Glass fiber reinforced PE water supply pipe and preparation method thereof

A water supply pipe and glass fiber technology, applied in the direction of pipes, rigid pipes, mechanical equipment, etc., can solve the problems of high density, sloshing, low strength of glass fiber tape, etc., to improve heat resistance and flame resistance, improve compression performance, Effect of improving wear resistance

Active Publication Date: 2020-04-17
ANHUI JIELANTE NEW MATERIAL CO LTD
View PDF16 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing PE water supply pipes and their preparation methods have the following technical problems: (1) Through the implementation standard detection of GB / T13663 and CJ / T358, hydrostatic strength, tensile strength, longitudinal retraction rate, oxidation induction time, melting Indicators such as volume flow rate cannot meet the requirements, and further improvements are needed on the structure, raw material composition, and preparation process; (2) The strength of the glass fiber tape is low and the density is high, and the higher strength cannot be improved while increasing the weight of the PE water supply pipe; ( 3) In the process of winding and forming, there will be a large amount of shaking, and the winding is not uniform and stable enough, which will affect the quality of the PE water supply pipe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass fiber reinforced PE water supply pipe and preparation method thereof
  • Glass fiber reinforced PE water supply pipe and preparation method thereof
  • Glass fiber reinforced PE water supply pipe and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] see Figure 1-4 As shown, this embodiment provides a glass fiber reinforced PE water supply pipe, which is composed of an inner layer 100, a core layer 200 and an outer layer 300. An inner transitional strengthening layer 400 is provided between the inner layer 100 and the core layer 200. The core An outer transition reinforcement layer 500 is provided between the layer 200 and the outer layer 300, and the core layer 200 is a wound pre-treated glass fiber tape layer;

[0039] Wherein, the inner layer 100 includes the following raw materials in parts by weight: 96 parts of HDPE resin, 3.3 parts of trimethylolpropane triacrylate, 17 parts of glass fiber, 1.9 parts of nano-silver antibacterial agent, 2.5 parts of lubricant magnesium stearate, 2.1 parts of expanded graphite;

[0040] The outer layer 300 includes the following raw materials in parts by weight: 107 parts of HDPE resin, 3.6 parts of trimethylolpropane triacrylate, 14 parts of glass fiber, 1.8 parts of nano-si...

Embodiment 2

[0053] see Figure 1-4 As shown, this embodiment provides a glass fiber reinforced PE water supply pipe, which is composed of an inner layer 100, a core layer 200 and an outer layer 300. An inner transitional strengthening layer 400 is provided between the inner layer 100 and the core layer 200. The core An outer transition reinforcement layer 500 is provided between the layer 200 and the outer layer 300, and the core layer 200 is a wound pre-treated glass fiber tape layer;

[0054] Wherein, the inner layer 100 includes the following raw materials in parts by weight: 96 parts of HDPE resin, 3.5 parts of trimethylolpropane triacrylate, 18 parts of glass fiber, 2.4 parts of nano-silver antibacterial agent, 2.5 parts of lubricant polyethylene wax, expansion 2.2 parts of graphite;

[0055] The outer layer 300 includes the following raw materials in parts by weight: 109 parts of HDPE resin, 3.6 parts of trimethylolpropane triacrylate, 15 parts of glass fiber, 2.0 parts of nano-sil...

Embodiment 3

[0063] see Figure 1-4 As shown, this embodiment provides a glass fiber reinforced PE water supply pipe, which is composed of an inner layer 100, a core layer 200 and an outer layer 300. An inner transitional strengthening layer 400 is provided between the inner layer 100 and the core layer 200. The core An outer transition reinforcement layer 500 is provided between the layer 200 and the outer layer 300, and the core layer 200 is a wound pre-treated glass fiber tape layer;

[0064]Wherein, the inner layer 100 includes the following raw materials in parts by weight: 98 parts of HDPE resin, 3.5 parts of trimethylolpropane triacrylate, 19 parts of glass fiber, 2.4 parts of nano-silver antibacterial agent, 2.8 parts of lubricant magnesium stearate, 1.9 parts of expanded graphite;

[0065] The outer layer 300 includes the following raw materials in parts by weight: 108 parts of HDPE resin, 3.6 parts of trimethylolpropane triacrylate, 16 parts of glass fiber, 2.1 parts of nano-sil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
elastic modulusaaaaaaaaaa
oxidation induction timeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a glass fiber reinforced PE water supply pipe and a preparation method thereof. The PE water supply pipe is formed by compositing an inner layer, a core layer and an outer layer, wherein an inner transition reinforcing layer is arranged between the inner layer and the core layer; an outer transition reinforcing layer is arranged between the core layer and the outer layer; the core layer is a layer wound by a pretreated glass fiber tape; both the inner layer and the outer layer adopt HDPE resin with good wear resistance, tensile resistance and chemical stability as a main component; and the inner layer has good pressure resistance, antibacterial property and aging resistance. The difference between the outer layer and the inner layer lies in that the HDPE resin content is increased, expanded graphite is replaced with polytetrafluoroethylene micro-powder which is high in flame retardance, good in compatibility and self-lubricating, and thus the heat resistance, flame retardance and wear resistance of the outer layer are improved; the inner layer and the outer layer are assisted by the inner transition reinforcing layer and the outer transition reinforcing layer, so that the core layer wound with the pretreated glass fiber tape is tightly wound therein, and the compression resistance and tensile strength of the PE water supply pipe are greatly improved.

Description

technical field [0001] The invention relates to the technical field of pipe materials, in particular to a glass fiber reinforced PE water supply pipe and a preparation method thereof. Background technique [0002] Due to the low heat resistance, low hardness, heat sensitivity and easy creep of polyethylene, it is often difficult for a single polyethylene material to meet the requirements of special working conditions such as load and high speed, and it often needs to be improved by blending and compounding. sex. Continuous glass fiber reinforced polyethylene composite pipe is a pipe made of high-strength thermoplastic continuous glass fiber prepreg tape, which is continuously wound and formed as the core layer, and is composited with inner and outer thermoplastic polyethylene plastics by extrusion molding. [0003] Prior art (CN106523801A) discloses a glass fiber reinforced polyethylene water supply pipe, including a pipe body, the pipe body is composed of an inner layer, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): F16L9/147C08K13/04C08K7/14C08K7/24C08L23/06C08L63/00C08L55/02C08L27/18C08K9/08B29C69/02B29L9/00B29L23/00
CPCB29C69/02B29L2009/00B29L2023/22C08K7/14C08K7/24C08K13/04C08L23/06C08L63/00C08L2203/18F16L9/147C08L27/18C08L55/02C08K9/08
Inventor 刘俊峰汪燕飞李国庆
Owner ANHUI JIELANTE NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap