A kind of latex emulsion adhesive with stable mechanical properties and preparation method thereof

A technology of adhesives and emulsions, applied in the direction of adhesives, natural rubber adhesives, polymer adhesive additives, etc., can solve problems such as unstable mechanical properties and effects

Active Publication Date: 2021-04-27
NANJING NORMAL UNIVERSITY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] CN109777322A discloses a method for improving the self-adhesive properties of natural latex-based adhesives, which involves adding nanoparticles into the adhesive as a filler, and the self-adhesive properties of the adhesive are improved by about 160%, but the effect of the improved mechanical properties is unstable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of latex emulsion adhesive with stable mechanical properties and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] 100 g of natural latex and 1.0 g of regenerated silk fibroin solution were placed in a stirred tank at 40° C. and stirred at a constant temperature for 30 minutes to prepare a natural latex-regenerated silk fibroin mixed emulsion. Put 5.0g of white oil and 0.5g of emulsifying thickener C-580 into a beaker, stir at 40°C for 5 minutes, then pour it into a stirring tank, continue to stir for 5 minutes, add 4.0g of water-based tackifying resin XY- 8025, stirred for 5 minutes, then added 0.15g of defoamer B-422, stirred for 5 minutes, after the stirring was completed, filtered, and the finished adhesive was obtained.

Embodiment 2

[0029] 100 g of natural latex and 2.0 g of regenerated silk fibroin solution were placed in a stirred tank at 40° C. and stirred at a constant temperature for 30 minutes to prepare a natural latex-regenerated silk fibroin mixed emulsion. Put 5.0g of white oil and 0.5g of emulsifying thickener C-580 into a beaker, stir at 40°C for 5 minutes, then pour it into a stirring tank, continue to stir for 5 minutes, add 4.0g of water-based tackifying resin XY- 8025, stirred for 5 minutes, then added 0.15g of defoamer B-422, stirred for 5 minutes, after the stirring was completed, filtered, and the finished adhesive was obtained.

Embodiment 3

[0031] 100 g of natural latex and 3.0 g of regenerated silk fibroin solution were placed in a stirred tank at 40° C. and stirred at a constant temperature for 30 minutes to prepare a natural latex-regenerated silk fibroin mixed emulsion. Put 5.0g of white oil and 0.5g of emulsifying thickener C-580 into a beaker, stir at 40°C for 5 minutes, then pour it into a stirring tank, continue to stir for 5 minutes, add 4.0g of water-based tackifying resin XY- 8025, stirred for 5 minutes, then added 0.15g of defoamer B-422, stirred for 5 minutes, after the stirring was completed, filtered, and the finished adhesive was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a latex emulsion adhesive with stable mechanical properties and a preparation method thereof. The adhesive mainly includes the following components in parts by weight: 100 parts of natural latex, 4-6 parts of tackifier, and 5 parts of plasticizer -6 parts, 0.2-0.6 parts of thickener, 0.1-0.3 parts of defoamer, 1-10 parts of toughening agent, the toughening agent is a regenerated silk fibroin solution made from silk powder. Compared with the prior art, the silk fibroin fiber and natural latex protein used in the present invention produce a cured structure, thereby strengthening the structural stability of natural latex, making it difficult for other additives to cross-link, thereby also reducing the self-efficacy of the adhesive. bonding.

Description

technical field [0001] The invention relates to a latex emulsion adhesive with stable mechanical properties and a preparation method thereof, belonging to the technical field of adhesive preparation. Background technique [0002] In recent years, the application range of adhesives has become more and more extensive, mainly used in medical, sports equipment, electronics industry, general industry, packaging and other fields, as the bonding of sports protection tapes, bandages, packaging tapes, double-sided tapes and labels, etc. Some are widely used. [0003] Natural latex is latex collected from natural plants, filtered and coagulated to make natural polymer compounds with polyisoprene as the main component. The latex particle of natural latex is essentially a polyisoprene core surrounded by a shell of non-rubber components (such as proteins and lipids). From the chemical structure of natural latex, it can be seen that natural latex is a non-polar unsaturated rubber, and i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J107/02C09J11/08
CPCC08L2205/035C09J11/08C09J107/02C08L89/00
Inventor 李利沈健侯迪
Owner NANJING NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com