A microfiber functionalized filter rod tow with functions of carrying fragrance and selectively reducing phenol content in smoke, and its preparation and application

An ultra-fine fiber and selective technology, applied in applications, e-liquid filter elements, tobacco, etc., can solve the problems of harm reduction, increase the production process and cost, and poor selectivity, so as to reduce the release of phenol and highlight the effect of selectivity reduction , the effect of unique fragrance

Active Publication Date: 2022-03-11
CHINA TOBACCO HUNAN INDAL CORP
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent (application number CN201110194289.1) discloses a hydrophilic ultrafine SiO 2 Particles modified by trimethylchlorosilane to obtain hydrophobic ultrafine SiO 2 particles, and add them to shredded tobacco, reconstituted tobacco leaves or shredded stems to reduce phenol in smoke, but this method will affect the combustion performance of cigarettes because it is added in the combustion section of cigarettes
Chinese patent (application number CN201110241462.9) discloses a microporous structure of ultrafine SiO 2 Ultrafine SiO with particle and surface hydrophobicity 2 Composite ultrafine SiO 2 Particles, added in the filter to reduce smoke phenol, but its selectivity is poor, and it needs to be prepared into a binary composite filter rod to achieve the harm reduction effect, which increases the preparation process and cost
[0006] Polyvinylpyrrolidone is a common high-molecular polymer in the prior art. At present, it is mainly used as an adhesive and a surfactant, and there is no relevant application of it as a harm-reducing functional material for cigarette filters. to report

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A microfiber functionalized filter rod tow with functions of carrying fragrance and selectively reducing phenol content in smoke, and its preparation and application
  • A microfiber functionalized filter rod tow with functions of carrying fragrance and selectively reducing phenol content in smoke, and its preparation and application
  • A microfiber functionalized filter rod tow with functions of carrying fragrance and selectively reducing phenol content in smoke, and its preparation and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Preparation of electrospun microfiber functional tow with fragrance carrying ability

[0041] Electrospinning is performed in an electrospinning chamber. Mix polyvinylpyrrolidone K30 and smoked extract at a mass ratio of 80:20 to form a spinnable fabric, then mix the spinnable fabric with solvent water at a mass ratio of 15:85, and continuously stir for 5 hours in a constant temperature water bath at 50°C to obtain The uniform spinnable solution is placed in the storage tank, and the material liquid is supplied to 80 electrospinning nozzles at a speed of 3mL / h through a micropump. The electrospinning voltage is 15KV, and the distance between the nozzle and the paper base is 10cm , the electrospinning ambient temperature is 28°C, each group of electrospinning nozzles has 20 nozzles, each group of nozzles forms a circuit, and each group of nozzles rotates continuously in the circuit at a constant speed, so that the electrospinning is uniform on the receiving substrate. O...

Embodiment 2

[0045] Preparation of electrospun microfiber functional tow with fragrance carrying ability

[0046] Electrospinning was performed in the electrospinning chamber in Example 1. The spinning equipment is the same as in Example 1.

[0047] Mix polyvinylpyrrolidone K60 and smoked extract at a mass ratio of 70:30 to form a spinnable fabric, then mix the spinnable fabric with solvent water at a mass ratio of 15:85, and continuously stir for 5 hours in a constant temperature water bath at 50°C to obtain Uniform spinnable solution, at room temperature, using 20KV voltage and 10cm receiving distance, spinning solution advancing speed 3ml / h, on the tow to prepare ultra-fine fibers with a diameter of about 940nm with fragrance-carrying ability, ultra-fine fibers on the silk The amount of spraying on the beam substrate is about 1.0g / m 2 ..

[0048] Functional tow filter rod and cigarette preparation and smoke analysis:

[0049] Replace the original tow on the filter rod forming machin...

Embodiment 3

[0051] Preparation of electrospun microfiber functional tow with fragrance carrying ability

[0052] Electrospinning was performed in the electrospinning chamber in Example 1. The spinning equipment is the same as in Example 1.

[0053] Mix polyvinylpyrrolidone K90 and green tea extract at a mass ratio of 60:40 to form a spinnable fabric, then mix the spinnable fabric with solvent water at a mass ratio of 20:80, and stir continuously for 5 hours in a constant temperature water bath at 50°C to obtain a uniform Spinnable solution, at room temperature, using 25KV voltage and 15cm receiving distance, spinning solution advancing speed 3.2ml / h, on the tow to prepare ultra-fine fibers with a diameter of about 800nm ​​with fragrance-carrying ability, the ultra-fine fibers are on the silk The amount of spraying on the bundle substrate is about 1.2g / m 2 ..

[0054] Functional tow filter rod and cigarette preparation and smoke analysis:

[0055] Replace the original tow on the filter...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a superfine fiber functionalized filter rod tow with the functions of carrying fragrance and selectively reducing the phenol content of smoke and its preparation and application. The superfine fiber functionalized filter rod tow is composed of a tow base material and its The aroma substances on the surface are doped with polyvinylpyrrolidone micro-nano ultra-fine fiber membrane layer, and the ultra-fine fiber functionalized filter rod tow is made into a cigarette filter rod, which has a significant selective reduction effect on phenol in smoke, and smoke The harmful component phenol in the gas can be reduced by 13-35%, while the tar in the flue gas has basically no significant change, which highlights the selective reduction effect on the phenol in the flue gas, and gives the flue gas a unique aroma.

Description

technical field [0001] The invention relates to a functional filter rod tow, in particular to an ultra-fine fiber functionalized filter rod tow with the functions of carrying fragrance and selectively reducing the phenol content of smoke, and also relates to an ultrafine fiber filter rod tow prepared by an electrospinning process. The method for fiber functionalized filter rod tow and the application of superfine fiber functionalized filter rod tow in preparing cigarette filter rods with functions of aromatization and selective reduction of smoke phenol content belong to the field of tobacco filter material application. Background technique [0002] In the tobacco industry, traditionally reducing the release of harmful components in smoke is achieved by reducing the release of mainstream smoke tar, but when the mainstream smoke tar of cigarettes is reduced to a certain level, the smoking flavor of cigarettes will be greatly affected This is one of the important factors restr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A24D3/02A24D3/04A24D3/10
CPCA24D3/02A24D3/04A24D3/10
Inventor 谢兰英刘琦金勇练文柳
Owner CHINA TOBACCO HUNAN INDAL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com