Catalyst for preparing methallyl alcohol by selectivey hydrogenating methylacrolein, and preparation method thereof

A technology of methallyl alcohol and methacrolein is applied in the preparation of hydroxyl compounds, chemical instruments and methods, metal/metal oxide/metal hydroxide catalysts, etc. Low problems, to achieve the effect of reducing preparation cost, high selectivity and high conversion rate

Active Publication Date: 2020-02-11
SHANGHAI HUAYI GRP CO
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The purpose of the present invention is to provide a new catalyst for the selective hydrogenation of methacrolein to methallyl alcohol. This catalyst has the advantages of high catalyst activity, good selectivity and high stability, and effectively solves the existing problems. The production process has serious environmental pollution and low atomic utilization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalyst for preparing methallyl alcohol by selectivey hydrogenating methylacrolein, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0021] The sintered body of element X, carrier and optional element Y in the catalyst of the present invention is prepared by an in-situ one-step method, followed by adding a compound Z selected from alkali metal chloride, lithium hydroxide or a mixture thereof. Therefore, the preparation method of catalyst of the present invention comprises:

[0022] (i) Mix the precursor salt compound solution of the X element and the optional Y element with the silicon source, add the lye dropwise until the pH is not less than 6.0, such as 6.0-12.0, and keep stirring at 20-60°C for 0.5- 5 hours, then dry at 80-150°C for 4-24 hours, and bake at 250-600°C for 1-12 hours.

[0023] The precursor salt compound of X element and optional Y element suitable for the method of the present invention is not particularly limited, as long as the precursor salt compound can form an aqueous solution. In a preferred example of the present invention, the precursor salt compound is a soluble salt. In an exa...

Embodiment 1

[0046] Ag15%-Au0.3%-NaCl0.05% / SiO 2 catalyst

[0047] Configure 10 mL of silver lactate aqueous solution and 10 mL of chloroauric acid solution in proportion, add 100 g of silica sol (silicon oxide content 30%) in sequence, stir at 25°C for 0.5 hours, then drip ammonia solution, control the pH value of the mixed solution to 11, and continue The mixed solution was stirred for 3.5 hours, then dried at 100° C. for 14 hours to obtain a dried sample, and then the dried sample was calcined at 450° C. for 6 hours. The obtained calcined product was crushed and formed into 20-60 mesh particles, then added to 0.1mol / L NaCl aqueous solution and soaked in equal volume for 3 hours, then dried at 110°C for 10 hours, and calcined at 430°C for 2.5 hours to obtain a supported catalyst sample .

[0048] By weight, in the final solid sample, the Ag element in Ag accounts for 15%, the Au element in Au accounts for 0.3%, and the NaCl in NaCl accounts for 0.05% (Ag15%-Au0.3%-NaCl0.05% catalyst )...

Embodiment 2

[0053] Ag20%-In0.2%-Cs0.1%-KCl0.03% / SiO 2 catalyst

[0054] Weigh silver lactate, indium nitrate, and cesium nitrate in proportion, dissolve them in 200mL of water to form a solution, mix them with 100g of fumed silicon oxide dispersion (30% silicon oxide content), stir at 25°C for 1 hour, then drip ammonia solution to control The pH value of the mixed solution was 8, and the mixed solution was continuously stirred for 1 hour; then dried at 120° C. for 16 hours to obtain a dried sample, and then baked at 450° C. for 5 hours. The obtained calcined product was crushed and shaped into 20-60 mesh particles, then added to 0.3mol / L KCl aqueous solution and immersed for 1.5 hours, then dried at 120°C for 6 hours, and calcined at 400°C for 5 hours to obtain a supported catalyst sample.

[0055] By weight, the final solid sample contains 20% Ag element as Ag, 0.2% In element as In, 0.1% Cs element as Cs, and 0.03 KCl as KCl in the final solid sample. %.

[0056] The obtained solid p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a catalyst for preparing methallyl alcohol through selectively hydrogenating methylacrolein, and a preparation method thereof. The catalyst is a silicon oxide-supported X-Y-Z catalyst, wherein X is one or a mixture of two of Ag and Au; Y is one or a mixture of more of Ir, Pd, Rh, In, Sn, Ce and Cs; Z is selected from an alkali metal chloride, a lithium hydroxide or a mixture thereof; and the catalyst comprises 1-30 wt% of the active X component, 0-5 wt% of the Y component, 0.01-5 wt% of the Z component, and the balance of the silicon oxide carrier.

Description

technical field [0001] The invention relates to a catalyst for the selective hydrogenation of methacrolein to produce methallyl alcohol, which has improved methacrolein conversion rate and methallyl alcohol selectivity. Background technique [0002] Methallyl alcohol, commonly known as "carbon tetraol", is an important organic intermediate, widely used in the synthesis of perfumes and resins, and can also be used as a starting material to synthesize the corresponding methacrylic acid and corresponding esters. Methallyl alcohol polyoxyethylene ether (HPEG) is synthesized from methallyl alcohol and ethylene oxide, which is a new generation of high-performance concrete water reducer. The polycarboxylate high-efficiency superplasticizer synthesized by this product has high-efficiency particle dispersion and retention capabilities, and has many advantages such as high water-reducing rate, low cement usage, good reinforcement effect, good durability, no corrosion of steel bars, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J23/66B01J27/10B01J27/125B01J27/13B01J27/135C07C29/141C07C33/03
CPCB01J27/10B01J27/125B01J27/13B01J27/135B01J23/66C07C29/141C07C33/03Y02P20/584
Inventor 廖湘洲宁春利芮果孙佳仕王海云庄岩马建学
Owner SHANGHAI HUAYI GRP CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka