Non-cured rubber asphalt waterproof coating, preparation method of coating and root puncture resistant waterproof material

A technology of asphalt waterproof coating and non-curing rubber, which is applied in the direction of asphalt coatings and coatings, which can solve the problems of no root puncture resistance, high dryness requirements, and limited application range, so as to eliminate fire hazards and reduce construction and maintenance costs, the effect of reducing the number of construction

Inactive Publication Date: 2020-01-24
CHINA PETROLEUM & CHEM CORP
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the thickness of the waterproof membrane is uniform, there are seams during construction, and there are many hidden dangers in the details. A large number of seams are easy to cause penetration
At the same time, the coiled material has high requirements on the construction environment temperature and the dryness of the base layer. Once it is broken, the self-healing ability is poor, which will lead to leakage of the building.
[0004] In recent years, non-curing rubber asphalt waterproof coatings have been greatly applied and promoted in the field of building waterproofing. However, although the non-curing asphalt coatings currently on the market have good waterproof effects, they do not have root puncture resistance, which limits range of application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-cured rubber asphalt waterproof coating, preparation method of coating and root puncture resistant waterproof material
  • Non-cured rubber asphalt waterproof coating, preparation method of coating and root puncture resistant waterproof material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of non-curing rubber asphalt waterproof coating, comprises following components by weight part: 55 parts of 70# road petroleum asphalts, 25 parts of catalytic cracking oil slurry, SBS 1301 8 parts, SBR (combined styrene content is 22% in SBR ~25%) 3 parts, coumarone resin 20 parts, 80 mesh waste rubber powder 5 parts, zeolite powder 25 parts, B2 0.5 parts.

[0030] The preparation method is:

[0031] (1) Weigh each component by parts by weight, mix petroleum pitch and softener, heat to 170°C, and stir at a speed of 2000r / min for 20min;

[0032] (2) Add modifiers SBS and SBR to the mixture of step (1), heat to 180°C, and stir at a speed of 2000r / min for 30min;

[0033] (3) Add tackifier, scrap rubber powder, filler and root inhibitor to the mixture in step (2) in sequence, cool down to 150°C, stir at 5000r / min for 60min, then cool down to room temperature.

Embodiment 2

[0035] A kind of non-curing rubber asphalt waterproof coating, comprising the following components by weight: 35 parts of 70# road petroleum asphalt, 10 parts of aromatic hydrocarbon oil, 3 parts of SBS 1401, 5 parts of SBR, 5 parts of terpene resin, 60 mesh waste 10 parts of rubber powder, 12 parts of diatomaceous earth, B2 1 copy.

[0036] The preparation method is:

[0037] (1) Weigh each component by parts by weight, mix petroleum pitch and softener, heat to 150°C, and stir at a speed of 2000r / min for 30min;

[0038] (2) Add modifiers SBS and SBR to the mixture of step (1), heat to 170°C, and stir for 40min at a speed of 2000r / min;

[0039] (3) Add tackifier, waste rubber powder, filler and root inhibitor to the mixture in step (2) in sequence, cool down to 140°C, stir at 5000r / min for 50min, then cool down to room temperature.

Embodiment 3

[0041] A kind of non-curing rubber asphalt waterproof coating, comprises the following components by weight: 45 parts of 90# road petroleum asphalt, 17 parts of naphthenic oil, 5 parts of SBS 4303, 3 parts of SBR, 12 parts of C5 petroleum resin, 100 parts 10 parts of waste rubber powder, 10 parts of bentonite, B5 0.6 parts.

[0042] The preparation method is:

[0043] (1) Weigh each component by parts by weight, mix petroleum pitch and softener, heat to 160°C, and stir for 40min at a speed of 2000r / min;

[0044] (2) Add modifiers SBS and SBR to the mixture of step (1), heat to 190°C, and stir at a speed of 2000r / min for 60min;

[0045] (3) Add tackifier, waste rubber powder, filler and root inhibitor to the mixture in step (2) in sequence, cool down to 160°C, stir at 5000r / min for 50min, then cool down to room temperature to obtain the product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of building waterproof materials, and particularly relates to a non-cured rubber asphalt waterproof coating, a preparation method thereof and a root puncture resistant waterproof material. The coating includes the following raw materials in parts by weight: 35-55 parts of petroleum asphalt, 10-25 parts of a softener, 3-8 parts of a modifier SBS, 3-5 parts of a modifier SBR, 5-20 parts of a tackifier, 5-15 parts of waste rubber powder, 10-25 parts of a filler and 0.1-1.5 parts of a root-blocking agent. The waterproof coating provided by the inventionhas the dual characteristics of water resistance and root puncture resistance, is used for planted roofs, and can greatly improve the reliability of water resistance, reduce construction and maintenance costs, prolong the waterproof service life of buildings, and reduce the load bearing pressure of the buildings; and the root puncture resistant waterproof material provided by the invention can ensure the long-term integrity of a waterproof layer, reduce the number and thickness of a waterproof system, reduce the load of the buildings and reduce the number of construction, and has superioritycompared with a current root puncture resistant waterproof system.

Description

technical field [0001] The invention belongs to the technical field of building waterproof materials, and in particular relates to a non-curing rubber asphalt waterproof coating, a preparation method thereof, and a root puncture-resistant waterproof material. Background technique [0002] The planting roof system refers to the planting surface on the top of the roof garden and the underground garage. At present, the planting roof structure has many layers, reaching nine or more layers, and the construction is relatively complicated. Because the plant root system has a strong penetrating ability, it can penetrate the roof structure layer and cause serious water leakage. Once leakage occurs, it will bring great difficulties to maintenance and cause large economic losses. . Therefore, the planted roof waterproof system is the key to success. [0003] Most of the existing planting roof waterproofing systems are mainly composed of root puncture-resistant waterproofing membrane...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D7/65
CPCC08L2205/035C09D195/00C09D7/65C08L53/02C08L9/06
Inventor 高淑美张传明马鹏程贾丽凤许金山刘爱华毛冬梅
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com