Ancient architecture timber structure waterproof anticorrosive paint and preparation method thereof

A waterproof and anti-corrosion coating, wood structure technology, applied in anti-corrosion coatings, anti-fouling/underwater coatings, coatings, etc., can solve the problems of moisture and mold invasion, damage to ancient wooden buildings, etc. , the effect of increasing roughness and improving compactness

Inactive Publication Date: 2020-05-12
卢定华
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The main technical problem to be solved by the present invention is to provide a wooden structure waterproof and anti-corrosion coating for ancient buildings and its preparation method in view of the defects that the ancient wooden structures are easily attacked by moisture and molds and cause damage to the ancient wooden structures.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ancient architecture timber structure waterproof anticorrosive paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0044] (1) Preparation of self-made metal antifungal agent:

[0045] Mix ethyl orthosilicate, absolute ethanol and deionized water at a mass ratio of 3:5:10 and put them into a beaker, then move the beaker into a water bath, heat up to 50-60°C, and add Adjust the pH to 3-4 with hydrochloric acid, and stir for 30-40 minutes;

[0046] After the above stirring reaction is completed, continue to stir at 40-50°C, and slowly add copper chloride solution and orthosilicate solution with a concentration of 1mol / L 2 to 3 times the mass of ethyl orthosilicate to the beaker under stirring. 3-Aminopropyltriethoxysilane with 50% ethyl ester mass, continuously stirred and reacted for 3-5 hours to obtain a self-made metal antifungal agent;

[0047] (2) Preparation of pre-emulsion:

[0048] In parts by weight, weigh 10-12 parts of the above self-made metal antifungal agent, 10-15 parts of tetraethyl orthosilicate, 5-8 parts of propylene glycol, 15-16 parts of n-butanol and 1-2 parts of hard ...

example 1

[0056] (1) Preparation of self-made metal antifungal agent:

[0057] Mix tetraethyl orthosilicate, absolute ethanol and deionized water at a mass ratio of 3:5:10 and put them into a beaker, then move the beaker into a water bath, heat up to 50°C, and add hydrochloric acid to the beaker to adjust pH to 3, stirred for 30 minutes;

[0058] After the above-mentioned stirring reaction is completed, continue to stir at 40°C. Under stirring, slowly add into the beaker a cupric chloride solution with a concentration twice the mass of ethyl orthosilicate and a concentration of 1mol / L and 50% of the mass of ethyl orthosilicate. % of 3-aminopropyltriethoxysilane, continuous stirring reaction 3h, obtains self-made metal antifungal agent;

[0059] (2) Preparation of pre-emulsion:

[0060] In parts by weight, weigh 10 parts of the above self-made metal antifungal agent, 10 parts of tetraethyl orthosilicate, 5 parts of propylene dione, 15 parts of n-butanol and 1 part of stearic acid into ...

example 2

[0068] (1) Preparation of self-made metal antifungal agent:

[0069] Mix tetraethyl orthosilicate, absolute ethanol and deionized water at a mass ratio of 3:5:10 and put them into a beaker, then move the beaker into a water bath, heat up to 55°C, and add hydrochloric acid to the beaker to adjust pH to 3, stirred for 35 minutes;

[0070] After the above-mentioned stirring reaction is completed, continue to stir at 45°C. Under stirring, slowly add into the beaker a cupric chloride solution with a concentration twice the mass of tetraethyl orthosilicate and a concentration of 1mol / L and a mass of tetraethyl orthosilicate of 50 mol / L. % of 3-aminopropyltriethoxysilane, continuous stirring reaction 4h, obtains self-made metal antifungal agent;

[0071] (2) Preparation of pre-emulsion:

[0072] In parts by weight, weigh 11 parts of the above-mentioned self-made metal antifungal agent, 13 parts of tetraethyl orthosilicate, 6 parts of propylene dione, 15 parts of n-butanol and 1 par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to ancient architecture timber structure waterproof anticorrosive paint and a preparation method thereof, and belongs to the technical field of timber protection. A timber impregnating compound is prepared from a mixed solution of triethylamine trihydrogen fluoride and ammonium hexafluorophosphate; ionization ions in the mixed solution of triethylamine trihydrofluoride and ammonium hexafluorophosphate can penetrate into an amorphous region of wood fibers to access to the outer surface of a crystallization zone; by destroying hydrogen bond bonding between water and cellulose, swelling in a cellulose amorphous region occurs, which further facilitates permeation of the waterproof anticorrosive paint; meanwhile, tetraethoxysilane and copper ions are compounded to preparethe silica gel immobilized copper mildew preventive, and after the coating permeates into the wood, the silica gel can firmly fix metal copper ions in the timber structure material, the protective performance of the ancient architecture timber structure to mold is improved through the good mold resistance of the metal copper ions, and the waterproof performance of the ancient architecture timber structure is also remarkably improved after the paint is used. Therefore, the paint of the invention has wide application prospects.

Description

technical field [0001] The invention relates to a waterproof and anti-corrosion paint for wooden structures of ancient buildings and a preparation method thereof, belonging to the technical field of wood protection. Background technique [0002] China is a large land and sea country, with a coastline length of 18,000 kilometers, ranking fourth in the world; along the coastline of the mainland, there are many bays and port cities, from north to south: Dalian, Qinhuangdao, Tianjin, Yantai, Qingdao, Lianyungang, Nantong , Shanghai, Ningbo, Wenzhou, Fuzhou, Xiamen, Guangzhou, Zhanjiang, Beihai, etc. In these cities, there are wooden ancient building groups of different ages. They are the country's non-renewable and precious historical heritage, an important symbol of national civilization, and a precious wealth of the nation. Strong winds in these coastal cities will bring the salt spray in the sea to the land, forming a salt spray corrosive environment. [0003] Therefore, it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D1/00C09D5/14C09D7/61C09D7/63C09D4/00C09D5/08
CPCC09D1/00C09D4/00C09D5/08C09D5/14C09D7/61C09D7/63
Inventor 卢定华
Owner 卢定华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products