Lightweight wear-resistant automobile side window glass and preparation method thereof

A technology for automotive side and window glass, applied in windshields, windows, vehicle parts, etc., can solve the problems of poor wear resistance, weather resistance and hydrophobicity, inability to waterproof and anti-fog, and affect the use performance, etc., to achieve weather resistance. Good property and hydrophobicity, improve adhesion, highlight the effect of weather resistance

Active Publication Date: 2022-02-22
SHENTONG TECH GRP CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the problems in the prior art when polycarbonate is directly used as the window glass, which has poor wear resistance, weather resistance and water repellency, is easy to scratch, has poor sealing performance, and cannot be waterproof and anti-fog, which will affect the line of sight. Therefore, it is necessary to apply a coating on the surface of polycarbonate glass, but it is difficult for the coating in the prior art to significantly improve the wear resistance, weather resistance and water repellency of polycarbonate glass at the same time, and the coating is in polycarbonate glass. The adhesion on the carbonate glass is poor, which affects the use performance. A light-weight wear-resistant automobile side window glass and its preparation method are provided. The surface coating is coated on the polycarbonate base layer and the PC / ABS black edge layer. , the coating has strong adhesion to the resin layer, and can significantly improve the wear resistance, weather resistance and water repellency of the window glass, realize the lightweight of the car and improve the performance of the window glass at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lightweight wear-resistant automobile side window glass and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Such as figure 1 Shown, a kind of lightweight wear-resistant automobile side window glass, comprises the polycarbonate base layer 1 that thickness is 5mm, is provided with the PC / ABS black border layer 2 that thickness is 2.5mm around one side of polycarbonate base layer, polycarbonate The surface on both sides of the ester base layer and the surface of the PC / ABS black edge layer are coated with a surface coating 3 with a thickness of 15 μm.

[0035] The preparation method of the coating used for the surface coating is:

[0036] (A) Nano-SiO 2 Dispersed in ethanol, added with nano-SiO 2 The ratio is 9mL: 5g of γ-aminopropyltriethoxysilane and 2 drops of triethylamine, stirred and reacted for 6h and then centrifuged, washed the product twice with ethanol, acetone and tetrahydrofuran in sequence, and then dispersed the product in tetrahydrofuran, Joined with nano-SiO 2 Glutaric anhydride with a mass ratio of 2.5:1 was centrifuged after stirring for 6 hours, washed re...

Embodiment 2

[0046] A light wear-resistant automobile side window glass, comprising a polycarbonate base layer with a thickness of 3mm, a PC / ABS black edge layer with a thickness of 2mm is provided around one side of the polycarbonate base layer, and the two sides of the polycarbonate base layer And the PC / ABS black edge layer is coated with a surface coating with a thickness of 10 μm.

[0047] The preparation method of the coating used for the surface coating is:

[0048] (A) Nano-SiO 2 Dispersed in ethanol, added with nano-SiO 2 The ratio is 8mL: 5g of γ-aminopropyltriethoxysilane and 1 drop of triethylamine, stirred and reacted for 5h and then centrifuged. After washing the product twice with ethanol, acetone and tetrahydrofuran, the product was dispersed in tetrahydrofuran. Joined with nano-SiO 2 Glutaric anhydride with a mass ratio of 2:1 was centrifuged after stirring for 5 hours, washed repeatedly with 0.1mol / L NaCl solution and dried to obtain carboxylated nano-SiO 2 ;

[0049...

Embodiment 3

[0058] A light wear-resistant automobile side window glass, comprising a polycarbonate base layer with a thickness of 8mm, a PC / ABS black border layer with a thickness of 3mm is provided around one side of the polycarbonate base layer, and the two sides of the polycarbonate base layer And the PC / ABS black edge layer is coated with a surface coating with a thickness of 20 μm.

[0059] The preparation method of the coating used for the surface coating is:

[0060] (A) Nano-SiO 2 Dispersed in ethanol, added with nano-SiO 2 The ratio is 10mL: 5g of γ-aminopropyltriethoxysilane and 3 drops of triethylamine, stirred and reacted for 8h and then centrifuged. After washing the product twice with ethanol, acetone and tetrahydrofuran, the product was dispersed in tetrahydrofuran. Joined with nano-SiO 2 Glutaric anhydride with a mass ratio of 3:1 was centrifuged after stirring for 8 hours, washed repeatedly with 0.1mol / L NaCl solution and dried to obtain carboxylated nano-SiO 2 ;

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of automobile window glass, and discloses a light-weight and wear-resistant automobile side window glass and a preparation method thereof. Edge layer, polycarbonate base layer and PC / ABS black edge layer are coated with surface coating, the coating composition of surface coating includes solvent, surface grafted polydimethylsiloxane nano-SiO 2 and polycarbonate-polydimethylsiloxane copolymer. The preparation method is as follows: using a two-color injection mold to inject the polycarbonate base layer first, and then injecting the PC / ABS black edge layer in the same mold; baking the polycarbonate base layer and the PC / ABS black edge layer to remove internal stress, And scrub the surface with alcohol solvent; shower and dry to get the surface coating. The invention coats the modified coating on the surface of the polycarbonate base layer and the PC / ABS black border layer, which greatly improves the wear resistance, weather resistance and water repellency of the side window glass.

Description

technical field [0001] The invention relates to the technical field of automobile window glass, in particular to a light-weight wear-resistant automobile side window glass and a preparation method thereof. Background technique [0002] With the continuous progress of society, people's living standards are also constantly improving, the demand for cars has also increased a lot than before, and the number of cars is also increasing. As countries implement policies that force automakers to reduce vehicle fuel consumption, vehicle lightweight has become an important breakthrough for major auto companies. According to statistics, every 1% reduction in vehicle weight can reduce fuel consumption by 0.6%-1.0%, and energy consumption is closely related to exhaust emissions. Therefore, the lightweight of automobiles is of great significance to energy saving and environmental protection. "Lightweight" has become an important national strategy, and more and more research institutions ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J7/046C08L69/00C08L55/02C09D183/10C09D7/62C09D5/18B60J1/08
CPCC08J7/04C09D183/10C09D7/62C09D5/18B60J1/08C08K2201/011C08J2369/00C08J2355/02C08J2469/00C08J2455/02C08J2483/10
Inventor 方立锋周宝聪徐鑫灿诸熔
Owner SHENTONG TECH GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com