Method for nondestructively measuring bonding strength of coating interface by ultrasonic body wave phase spectrum

A technology that combines strength and ultrasonic waves at the interface. It is applied in the analysis of solids using sound waves/ultrasonic waves/infrasonic waves, material analysis using sound waves/ultrasonic waves/infrasonic waves, and measurement devices. It can solve difficult engineering applications, low quantitative accuracy, and complicated operations. problems, to achieve the effects of avoiding interference, wide application range, and simple engineering application

Active Publication Date: 2020-01-24
DALIAN UNIV OF TECH
View PDF10 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Solve the aliasing problems of the surface echo on the coating and the echo of the coating / substrate interface when a single ultrasonic body wave probe is vertically incident, and overcome the relatively expensive equipment, complicated operation, and difficulty in engineering application of ultrasonic surface wave technology and ultrasonic microscopy technology. The existing ultrasonic body wave technology is easily affected by the thickness of the coating, etc., and the quantitative accuracy is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for nondestructively measuring bonding strength of coating interface by ultrasonic body wave phase spectrum
  • Method for nondestructively measuring bonding strength of coating interface by ultrasonic body wave phase spectrum
  • Method for nondestructively measuring bonding strength of coating interface by ultrasonic body wave phase spectrum

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] The detection system of the ultrasonic phase spectrum quantitative detection method for the bonding strength of the coating and the substrate interface consists of figure 1 The water tank 1 shown, the coating sample 2, the ultrasonic water immersion probe 3 with a nominal frequency of 5.0 MHz, the XYZ three-dimensional stepping device 4, the ultrasonic flaw detector 5 and the computer 6 are composed. It uses the following measurement steps:

[0040] (1) Place the ultrasonic water immersion probe above the reference test block to ensure that the axis of the main sound beam of the probe is perpendicular to the surface of the test block; the ultrasonic wave is incident on the reference test block through the coupling medium in the water tank, and the reflection echo signal on the surface of the reference test block is collected. A scan waveform P 0 (t), such as figure 2 (a), t is time, the unit is second, for P 0 (t) Perform fast Fourier transform to obtain its power s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method for nondestructively measuring the bonding strength of a coating interface by ultrasonic body wave phase spectrum belongs to the technical field of ultrasonic nondestructive testing. The method adopts a set of ultrasonic detection system which comprises a water tank, a coating sample, an ultrasonic water immersion probe, an ultrasonic flaw detector, an XYZ three-dimensional stepping device and a computer; wherein ultrasonic body waves of the ultrasonic detection system are vertically incident to the coating sample to perform detection, aliasing signals P<r>(t) of water / coating and coating / substrate interfaces are collected, fast Fourier transform is performed on the P<r>(t) to obtain an unwrapped phase psi<0>(f), the psi<0>(f) is subjected to linear fitting to obtain a phase spectrum psi(f), resonance frequencies f<n> and f<n+2> corresponding to adjacent odd or even zero phases of the psi(f) are identified, phase change phi<k> caused by interface rigidity change is solved, and quantitative measurement of interface bonding strength is realized according to a theoretical relationship between the phi<k> and a rigidity coefficient K<n>. The method of the invention solvesthe problems that the operation of ultrasonic surface wave and ultrasonic microscope technical equipment is complex, the engineering application is difficult, a traditional ultrasonic bulk wave technology is easily influenced by the thickness of a coating, and the quantitative precision is low.

Description

technical field [0001] The invention relates to a method for nondestructively measuring coating interface bonding strength by ultrasonic body wave phase spectrum, which belongs to the technical field of ultrasonic nondestructive testing. Background technique [0002] Key components in aerospace, nuclear power and other fields generally use coating technology to meet their service requirements of high performance, long life, and high reliability. The harsh high temperature, high pressure, high wear and other service environments of components require high bonding strength at the coating / substrate interface. Lima et al. pointed out that the bonding strength of the coating interface is directly related to the coating failure. Ghasemi et al pointed out that thermal barrier coatings generally have residual stress and local micro-defects, and sufficient interface bonding strength between the coating and the substrate is required to avoid shedding failure. Therefore, the developm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N29/04G01N29/28
CPCG01N29/04G01N29/28G01N2291/0237
Inventor 马志远林莉齐天之罗忠兵
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products