A kind of intelligent preparation method of compacted graphite cast iron brake drum

A technology of intelligent preparation and vermicular graphite cast iron, which is applied in casting molding equipment, casting molds, casting mold components, etc., can solve the problems of large brake drum volume, easy entry of impurities, low efficiency, etc., and achieves good electromagnetic stirring effect. The effect of convenient starting operation and convenient replacement of steel grades

Active Publication Date: 2021-06-01
山东时风(集团)有限责任公司 +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the relatively large volume of the brake drum, more molten iron is consumed, so the whole process takes a long time, the efficiency is not high, and the energy consumption is relatively high.
[0008] 2. The quality of the casting model is not considered in the whole process, the surface of the casting brake drum is not smooth, and the brake drum made of vermicular graphite cast iron is difficult to polish, which increases the processing cost
[0009] 3. 7.5-8.5% RE is used in the vermicular agent, and the amount of rare earth used is large, resulting in high production cost, which limits its application in ordinary occasions
[0010] 4. The materials used in the process are pig iron, steel and other materials, which are not suitable for occasions where scrap steel, recycled materials and other raw materials are used
[0011] 5. During vermicularization, the remaining impurities after the reaction of the vermative agent are easy to enter the molten iron, which will have a certain impact on the quality of the pouring, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of intelligent preparation method of compacted graphite cast iron brake drum
  • A kind of intelligent preparation method of compacted graphite cast iron brake drum
  • A kind of intelligent preparation method of compacted graphite cast iron brake drum

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] Example 1. An intelligent preparation method for a vermicular graphite cast iron brake drum, comprising the steps of:

[0052] Step 1: Prepare 30kg of steel scrap and 50kg of recycled material for every 100kg of pig iron according to the weight ratio, and put part of the pig iron, all of the scrap steel, and all of the recycled material into a low-frequency induction furnace for melting.

[0053] Step 2: Add carburant, control the amount of carburant added, so that the carbon content of the solution is: 3.6%; wherein the carbon equivalent needs to be kept at 4.07%, and the carbon equivalent=mass percentage of carbon+(mass percentage of silicon / 3); remove the slag, spare.

[0054] Step 3: Lay a layer of ferrosilicon on the bottom of the intermediate frequency induction furnace to form a ferrosilicon layer, then add some pig iron to form a pig iron layer, raise the temperature, add a part of electrolytic copper and ferromanganese before the added ferrosilicon and pig ir...

Embodiment 2

[0068] Example 2. The difference between this embodiment and Embodiment 1 is that an intelligent preparation method of a vermicular graphite cast iron brake drum includes the following steps:

[0069] Step 1: Prepare 25kg of steel scrap and 45kg of recycled material for every 100kg of pig iron according to the weight ratio, and put part of the pig iron, all of the scrap steel, and all of the recycled material into a low-frequency induction furnace for melting.

[0070] Step 2: add carburant, control the amount of carburant added, so that the carbon content of the solution is: 3.7%; wherein the carbon equivalent needs to be kept at 4.2%, and the carbon equivalent=mass percentage of carbon+(mass percentage of silicon / 3); remove the slag, spare.

[0071] Step 3: Lay a layer of ferrosilicon on the bottom of the intermediate frequency induction furnace to form a ferrosilicon layer, then add some pig iron to form a pig iron layer, raise the temperature, add a part of electrolytic ...

Embodiment 3

[0086] Example 3. The difference between this embodiment and Embodiment 1 is that an intelligent preparation method of a vermicular graphite cast iron brake drum includes the following steps:

[0087] Step 1: Prepare 25kg of steel scrap and 40kg of recycled material for every 100kg of pig iron according to the weight ratio, and put part of the pig iron, all of the scrap steel, and all of the recycled material into a low-frequency induction furnace for melting.

[0088] Step 2: Add carburant, control the amount of carburant added, so that the carbon content of the solution is: 3.71%; wherein the carbon equivalent needs to be kept at 4.28%, and the carbon equivalent=mass percentage of carbon+(mass percentage of silicon / 3); remove the slag, spare.

[0089] Step 3: Lay a layer of ferrosilicon on the bottom of the intermediate frequency induction furnace to form a ferrosilicon layer, then add some pig iron to form a pig iron layer, raise the temperature, add a part of electrolyti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heightaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an intelligent preparation method of vermicular graphite cast iron brake drum, which includes: adding part of pig iron, scrap steel and returned materials to a low-frequency induction furnace to melt, controlling the amount of carburant added; laying a layer on the bottom of the medium-frequency induction furnace Ferrosilicon forms a ferrosilicon layer, and then adds part of pig iron to form a pig iron layer. When the temperature rises, before the added ferrosilicon and pig iron are completely melted, add a part of electrolytic copper and ferromanganese; The center of the top is poured into the low-frequency induction furnace solution; the medium-frequency induction furnace solution is vermigrated in the vermicular ladle; pouring. The invention has the characteristics of fast production speed of the brake drum, good quality of the brake drum and low cost.

Description

technical field [0001] The invention relates to the field of brake drums, in particular to a method for manufacturing a brake drum. Background technique [0002] The brake drum is the main braking element in the axle braking system. When the car is braking, the braking force is generated by the friction between the brake pads and the inner wall of the brake drum. The friction between the inner wall of the brake drum and the brake pads produces the braking effect. During the friction process, heat will be generated. During the friction process and after the friction is stopped, different parts of the brake drum will also alternate between cold and heat. The moving drum has good wear resistance, thermal conductivity and thermal fatigue resistance. [0003] According to statistics, at present, brake drum cracking accounts for more than 80% of the failure cases, and the cracking is mainly caused by thermal fatigue cracks. Existing brake drums are generally made of gray cast i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C33/10C22C37/10B22C1/02B22C9/02B22C9/22B22D1/00C21C1/08
CPCB22C1/02B22C9/02B22C9/22B22D1/00C21C1/08C22C33/10C22C37/10Y02P10/20
Inventor 刘成强林连华徐海港纪昌勇于子岭张中凯林堂国许爱国李汝学刘兴明
Owner 山东时风(集团)有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com