High-gloss, low-odor and flame-retardant PC material as well as preparation method and device thereof

A low-odor, high-gloss technology, applied in the field of material processing, can solve the problems of difficult cutting, damage to the dimensional integrity of pearlescent resin, affecting the gloss of composite materials, etc., to achieve the effect of improving gloss, retaining complete performance and increasing content.

Inactive Publication Date: 2020-05-05
重庆科聚孚新材料有限责任公司 +1
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, the present invention aims to solve the problem that traditional extruders prepare high-gloss materials through screw pushing and shearing extrusion processing, which will cause serious damage to the dimensional integrity of pearlescent resin and affect the gloss of composite materials, as well as feeding In the process, because the pearlescent resin cannot be uniformly dispersed, it is difficult to stably discharge the material. To provide a high-gloss, low-odor, flame-retardant PC material and its preparation method and device

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-gloss, low-odor and flame-retardant PC material as well as preparation method and device thereof
  • High-gloss, low-odor and flame-retardant PC material as well as preparation method and device thereof
  • High-gloss, low-odor and flame-retardant PC material as well as preparation method and device thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] like figure 1 Shown a kind of preparation method of high gloss, low smell, flame-retardant PC material, comprises the steps:

[0038] A. Weigh 98 parts of PC resin, 0.1 part of glass pearl powder, 0.1 part of polyether modified silicone oil, 1.0 part of adsorbent, 0.4 part of heat stabilizer (0.2 parts of antioxidant 1010 and 168) and 0.4 part of flame retardant Heavy standby;

[0039] B. Mix the PC resin, polyether modified silicone oil, heat stabilizer, and flame retardant according to the proportion and add them into the machine barrel. The mixture is first passed through the conveying section of the machine barrel through the screw. The screw speed is 400rpm, and the conveying section The temperatures in zone 1, zone 2 and zone 3 are 60°C, 130°C and 180°C respectively, and then the temperatures in zone 4, zone 5, zone 6 and zone 7 of the melting section entering the barrel are 190°C, 210°C, 220°C respectively ℃ and 230℃, after fully melted, carry out vacuum extrac...

Embodiment 2

[0043] A method for preparing a high-gloss, low-odor, flame-retardant PC material, comprising the steps of:

[0044] A. Weigh 97.3 parts of PC resin, 0.2 part of glass pearl powder, 0.1 part of polyether modified silicone oil, 1.0 part of adsorbent, 0.4 part of heat stabilizer (0.2 parts of antioxidant 1010 and 168) and 1.0 part of flame retardant Heavy standby;

[0045] B. Mix the PC resin, polyether modified silicone oil, heat stabilizer, and flame retardant according to the proportion and add them into the machine barrel. The mixture is first passed through the conveying section of the machine barrel through the screw. The screw speed is 400rpm, and the conveying section The temperatures in zone 1, zone 2 and zone 3 are 60°C, 130°C and 180°C respectively, and then the temperatures in zone 4, zone 5, zone 6 and zone 7 of the melting section entering the barrel are 190°C, 210°C, 220°C respectively ℃ and 230℃, after fully melted, carry out vacuum extraction through the vacuum...

Embodiment 3

[0049] A preparation method of high-gloss, low-odor, flame-retardant PC material, comprising the steps of:

[0050] A. 97.3 parts of PC resin, 0.2 part of synthetic pearl powder, 0.1 part of polyether modified silicone oil, 1.0 part of adsorbent, 0.4 part of heat stabilizer (0.2 parts of antioxidant 1010 and 168) and 1.0 part of flame retardant weighing spare;

[0051] B. Mix the PC resin, polyether modified silicone oil, heat stabilizer, and flame retardant according to the proportion and add them into the machine barrel. The mixture is first passed through the conveying section of the machine barrel through the screw. The screw speed is 400rpm, and the conveying section The temperatures in zone 1, zone 2 and zone 3 are 60°C, 130°C and 180°C respectively, and then the temperatures in zone 4, zone 5, zone 6 and zone 7 of the melting section entering the barrel are 190°C, 210°C, 220°C respectively ℃ and 230℃, after fully melted, carry out vacuum extraction through the vacuum p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of material processing, and relates to a high-gloss, low-odor and flame-retardant PC (polycarbonate) material as well as a preparation method and device thereof. The raw materials comprise, in parts by weight, 95.3 to 99 parts of PC resin, 0.1 to 2.0 parts of pearlescent resin, 0.05 to 0.1 parts of silicone oil, 0.5 to 1.0 part of an adsorbent, 0.2 to 0.6 parts of a heat stabilizer, and 0.1 to 1.0 part of a flame retardant. In the preparation process, pearlescent resin is added from a pearlescent resin feeding device close to the head end of an extruder. The size integrity of the pearlescent resin in the preparation process is greatly retained, a considerable part of pearlescent resin is selectively dispersed on the surface layer of the plastic,the content of the pearlescent resin on the surface layer is increased, so that the glossiness of the PC material is greatly improved, the flame retardance is also improved, the total use amount of the pearlescent resin is reduced, the cost of the composite material is reduced, and the impact toughness and the ductility are also greatly improved compared with an equivalent high-gloss material prepared by a traditional method.

Description

technical field [0001] The invention belongs to the technical field of material processing, and relates to a high-gloss, low-odor, flame-retardant PC material and a preparation method and device thereof. Background technique [0002] With the development of society, people's requirements for beauty are getting higher and higher, and high-gloss PC materials are used more and more widely. Traditional high-gloss PC materials are realized by spraying primer first, and then spraying high-gloss topcoat or electroplating. Since the primer is a thermosetting material, it is difficult to melt again. The physical properties and recycling performance of the plastic products after spraying are poor, which will affect the re-use use; and the spraying process is cumbersome, and the reject rate is high; the primer contains a large amount of toxic and harmful organic solvents, which is easy to produce toxic and harmful gases and dust, seriously endangering human health, and also causing pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L83/12C08K5/134C08K5/526B29C48/285
CPCB29C48/022B29C48/297C08L69/00C08L2201/02C08L83/12C08K5/1345C08K5/526
Inventor 刘小林周雷陈健李福顺肖利群吕强苏俊业叶淑英胡志唐良忠刘罡
Owner 重庆科聚孚新材料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com