A Prussian blue analog nanosheet array material and its application in electrolysis of water

A nanosheet array and aqueous solution technology, which is applied in electrolytic components, electrolytic processes, electrodes, etc., can solve the problems of low utilization of active sites, poor conductivity of PBA, low electrocatalytic performance, etc., and achieve fast mass transfer and electron transport capabilities , high stability, large specific surface area effect

Active Publication Date: 2021-04-02
FUDAN UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the poor conductivity and low utilization of active sites of PBA, its electrocatalytic performance is far lower than that of noble metals, which limits its further application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Prussian blue analog nanosheet array material and its application in electrolysis of water
  • A Prussian blue analog nanosheet array material and its application in electrolysis of water
  • A Prussian blue analog nanosheet array material and its application in electrolysis of water

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The preparation process of ultrathin Prussian blue analog nanosheet catalyst (2D CoFe-PBA@NF-24) is as follows:

[0038] 1) Cut blank nickel foam (1cm×2cm) and use acetone, ethanol, and deionized water to sonicate for 15 minutes respectively to remove surface pollutants, and put it in a 60°C oven for 6 hours before using it as a substrate.

[0039] 2) 100mL Co(NO 3 ) 2 ·6H 2 O (3mmol) aqueous solution was added to 100mL Na 2 Fe(CN) 5 NO·H 2 O (1 mmol) aqueous solution, the resulting solution was stirred at room temperature for 1 min until the solution became cloudy. Put the treated foamed nickel substrate into it, and let it stand in a dark place at room temperature for 24 hours. Finally, the nickel foam obtained by the reaction was rinsed with deionized water, and dried in an oven at 60°C for 12 hours to obtain the product 2D CoFe-PBA@NF-24.

[0040] When the 2D CoFe-PBA@NF-24 electrocatalyst prepared in this example is used to catalyze the hydrogen evolution re...

Embodiment 2

[0054] In this example, when Co(NO 3 ) 2 ·6H 2 O solution and Na 2 Fe(CN) 5 NO·H 2 After the O solution was mixed, the nickel foam substrate was put into the mixed solution, and left to react for 2 hours at room temperature in the dark, and the rest was the same as in Example 1 to prepare a 2D CoFe-PBA@NF-2 electrocatalyst.

Embodiment 3

[0056] In this example, when Co(NO 3 ) 2 ·6H 2 O solution and Na 2 Fe(CN) 5 NO·H 2 After the O solution was mixed, the nickel foam substrate was put into the mixed solution, and left to react for 12 hours at room temperature in the dark, and the rest was the same as in Example 1 to prepare a 2D CoFe-PBA@NF-12 electrocatalyst.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a prussian blue analogue nanosheet array material and a water electrolysis application thereof, wherein a preparation method of the material comprises the following steps: 1)pretreating foamed nickel to serve as a matrix; 2) mixing a Co(NO3)2.6H2O solution with a Na2Fe(CN)5NO.H2O solution, and then stirring at room temperature until the solution is turbid to obtain a mixed solution; and 3) putting the matrix into the mixed solution, carrying out standing reaction for 2-48 h, and carrying out post-treatment to obtain the prussian blue analogue nanosheet array material.The material is used as a catalyst for water electrolysis reaction. Compared with the prior art, the prepared ultrathin prussian blue analogue nanosheet array material is simple in preparation process and low in cost, can be used for carrying out stable and efficient hydrogen evolution reaction, oxygen evolution reaction and total water decomposition under different current densities, and has huge potential value in large-scale hydrogen production application.

Description

technical field [0001] The invention belongs to the technical field of materials and energy, and relates to a Prussian blue analogue nanosheet array material, its preparation and its application in electrolyzing water. Background technique [0002] The depletion of fossil fuels and emerging environmental issues are driving the rapid development of hydrogen energy. As a way to produce hydrogen, electrolysis of water can be used in conjunction with photovoltaic systems and wind turbines to convert electrical energy into stable chemical energy in an environmentally friendly manner. It is a practical technology in line with sustainable development and has broad development prospect. During water electrolysis, two electrode half-reactions mainly occur, namely hydrogen evolution reaction (HER) and oxygen evolution reaction (OER). However, due to the existence of energy barriers in the thermodynamic and kinetic processes of these two half-reactions, a high overpotential is requir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25B1/04C25B11/052C25B11/061C25B11/085C25B11/03B01J31/22B01J35/10B01J37/03
CPCB01J31/1691B01J31/1805B01J35/0033B01J35/1057B01J37/031B01J2531/842B01J2531/845C25B1/04C25B11/031C25B11/075Y02E60/36
Inventor 吴仁兵费奔陈子亮
Owner FUDAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com