation method thereof

A technology of 3D printing and high plasticity, which is applied in the field of 3D printing materials, can solve the problems of increasing impurities, long process and limitation, etc., and achieve excellent plasticity and heat resistance, fine grain structure and good heat resistance.

Active Publication Date: 2021-06-25
苏州轻金三维科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

3D printing technology originated from the photographic sculpture and landform forming technology researched in the United States at the end of the 19th century, but limited by the technical conditions at that time, no breakthroughs were made.
The whole preparation process is long, energy consumption is high, impurities are easy to increase, and the utilization rate of materials is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] This embodiment relates to a high-plasticity Mg-Zn-Er-Nd-Mn-Zr magnesium alloy material, which includes the following components in weight percentage: 1wt.%Zn, 7wt.%Er, 0.2wt. %Nd, 2wt.%Mn, 0.1wt.%Zr, the balance is Mg and unavoidable impurities. Mg-1Zn-7Er-0.2Nd-2Mn-0.1Zr magnesium alloy is not combined with raw materials (pure magnesium, pure zinc, Mg-Er master alloy, Mg-Nd master alloy, Mg-Mn master alloy, Mg-Zr master alloy) The traditional smelting process is used to prepare, but the following steps are followed in turn:

[0018] (1) Use the mechanical grinding process to make the raw materials pure magnesium, pure zinc, Mg-Er master alloy, Mg-Nd master alloy, Mg-Mn master alloy, Mg-Zr master alloy into spherical powder, particle size 30~140μm, containing Oxygen content 0.06~0.18.

[0019] (2) According to the specific content of each element of the Mg-1Zn-7Er-0.2Nd-2Mn-0.1Zr magnesium alloy, weigh various raw material powders, put the taken powders into a powder...

Embodiment 2

[0027] This embodiment relates to a high-plasticity Mg-Zn-Er-Nd-Mn-Zr magnesium alloy material, which includes the following components in weight percentage: 8wt.%Zn, 1wt.%Er, 5wt.% Nd, 0.2wt.%Mn, 1wt.%Zr, the balance is Mg and unavoidable impurities. Mg-8Zn-1Er-5Nd-0.2Mn-1Zr magnesium alloy is not made of raw materials (pure magnesium, pure zinc, Mg-Er master alloy, Mg-Nd master alloy, Mg-Mn master alloy, Mg-Zr master alloy) combined with traditional The smelting process is prepared, but in turn follow the following steps:

[0028] (1) Use the mechanical grinding process to make the raw materials pure magnesium, pure zinc, Mg-Er master alloy, Mg-Nd master alloy, Mg-Mn master alloy, Mg-Zr master alloy into spherical powder, particle size 30~140μm, containing Oxygen content 0.06~0.18.

[0029] (2) According to the specific content of each element of the Mg-8Zn-1Er-5Nd-0.2Mn-1Zr magnesium alloy, weigh various raw material powders, put the taken powders into a powder mixer and ...

Embodiment 3

[0037] This embodiment relates to a high-plasticity Mg-Zn-Er-Nd-Mn-Zr magnesium alloy material, which includes the following components in weight percentage: 4.5wt.%Zn, 4wt.%Er, 2.5wt .%Nd, 1wt.%Mn, 0.5wt.%Zr, the balance is Mg and unavoidable impurities. Mg-4.5Zn-4Er-2.5Nd-1Mn-0.5Zr magnesium alloy is not a raw material (pure magnesium, pure zinc, Mg-Er master alloy, Mg-Nd master alloy, Mg-Mn master alloy, Mg-Zr master alloy) Combined with the traditional smelting process for preparation, but follow the following steps in sequence:

[0038](1) Use the mechanical grinding process to make the raw materials pure magnesium, pure zinc, Mg-Er master alloy, Mg-Nd master alloy, Mg-Mn master alloy, Mg-Zr master alloy into spherical powder, particle size 30~140μm, containing Oxygen content 0.06~0.18.

[0039] (2) According to the specific content of each element of the Mg-4.5Zn-4Er-2.5Nd-1Mn-0.5Zr magnesium alloy, weigh various raw material powders, put the taken powders into a powde...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-plastic light alloy for three-dimensional printing and a preparation method thereof. The mass percentages of the components of the alloy are: 1-8wt.%Zn, 1-7wt.%Er, 0.2-5wt.%Nd, 0.2~2wt.%Mn, 0.1~1wt.%Zr, the balance is Mg and unavoidable impurities. The preparation method is as follows: after designing the composition, the raw materials are made into spherical powder, and the metal powder is fully mixed, the mixed raw material powder is sintered and solid solution heat treated, and then the light alloy spherical powder is obtained through mechanical grinding and alloying. The finished product obtained by three-dimensional printing has the advantages of high plasticity, light weight, good heat resistance and wear resistance under the premise of maintaining high strength.

Description

technical field [0001] The invention belongs to the technical field of 3D printing materials, and in particular relates to a high plasticity light alloy for 3D printing and a preparation method thereof. Background technique [0002] 3D printing technology, also known as additive manufacturing according to its manufacturing process, belongs to a kind of rapid prototyping technology. It uses powdered metal or plastic and other bondable materials, and finally prints directly Produce products and form "digital manufacturing". 3D printing technology originated from the photographic sculpture and landform forming technology researched in the United States at the end of the 19th century, but limited by the technical conditions at that time, no breakthroughs were made. In the 1980s, with the vigorous development of computer technology and new material technology, 3D printing technology has made great progress, but its commercialization and marketization process is slow. In the 21s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C23/06C22C23/04C22C1/04C22F1/06B22F1/00B33Y70/00
CPCB22F1/00B33Y70/00C22C1/04C22C23/04C22C23/06C22F1/06
Inventor 刘文才李俊锋
Owner 苏州轻金三维科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com