Seaweed carbon fiber far infrared moisture-absorption multifunctional fabric and preparation method thereof

A seaweed charcoal fiber and far-infrared technology, which is applied in the field of fabric production, can solve the problems of inconspicuous moisture absorption, achieve remarkable far-infrared effects, promote blood circulation in the body, and have good moisture absorption and perspiration effects

Pending Publication Date: 2019-12-31
NINGBO DAQIAN TEXTILE
View PDF12 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Far-infrared health-care fabric is a new functional textile in recent years. It has the functions of warming up, health care, etc., but the traditional fabric with far-infrared function has no obvious moisture absorption effect. Fabric development is still in a blank stage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A production method of seaweed charcoal fiber far-infrared moisture-absorbing multifunctional fabric, comprising the following steps:

[0029] (1) Burning seaweed carbon: the seaweed that has been washed, cut into sections, and dried at 50-60°C is pulverized in a pulverizer to 0.2-0.3 cm, and sent to a carbonization furnace for carbonization;

[0030] (2) Pre-carbonization treatment: first raise the temperature in the carbonization furnace to 100°C at a rate of 2°C / min, then raise the temperature to 180°C at a rate of 8°C / min and keep it at this temperature for 2 hours, then heat it at 10°C Raise the temperature from 180°C to 230°C at a speed of 1 / min, and keep it at 230°C for 6 hours;

[0031] (3) Carbonization and sintering: raise the temperature from 230°C to 300°C at a rate of 9°C / min, and keep the temperature for 2.5 hours to obtain a black carbon body, and crush the above carbon body to 40-60nm to obtain microparticle seaweed carbon;

[0032] (4) Preparation of f...

Embodiment 2

[0039] A production method of seaweed charcoal fiber far-infrared moisture-absorbing multifunctional fabric, comprising the following steps:

[0040] (1) Burning seaweed carbon: the seaweed that has been washed, cut into sections, and dried at 50-60°C is pulverized in a pulverizer to 0.2-0.3 cm, and sent to a carbonization furnace for carbonization;

[0041] (2) Pre-carbonization treatment: first raise the temperature in the carbonization furnace to 100°C at a rate of 2°C / min, then raise the temperature to 180°C at a rate of 8°C / min and keep it at this temperature for 2 hours, then heat it at 10°C Raise the temperature from 180°C to 230°C at a speed of 1 / min, and keep it at 230°C for 7 hours;

[0042] (3) Carbonization and sintering: raise the temperature from 230°C to 320°C at a rate of 10°C / min, and keep the temperature for 2.5 hours to obtain a black carbon body, and crush the above carbon body to 40-60nm to obtain micronized seaweed carbon;

[0043] (4) Preparation of far...

Embodiment 3

[0050] A production method of seaweed charcoal fiber far-infrared moisture-absorbing multifunctional fabric, comprising the following steps:

[0051] (1) Burning seaweed carbon: the seaweed that has been washed, cut into sections, and dried at 50-60°C is pulverized in a pulverizer to 0.2-0.3 cm, and sent to a carbonization furnace for carbonization;

[0052] (2) Pre-carbonization treatment: first raise the temperature in the carbonization furnace to 100°C at a rate of 2°C / min, then raise the temperature to 180°C at a rate of 8°C / min and keep it at this temperature for 2 hours, then heat it at 10°C Raise the temperature from 180°C to 230°C at a speed of 1 / min, and keep it at 230°C for 8 hours;

[0053] (3) Carbonization and sintering: raise the temperature from 230°C to 350°C at a rate of 12°C / min, and keep the temperature for 3 hours to obtain a black carbon body, and pulverize the above carbon body to 40-60nm to obtain microparticle seaweed carbon;

[0054] (4) Preparation of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a seaweed carbon fiber far infrared moisture-absorption multifunctional fabric and a preparation method thereof. The preparation method comprises the following steps: cleaning, segmenting, drying and crushing seaweed, and then carrying out carbonizing to obtain seaweed carbon; mixing the seaweed carbon with far infrared ceramic ultrafine powder, adding a polymer spinning aid, and carrying out granulating to obtain far infrared masterbatches; blending the far infrared masterbatches and fiber slices, and carrying out spinning, winding and stretching to form seaweed carbon far infrared fibers; blending the seaweed carbon far infrared fibers with the moisture-absorption and sweat-releasing polyester fibers to obtain blended yarns; and preparing the seaweed carbon fiberfar infrared moisture-absorption multifunctional fabric through weaving, printing, dyeing and finishing processes. According to the preparation method, the far infrared ceramic superfine powder is added into the seaweed carbon, so that the far infrared effect of the fabric is remarkable, the far infrared radiation rate can reach 90% or above, the moisture absorption of the fabric is greater than220%, and the fabric has a good moisture-absorption and sweat-releasing effect.

Description

technical field [0001] The invention relates to the field of fabric production methods, in particular to a seaweed charcoal fiber far-infrared moisture-absorbing multifunctional fabric and a preparation method thereof. Background technique [0002] Far-infrared health-care fabric is a new functional textile in recent years. It has the functions of warming up, health care, etc., but the traditional fabric with far-infrared function has no obvious moisture absorption effect. The development of fabrics is still in a blank stage. [0003] Seaweed charcoal fiber is the carbonized product of seaweed charcoal, which is crushed into ultra-fine particles, and then blended with polyester solution or nylon solution, spun and processed into fibers. This fiber has good far-infrared radiation performance , can be woven into various fabrics with far-infrared radiation function. [0004] Therefore, it is a problem to be solved by those skilled in the art to study how to utilize seaweed ch...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04D01F1/10D04B1/16C01B32/05
CPCD02G3/045D01F1/10D04B1/16C01B32/05D10B2101/12D10B2331/04D10B2401/02D10B2501/02D10B2501/021
Inventor 原鹏飞何立锋关力源毛丹丹
Owner NINGBO DAQIAN TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap