Zeolite modified cement bonded chromium-containing corundum castable and preparation method thereof

A cement-bonded, chromium-corundum-based technology, applied in the field of castables and their preparation, can solve problems such as environmental pollution, and achieve the effects of improving mechanical properties, good mechanical properties, and strong adsorption properties

Active Publication Date: 2020-02-11
WUHAN UNIV OF SCI & TECH
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem that the existing calcium aluminate cement combined with chromium-containing refractory castables is likely to cause environmental pollution, the present invention proposes a zeolite modified cement combined with chromium-containing corundum castables and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0021] Embodiment 1: In this embodiment, the zeolite modified cement combined with chromium-containing corundum castable consists of 10-20wt% platy corundum fine powder and 5-9wt% active α-Al 2 o 3 Micropowder, 3-12wt% chromium oxide fine powder, 2-6wt% calcium aluminate cement, 0.5-3wt% zeolite powder, 0.05-0.2wt% polycarboxylate dispersant and the rest platy corundum Granules are prepared.

[0022] This embodiment has the following beneficial effects:

[0023] 1. In this embodiment, platy corundum particles are used as aggregate, platy corundum fine powder and chromium oxide fine powder are used as matrix, calcium aluminate cement and zeolite powder are used as composite binder, and polycarboxylate is used as dispersant. A chromium-containing refractory castable is prepared. The preparation process is simple, and the production and use process is green and environment-friendly. Zeolite is an inexpensive, framework-like structure and porous hydrous aluminosilicate crystal...

specific Embodiment approach 2

[0025] Specific embodiment two: the preparation method of zeolite modified cement combined with chromium-containing corundum castable in this embodiment is carried out according to the following steps:

[0026] 1. Weigh the raw materials;

[0027] Weigh 10-20wt% platy corundum fine powder, 5-9wt% active α-Al 2 o 3 Micropowder, 3-12wt% chromium oxide fine powder, 2-6wt% calcium aluminate cement, 0.5-3wt% zeolite powder, 0.05-0.2wt% polycarboxylate dispersant and the rest platy corundum pellets as raw material;

[0028] 2. Mix the calcium aluminate cement and zeolite powder weighed in step 1 evenly to obtain a composite binder;

[0029] 3. The polycarboxylate dispersant, platy corundum particles, platy corundum fine powder, active α-Al 2 o 3 Micropowder and chromium oxide fine powder, and the composite binding agent obtained in step 2 are mixed uniformly to obtain a premix;

[0030] 4. Add 3-6wt% water to the premix obtained in step 3 and mix evenly to obtain a wet mixture...

specific Embodiment approach 3

[0036] Specific embodiment three: the difference between this embodiment and specific embodiment two is: the Al in the plate-shaped corundum particles described in step one 2 o 3 content>99wt%; the distribution of particle size d in tabular alumina particles is: the content of tabular alumina particles with d<1mm is 20-30wt%, and the content of tabular corundum particles with 1≤d<3mm is 35-45wt %, 3≤d<5mm plate-shaped corundum particles are the balance. Other steps and parameters are the same as in the second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a castable and a preparation method thereof, and concretely relates to a zeolite modified cement bonded chromium-containing corundum castable and a preparation method thereof.The purpose of the invention is to solve the problem that the existing Cr2O3-containing refractory castable taking calcium aluminate cement as a binding agent easily causes environmental pollution. The castable is prepared from fine tabular corundum powder, active alpha-Al2O3 micro-powder, fine chromium oxide powder, calcium aluminate cement, zeolite powder, a polycarboxylate dispersant and tabular corundum particles. The preparation method comprises the following steps: weighing and mixing the above raw materials to obtain a premix, adding water, performing stirring to obtain a wet mixture,carrying out pouring and vibration molding on the wet mixture, and finally sequentially carrying out maintenance, drying and heat treatment. The zeolite powder can control migration and diffusion of metal ions and inhibit generation and leaching of Cr (VI) compounds, so that green and environmentally-friendly production is realized; and the sintering densification of the castable is promoted, andthe mechanical properties and the slag corrosion resistance of the chromium-containing castable are remarkably improved. The preparation method is suitable for preparing the chromium-containing castable.

Description

technical field [0001] The invention relates to a pouring material and a preparation method thereof. Background technique [0002] Chromium-free (Cr 2 o 3 ) refractory materials in the case of high service temperature and complex and changeable slag composition, the service life will be significantly reduced, so the use cost will increase and the adaptability will be poor. Due to Cr 2 o 3 It has the advantages of high melting point, good chemical stability and low solubility in liquid slag, and a small amount of Cr 2 o 3 Dissolving in the slag can significantly increase the viscosity of the slag, so the introduction of Cr into the refractory material 2 o 3 It can significantly improve the anti-slag erosion performance of the material. In addition, Cr 2 o 3 at high temperature with Al 2 o 3 Reaction to form (Al,Cr) with lower coefficient of expansion 2 o 3 Solid solution, which improves the high-temperature mechanical properties and thermal shock stability of re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
CPCC04B35/66C04B2235/3217C04B2235/3222C04B2235/3241C04B2235/3463
Inventor 李亚伟徐腾腾廖宁桑绍柏徐义彪
Owner WUHAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com