High-temperature-resistant and corrosion-resistant conveying belt and preparation method thereof

A corrosion-resistant, conveyor belt technology, applied in building insulation materials, building components, buildings, etc., can solve problems such as secondary disasters of life and property, corrosion of equipment and instruments, and obstruction of disaster relief work, achieving remarkable corrosion resistance and high production efficiency and the effect of high yield and low manufacturing cost

Pending Publication Date: 2020-05-15
浙江环能传动科技有限公司
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

One is to hinder the smooth progress of disaster relief work, causing secondary disasters to life and property, the other is to corrode equipment and instruments, and the third is to cause environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant and corrosion-resistant conveying belt and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A high-temperature-resistant and corrosion-resistant conveyor belt, characterized in that, the formulation of the preparation material for the high-temperature-resistant and corrosion-resistant conveyor belt includes the following components in parts by weight: 15 parts of fluorinated phosphazene rubber, 100 parts of EPDM rubber, 5 parts of polyisoprene, 3,3-diphenylacrylonitrile / [2-(triethoxysilyl)ethyl]vinyl ether / allyl 1H,1H-heptafluorobutyl ether / propylene 10 parts of adamantyl triazine copolymer, 10 parts of black phosphorene, 1 part of asphalt powder, 10 parts of zircon powder, 1 part of silane coupling agent KH5501, 1 part of diisopropyl peroxydicarbonate, 0.5 parts of vulcanizing agent DTDM share.

[0028]The 3,3-diphenylacrylonitrile / [2-(triethoxysilyl)ethyl]vinyl ether / allyl 1H,1H-heptafluorobutyl ether / acryl adamantyl triazine The preparation method of the copolymer comprises the following steps: 10 g of 3,3-diphenylacrylonitrile, 20 g of [2-(triethoxysilyl)...

Embodiment 2

[0034] A high-temperature-resistant and corrosion-resistant conveyor belt, characterized in that, the formula for the preparation material of the high-temperature-resistant and corrosion-resistant conveyor belt includes the following components in parts by weight: 17 parts of fluorinated phosphazene rubber, 100 parts of EPDM rubber, 6 parts of polyisoprene, 3,3-diphenylacrylonitrile / [2-(triethoxysilyl)ethyl]vinyl ether / allyl 1H,1H-heptafluorobutyl ether / propylene 11 parts of adamantyl triazine copolymer, 12 parts of black phosphorene, 2 parts of asphalt powder, 12 parts of zircon powder, 1.5 parts of silane coupling agent KH560, 1.2 parts of cyclohexanone peroxide, 0.7 parts of vulcanizing agent DTDM .

[0035] The 3,3-diphenylacrylonitrile / [2-(triethoxysilyl)ethyl]vinyl ether / allyl 1H,1H-heptafluorobutyl ether / acryl adamantyl triazine The preparation method of the copolymer comprises the following steps: 10 g of 3,3-diphenylacrylonitrile, 20 g of [2-(triethoxysilyl) ethyl] v...

Embodiment 3

[0041] A high-temperature-resistant and corrosion-resistant conveyor belt, characterized in that, the formulation of the high-temperature-resistant and corrosion-resistant conveyor belt preparation material includes the following components in parts by weight: 20 parts of fluorinated phosphazene rubber, 100 parts of EPDM rubber, 8 parts of polyisoprene, 3,3-diphenylacrylonitrile / [2-(triethoxysilyl)ethyl]vinyl ether / allyl 1H,1H-heptafluorobutyl ether / propylene 13 parts of adamantyl triazine copolymer, 15 parts of black phosphorene, 2.5 parts of pitch powder, 15 parts of zircon powder, 2 parts of silane coupling agent KH5702, 1.5 parts of tert-butyl peroxy tert-valerate, vulcanizing agent DTDM 1 serving.

[0042] The 3,3-diphenylacrylonitrile / [2-(triethoxysilyl)ethyl]vinyl ether / allyl 1H,1H-heptafluorobutyl ether / acryl adamantyl triazine The preparation method of the copolymer comprises the following steps: 10 g of 3,3-diphenylacrylonitrile, 20 g of [2-(triethoxysilyl) ethyl] v...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-temperature-resistant and corrosion-resistant conveying belt. The high-temperature-resistant and corrosion-resistant conveyor belt is prepared from, by weight, 15-25 parts of fluorinated phosphazene rubber, 100 parts of ethylene-propylene-diene monomer rubber, 5-10 parts of polyisoprene, 10-15 parts of 3,3-diphenylacrylonitrile / [2-(triethoxysilyl)ethyl]vinyl ether / allyl 1H,1H-heptafluorobutyl ether / propenyl adamantyl triazine copolymer, 10-20 parts of black phosphorene, 1-4 parts of asphalt powder, 10-20 parts of zircon powder, 1-3 parts of a coupling agent, 1-2 parts of an initiator and 0.5-1.5 parts of a vulcanizing agent DTDM. The invention further provides a preparation method of the high-temperature-resistant and corrosion-resistant conveying belt. The high-temperature-resistant and corrosion-resistant conveying belt is excellent in high-temperature resistance, flame retardance and wear resistance, remarkable in corrosion resistance effect, good in fatigue resistance, impact resistance and aging resistance, high in mechanical strength, good in performance stability, long in service life, safe during combustion and environmentally friendly.

Description

technical field [0001] The invention relates to the technical field of conveyor belts, in particular to a high-temperature and corrosion-resistant conveyor belt and a preparation method thereof. Background technique [0002] In recent years, with the rapid development of my country's economy and the acceleration of urban modernization, various construction projects have sprung up like mushrooms. They have brought new business cards to the city and become a symbol of modern civilization. Behind this large-scale construction project is inseparable from the extensive use of construction materials such as steel and cement. The continuous expansion of market demand has prompted the rapid increase of the production scale and production capacity of the steel and cement industries. At the same time, this also puts forward higher requirements for the key components of material transportation in the production of steel and cement industries - conveyor belts. [0003] Conveyor belt is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/16C08L85/02C08L9/00C08L95/00C08L29/10C08K13/02C08K3/02C08K3/22C08K3/36
CPCC08K2003/026C08K2003/2244C08L23/16C08L2201/02C08L2201/08C08L2205/035C08L2205/05C08L85/02C08L9/00C08L95/00C08L29/10C08K13/02C08K3/02C08K3/22C08K3/36
Inventor 许小虎王启超王如兴
Owner 浙江环能传动科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com