High-water-resistance primer for silane modified building sealant

A silane modification and sealant technology, applied in the field of materials, can solve the problems of poor water resistance and hydrolysis resistance, high polarity of silicone resin, poor compatibility, etc.

Active Publication Date: 2020-05-08
娄从江
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The Chinese invention patent with the application number of 2014108307412 discloses a primer for silane-modified polyether sealant and its preparation method, which can be directly coated on the substrate to be bonded, and then sizing on the surface of the substrate after a few minutes The process can enhance the bonding strength between the silane-modified polyether sealant and the substrate. Even if the substrate is soaked in water for a long time, the silane-modified polyether sealant is completely bonded to the substrate, but the silicone resin is extremely The primer has the disadvantages of poor low temperature flexibility and poor compatibility with silane-modified sealants
The Chinese patent with the publication number CN107474726 A discloses a primer, which has poor water resistance and hydrolysis resistance, especially the alkalinity of concrete after encountering water, which increases the risk of bonding failure in a long-term water environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-water-resistance primer for silane modified building sealant
  • High-water-resistance primer for silane modified building sealant
  • High-water-resistance primer for silane modified building sealant

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0086]

[0087]

[0088] Concrete selection and mass percent of each component in table 1 embodiment 1

[0089] In this embodiment 1, the silane-modified polymer (A) is a silane-terminated polybutadiene of formula I(a), that is, in the structural formula of formula I(a), m1=0, R 2 for -CH 2 CH 2 CH 2 -, p=0, R 4 for -CH3;

[0090] R in Formula III a , R b , R c , R d , R e and R f Both are H atoms, the range of x1+x2 is 10% to 60%, the range of x3 is 40% to 90%; x4=0; the unit structure of which the molar content is x3 – CH2-CH=CH-CH2-, has The following two isomeric forms:

[0091]

[0092] Specifically in the present embodiment, select the product of commercially available Evonik for use EP ST-M is a silane-modified polymer (A), which is trimethoxysiloxane-terminated polybutadiene with a number-average molecular weight of 3500 g / mol and an average functionality of siloxane of 6.9 to 7.2.

[0093] The cross-linking agent (B) has a polysiloxane polymer o...

Embodiment 2

[0098]

[0099] Concrete selection and mass percent of each component in table 2 embodiment 2

[0100] Same as in Example 1, the silane-modified polymer (A) is a silane-terminated polybutadiene of formula I(a) EP ST-M. 1146 is a commercial product of EVONIK, which is an oligomer copolymerized with aminosilane and alkylsilane, and is used as the silane coupling agent (C) in this embodiment.

[0101] The preparation steps are the same as in Example 1, and will not be repeated here.

Embodiment 3

[0103]

[0104]

[0105] Concrete selection and mass percent of each component in table 3 embodiment 3

[0106] In this embodiment 3, the silane-modified polymer (A) is a silane-modified polyisoprene of formula I(b), and the preparation method is: using hydroxyl-terminated isoprene (1,2 addition structure is Mainly, the molecular weight is 30000,) using hydroxyl-terminated polybutadiene (POLY R-15, commercially available from CRAY VALLEY in the United States, obtained by free radical polymerization, with a number average molecular weight of 2500 to 2800 mol / g, and an average hydroxyl group functionality of 2.2 to 2.6) was mixed at a mass ratio of 1:1 and heated to 110°C And vacuum stirring and dehydration for 2h, and cooling to room temperature, the mixture of the obtained hydroxyl-terminated polybutadiene and hydroxyl-terminated polyisoprene is used as a raw material, firstly mixed with TDI (toluene diisocyanate, commercially available Commercially available) was reac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Number average molecular weightaaaaaaaaaa
Number average molecular weightaaaaaaaaaa
Number average molecular weightaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-water-resistance primer for a silane modified building sealant, wherein the high-water-resistance primer comprises the following components in percentage by mass: 5-50%of an alkoxy modified polymer (A), 3-50% of a cross-linking agent (B), 0.5-10% of a silane coupling agent (C), 0-2% of a catalyst (D) and 10-90% of a solvent (E). According to the invention, the primer can be used for pretreating a porous base material bonded by a silane modified building sealant; and the primer is volatilized along with the solvent after being applied,, the primer is hydrolyzed and cross-linked by siloxane groups after curing in the presence of moisture, a film is formed on the bonding interface of the porous base material, the cured film-forming polymer contains a large number of non-polar main chain structures, the hydrolysis resistance is excellent, and the siloxane curing bonding point and the bonded sealant have excellent bonding compatibility, so that the bonding capability between the sealant and the base material can be improved, and the primer is suitable for most silane modified sealants sold in the market, such as modified silicone (MS), silane terminated polyurethane (SPU), silane terminated polyether (STPE) and the like.

Description

technical field [0001] The invention relates to a primer, in particular to a highly water-resistant primer used for silane-modified building sealants; it belongs to the field of material technology. Background technique [0002] Building sealant is an adhesive used to firmly stick different building materials together, and most of them have good viscosity. However, due to the wide range and diversity of bonding objects, as well as the uncertainty of use conditions, construction sealants need to use a primer (or primer liquid) to improve the bonding between the sealant and the substrate in actual use. The effect, and practice has also proved that in some bonding parts that require relatively high bonding effect, the use of primer can achieve satisfactory bonding strength and bonding stability. [0003] Both at home and abroad, they are committed to optimizing and improving the performance of primers. Adhesion promoter compositions as disclosed in PCT application WO2007 / 0352...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D147/00C09D183/04C09D115/00C09D7/63
CPCC09D5/002C09D115/00C09D147/00C09D183/04C09D7/63C08L83/04C08K5/544C08K5/5435C08L47/00
Inventor 娄从江
Owner 娄从江
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com