Flame-retardant polyester material, preparation method thereof, granule and fiber product

A technology of flame-retardant polyester and pellets, which is applied in the field of polyester materials, can solve problems such as fire accidents, and achieve the effects of easy operation, good compatibility, and widespread application

Active Publication Date: 2020-03-13
东莞市道尔新材料科技有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] As we all know, most organic polymer materials are flammab...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant polyester material, preparation method thereof, granule and fiber product
  • Flame-retardant polyester material, preparation method thereof, granule and fiber product
  • Flame-retardant polyester material, preparation method thereof, granule and fiber product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Embodiment 1: A kind of preparation method of flame-retardant polyester pellet provided in this embodiment, it comprises the following steps:

[0029] (1) 1 part of 2,4-dihydroxybenzophenone derivative (R 1 : -H, R 2 :-H), 1.2 parts of succinic anhydride, 0.01% part of 4-dimethylaminopyridine, and 50 parts of tetrahydrofuran were placed in a three-necked flask, mechanically stirred, heated to reflux for 10 h, left to stand, filtered, and the organic phase was distilled under reduced pressure to obtain terminal Carboxyl benzophenone derivatives (IR: 3352cm -1 : Phenol-OH weakened; 3386cm -1 : -OH generation; 1780cm -1 : Ring-C=O disappears; 1750cm -1 :-C=O generates), be recorded as A;

[0030] (2) Put 1 part of A, 1.2 parts of hydroxyethyl isocyanurate, 0.01% part of 4-dimethylaminopyridine, and 60 parts of tetrahydrofuran in a three-necked flask, mechanically stir, heat and reflux for 10 hours, let stand, filter, The organic phase was distilled under reduced pres...

Embodiment 2

[0033] Embodiment 2: A kind of preparation method of flame-retardant polyester pellet provided in this embodiment, it comprises the following steps:

[0034] (1) 1 part of 2,4-dihydroxybenzophenone derivative (R 1 : -H, R2 :-OCH 3 ), 1.0 parts of phthalic anhydride, 5% parts of zinc acetate, and 50 parts of acetone are placed in a three-necked flask, mechanically stirred, heated to reflux for 15h, left to stand, filtered, and the organic phase is distilled under reduced pressure to obtain the carboxyl-terminated diphenylmethane Ketone derivatives (IR: 3352cm -1 : Phenol-OH weakened; 3386cm -1 : -OH generation; 1780cm -1 : Ring-C=O disappears; 1750cm -1 :-C=O generates), be recorded as A;

[0035] (2) Put 1 part of A, 1.0 part of hydroxyethyl isocyanurate, 5% part of zinc acetate, and 60 parts of acetone in a three-necked flask, mechanically stir, heat and reflux for 20 hours, let stand, filter, and decompress the organic phase After distillation and vacuum drying, isocya...

Embodiment 3

[0038] Embodiment 3: A kind of preparation method of flame-retardant polyester pellet provided in this embodiment, it comprises the following steps:

[0039] (1) 1 part of 2,4-dihydroxybenzophenone derivative (R 1 : -OH, R 2 :-OC 2 h 5 ), 1.1 parts of succinic anhydride, 1% part of antimony trioxide, 50 parts of N,N-dimethylformamide were placed in a three-necked flask, mechanically stirred, heated to reflux for 12h, left to stand, filtered, and the organic phase was distilled under reduced pressure , to obtain carboxyl-terminated benzophenone derivatives (IR: 3352cm -1 : Phenol-OH weakened; 3386cm -1 : -OH generation; 1780cm -1 : Ring-C=O disappears; 1750cm -1 :-C=O generates), be recorded as A;

[0040] (2) Put 1 part of A, 1.1 parts of hydroxyethyl isocyanurate, 1% part of antimony trioxide, and 60 parts of N,N-dimethylformamide in a three-necked flask, stir mechanically, and heat to reflux for 15 hours , stand still, filter, the organic phase is distilled under red...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a flame-retardant polyester material, a preparation method thereof, a granule and a fiber product. An o-hydroxybenzophenone derivative, acid anhydride, 2-hydroxyethyl isocyanurate, chloroethanol, terephthalic acid and ethylene glycol are used as raw materials, the defect that traditional polyester is inflammable is overcome, and reaction steps are simple and are easy to operate; 2-hydroxyethyl isocyanurate is adopted as one of the raw materials, so that the reaction activity of -OH and-NH2 is high, the reaction flexibility is high, the nitrogen content is high, and theflame retardance of the material is outstanding; the o-hydroxybenzophenone derivative is used as one of the raw materials, the o-hydroxybenzophenone derivative has an ultraviolet absorption effect andcan be used as a light stabilizer, para-hydroxyl groups in the structure can be used as reaction points for esterification, and the contained benzene ring structure is similar to a polyester structure, so good compatibility and facilitation of wide promotion and application are achieved.

Description

technical field [0001] The invention relates to the technical field of polyester materials, in particular to a flame-retardant polyester material, a preparation method thereof, pellets and fiber products. Background technique [0002] Conventional polyester fibers are single-functional and flammable, which can no longer meet the needs of domestic and foreign markets for product diversification and functionalization. Endowing conventional chemical fibers with new functions is one of the key points and hotspots in the field of new chemical fiber materials research. The flame retardancy of fiber is one of the hotspots that people pay attention to at present. Most of the flame retardant properties of textiles on the market are improved by post-additive additives. The product obtained in this way has the disadvantages of being not wear-resistant and washable, and most of the flame retardants used are halogen-based flame retardants, which are harmful to human health and the envir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G63/685C08G63/78D01F6/92D01F1/07D01F1/10
CPCC08G63/6856C08G63/78D01F6/92D01F1/07D01F1/106
Inventor 查皓查家华谢旭鹏
Owner 东莞市道尔新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap