A kind of porous silicon oxide composite material and its preparation and application

A silicon oxide and composite material technology, which is applied in the preparation/purification of silicon oxide, silicon dioxide, carbon, etc., can solve the problems of complex preparation process and low initial efficiency, and achieve simple process, low cost and enhanced combination Effect

Active Publication Date: 2022-01-25
湖南宸宇富基新能源科技有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies of the prior art and improving the low efficiency and complex preparation process of the silicon oxide negative electrode material for the first time, the first purpose of the present invention is to provide a new negative electrode active material with a special structure and special composition (porous silicon oxide composite materials), aiming to improve electrical properties such as first-time efficiency and cycle stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of porous silicon oxide composite material and its preparation and application
  • A kind of porous silicon oxide composite material and its preparation and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0069] Put silicon particles with a silicon content of 99.5wt% and a particle size of 25mm into a roller ball mill with a filling factor of 25%; blow in air at 115°C and a humidity of 60%, the positive pressure of the ball mill is 750Pa, and the negative pressure of the collection device is 600Pa; at 60 rpm The ball milling reaction under the rotating speed produces silicon fine particles wrapped in silicon oxide, the particle size is 25 μm, and the oxygen content is 45 wt%. Granules, metal magnesium powder, mixed salt particles (the molar ratio of lithium chloride: sodium chloride is 7:3, eutectic point 570°C) and medium-temperature asphalt according to the ratio of 1:0.2:10:1 are processed by extrusion granulation Mix and granulate to obtain a composite precursor; put the composite precursor into a sintering boat and place it in a muffle furnace, and carry out a sintering reaction under an argon atmosphere, and raise the temperature to 700°C at a rate of 5°C / min, and react fo...

Embodiment 2

[0072] Put silicon particles with a silicon content of 99.5wt% and a particle size of 45mm into a roller ball mill with a filling factor of 30%; blow in air at 120°C and a humidity of 68%, the positive pressure of the ball mill is 760Pa, and the negative pressure of the collection device is 580Pa; at 50 rpm The ball milling reaction under the rotating speed produces silicon fine particles wrapped in silicon oxide, with a particle size of 32 μm and an oxygen content of 65 wt%. Granules, metal magnesium powder, mixed salt particles (the molar ratio of lithium chloride: sodium chloride is 7:3, eutectic point 570°C) and medium-temperature asphalt in the ratio of 1:0.3:10:1 are processed by extrusion granulation Mix and granulate to obtain a composite precursor; put the composite precursor into a sintering boat and place it in a muffle furnace, and carry out a sintering reaction under an argon atmosphere, and raise the temperature to 700°C at a rate of 5°C / min, and react for 6 hours...

Embodiment 3

[0075] Put silicon particles with a silicon content of 99.5wt% and a particle size of 10mm into a roller ball mill with a filling factor of 18%; blow in air at 110°C and a humidity of 55%, the positive pressure of the ball mill is 730Pa, and the negative pressure of the collection device is 620Pa; The ball milling reaction under the rotating speed produces silicon fine particles wrapped in silicon oxide, the particle size is 22 μm, and the oxygen content is 39 wt%. Granules, metal magnesium powder, mixed salt particles (the molar ratio of lithium chloride: sodium chloride is 7:3, eutectic point 570°C) and medium-temperature asphalt in the ratio of 1:0.15:10:1 are processed by extrusion granulation Mix and granulate to obtain a composite precursor; put the composite precursor into a sintering boat and place it in a muffle furnace, and carry out a sintering reaction under an argon atmosphere, and raise the temperature to 700°C at a rate of 5°C / min, and react for 6 hours. After c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
pore sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of lithium ion battery materials, and specifically discloses a porous silicon oxide composite material, which includes an inner core, an intermediate layer compounded on the surface of the inner core, and an outer layer compounded on the surface of the intermediate layer; wherein, the inner core is silicon; the intermediate layer It is silicate of silicon oxide and metal M dispersed in silicon oxide; the outer layer is a carbon coating layer; metal M is a metal element that can reduce silicon oxide. The invention also provides the preparation method of the composite material and its application in the negative electrode active material of the lithium ion secondary battery. The research of the present invention finds that the composite material has the characteristics of long cycle life, high initial efficiency and the like.

Description

technical field [0001] The invention belongs to the technical field of lithium battery electrode materials, and in particular relates to a porous silicon oxide composite powder material and a preparation method thereof. Background technique [0002] With the continuous update of consumer electronics products and the rapid development of electric vehicles, the demand for a new generation of high-energy lithium-ion batteries is increasing, prompting its anode materials to shift from intercalated carbon-based materials (theoretical capacity 372mAh / g) to those with Lithiated metal materials, metal compounds and composite materials with high theoretical capacity are developed. Among them, silicon has become the mainstream of research on new anode materials at home and abroad due to its advantages such as high theoretical capacity (4211mAh / g), good safety performance and wide sources. However, the huge volume expansion and low intrinsic conductivity of silicon during the charge-d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/38H01M4/48H01M4/62H01M10/0525C01B32/05C01B33/12C01B33/22C01B33/26C01B33/32
CPCH01M4/366H01M4/386H01M4/483H01M4/625H01M4/628H01M10/0525C01B33/12C01B33/32C01B33/22C01B33/26C01B32/05H01M2004/021H01M2004/027C01P2004/80C01P2002/72C01P2004/03C01P2004/61C01P2002/88C01P2006/40Y02E60/10
Inventor 杨娟唐晶晶周向阳刘晓剑周昊宸王鹏侯林
Owner 湖南宸宇富基新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com