Method for preparing glazed tile from biomass fiber-epoxy resin composite material

A technology of biomass fiber and epoxy resin, which is applied in the direction of clay products, applications, household appliances, etc., can solve the problems of no significant improvement in the preparation method, poor use stability, poor compatibility, etc., and achieve improved performance and competitiveness, enhance the effect of action, increase the effect of swelling degree

Inactive Publication Date: 2019-12-27
霍邱县明楼琉璃瓦有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

By optimizing the composition of the glazed tile body and glaze, the invention improves the color rendering effect, compression resistance, fire resistance, acid and alkali resistance, and physical and chemical properties of the glazed tile, such as water absorption and air permeability. Obviously, the invention has no significant impact on the preparation method. Only the composition of the raw materials has been adjusted, the compatibility between the black soil and other raw material components is poor, the overall use stability is not good, and the competitiveness of the product is reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing glazed tile from biomass fiber-epoxy resin composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of biomass fiber-epoxy resin composite material prepares the method for glazed tile, comprises the steps:

[0033] (1) Preparation of grouting blank:

[0034] a. Immerse the bamboo pulp fibers in the treatment solution A, then heat the treatment solution A immersed in the bamboo pulp fibers in a water bath, place it in a low-temperature environment immediately after the water bath heating, and leave it for 30 minutes to centrifuge, discard the supernatant, and use a purification After the water was centrifuged and washed 3 times, the precipitate was taken out and dried for later use;

[0035] b. Put the bamboo pulp fiber and epoxy resin powder after the treatment liquid A in operation a into the bead mill for grinding treatment according to the weight ratio of 8:1, and put them in the electron beam irradiation device for irradiation after completion After processing, take out the mixed powder for later use;

[0036] c. Put the mixed powder obtained in operation...

Embodiment 2

[0056] A kind of biomass fiber-epoxy resin composite material prepares the method for glazed tile, comprises the steps:

[0057] (1) Preparation of grouting blank:

[0058] a. Immerse the bamboo pulp fiber in the treatment solution A, then carry out the treatment solution A soaked with the bamboo pulp fiber in a water bath heat treatment, place it in a low temperature environment immediately after the water bath heating and let it stand for 35min and then centrifuge, discard the supernatant, and use a purification After the water was centrifuged and washed 3 times, the precipitate was taken out and dried for later use;

[0059] b. Put the bamboo pulp fiber and epoxy resin powder after the treatment liquid A of operation a into the bead mill for grinding treatment according to the weight ratio of 9:1.15, and then put them in the electron beam irradiation device for irradiation after completion After processing, take out the mixed powder for later use;

[0060] c. Put the mixe...

Embodiment 3

[0080] A kind of biomass fiber-epoxy resin composite material prepares the method for glazed tile, comprises the steps:

[0081] (1) Preparation of grouting blank:

[0082] a. Immerse the bamboo pulp fiber in the treatment solution A, then carry out the treatment solution A soaked with the bamboo pulp fiber in a water bath heat treatment, place it in a low temperature environment immediately after the water bath heating and let it stand for 40min and then centrifuge, discard the supernatant, and use a purification After the water was centrifuged for 4 times, the precipitate was taken out and dried for later use;

[0083] b. Put the bamboo pulp fiber and epoxy resin powder processed by the treatment solution A in operation a into the bead mill for grinding treatment according to the weight ratio of 10:1.3, and place them in the electron beam irradiation device for irradiation after completion After processing, take out the mixed powder for later use;

[0084] c. Put the mixed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a glazed tile from a biomass fiber-epoxy resin composite material, and belongs to the technical field of glazed tile preparation; the method comprises the following steps: (1) preparing a grouting blank; (2) molding the grouting blank; (3) treating the green body; (4) preparing glaze; (5) glazing the green body; and (6) firing and polishing the glazedgreen body. By means of the method, the water absorption rate of the glazed tile can be reduced, the bending strength of the glazed tile is improved, and the rapid cooling, rapid heating and freezingresistance can meet the requirements of the national building colored glaze product standard GB 9197-88 and the national building material industry building colored glaze product standard JC / T 765-2006.

Description

technical field [0001] The invention belongs to the technical field of glazed tile preparation, and in particular relates to a method for preparing glazed tiles from a biomass fiber-epoxy resin composite material. Background technique [0002] Ambilight glazed tiles are traditional Chinese architectural elements, usually painted with golden, emerald green, blue and other colored lead glazes. As early as the Southern and Northern Dynasties, my country used glazed tiles for decoration in buildings. After the development of past dynasties, glazed tiles have formed a series of products with rich varieties, exquisite shapes and strong assembly. Zheng kiss, close horn kiss, pendant beast, money beast, treasure top and so on. Existing glazed tiles are usually made by mixing and firing various mud materials. The glaze layer is generally thick and produces stress, and the quality is heavy, which may easily lead to defects such as cracks and chipping on the glaze surface of the prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/36C04B33/04C04B33/13C04B41/86C03C8/00
CPCC03C8/00C04B33/04C04B33/1305C04B33/36C04B41/009C04B41/5022C04B41/86C04B2235/602C04B2235/606C04B2235/656C04B2235/6562C04B2235/6567C04B2235/96C04B2235/9607C04B41/4535
Inventor 余涛
Owner 霍邱县明楼琉璃瓦有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com