Method for preparing low-smoke foamed sponge

A foam sponge and foam stabilizer technology, applied in the field of foam sponge, can solve problems such as disorientation, environmental pollution, and a large amount of smoke, and achieve the effects of inhibiting degradation, preventing environmental pollution, and prolonging service life

Inactive Publication Date: 2019-12-13
亚罗斯建材(江苏)有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a preparation method of low-smoke foamed sponge, which has the advantages of low-smoke and flame-retardant, and solves the problem that the foamed sponge added with halogen flame retardants is prone to produce a large amount of smoke, which makes escapers Suffocation and disorientation, and at the same time bring certain pollution problems to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A preparation method of low-smoke foaming sponge, comprising the following steps:

[0029] 1) Put the polyethylene resin into the plastic internal mixer first, and when the internal mixing temperature rises to 150°C, add Evapine rubber, and discharge it after internal mixing for 2-5 minutes, which is the foamed sponge matrix;

[0030] 2) Mix the natural rubber latex, vulcanizing agent, accelerator and anti-aging agent evenly, and let it stand at room temperature for 15 minutes to obtain the mixed natural rubber latex. Add foam stabilizer and foaming agent to the mixed natural rubber latex, stir and foam, and then add retarded rubber Coagulant and active agent, obtain foam latex;

[0031] 3) Preheat the training machine for 6 minutes, then mix the foam masterbatch prepared in step 1 and the foam latex prepared in step 2 with dispersant, antioxidant, protective wax, softener, reinforcing agent and Put the anti-hydrolysis agent into the open mixer, then mix for 10-20 minu...

Embodiment 2

[0034] A preparation method of low-smoke foaming sponge, comprising the following steps:

[0035] 1) Put the polyethylene resin into the plastic internal mixer first, and when the internal mixing temperature rises to 150°C, add Evapine rubber, and discharge it after internal mixing for 2-5 minutes, which is the foamed sponge matrix;

[0036] 2) Mix the natural rubber latex, vulcanizing agent, accelerator and anti-aging agent evenly, and let it stand at room temperature for 15 minutes to obtain the mixed natural rubber latex. Add foam stabilizer and foaming agent to the mixed natural rubber latex, stir and foam, and then add retarded rubber Coagulant and active agent, obtain foam latex;

[0037] 3) Preheat the training machine for 6 minutes, then mix the foam masterbatch prepared in step 1 and the foam latex prepared in step 2 with dispersant, antioxidant, protective wax, softener, reinforcing agent and Put the anti-hydrolysis agent into the open mixer, then mix for 10-20 minu...

Embodiment 3

[0041] A preparation method of low-smoke foaming sponge, comprising the following steps:

[0042] 1) Put the polyethylene resin into the plastic internal mixer first, and when the internal mixing temperature rises to 150°C, add Evapine rubber, and discharge it after internal mixing for 2-5 minutes, which is the foamed sponge matrix;

[0043] 2) Mix the natural rubber latex, vulcanizing agent, accelerator and anti-aging agent evenly, and let it stand at room temperature for 15 minutes to obtain the mixed natural rubber latex. Add foam stabilizer and foaming agent to the mixed natural rubber latex, stir and foam, and then add retarded rubber Coagulant and active agent, obtain foam latex;

[0044] 3) Preheat the training machine for 6 minutes, then mix the foam masterbatch prepared in step 1 and the foam latex prepared in step 2 with dispersant, antioxidant, protective wax, softener, reinforcing agent and Put the anti-hydrolysis agent into the open mixer, then mix for 10-20 minu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of foamed sponge and discloses a method for preparing low-smoke foamed sponge. The low-smoke foamed sponge comprises the following raw materials in parts by weight: 70-100 parts of polyethylene resin, 30-50 parts of levapren rubber, 20-30 parts of natural latex, 2-5 parts of a vulcanizing agent, 0.5-2.5 parts of an accelerant, 0.5-1.5 parts of an anti-aging agent, 0.5-3 parts of a retardant gelatinizing agent, 1-5 parts of a foam stabilizer, 7-9 parts of an activator, 2-3 parts of a dispersant, 3-5 parts of a foaming agent, 2-3 parts of an antioxidant and 2-3 parts of a protective wax. Due to addition of the levapren rubber raw material, the levapren rubber has very excellent flame retardance and can be used as a flame retardant in a product formula, high flame retardance requirements can be met without a halogen flame retardant, then the foamed sponge is liable to generate a great amount of smoke, the purpose of environment pollution prevention is achieved, and the prepared foamed sponge has properties of rubber and is good in elasticity, good in rebound resilience and not easy to deform.

Description

technical field [0001] The invention relates to the technical field of foam sponges, in particular to a method for preparing low-smoke foam sponges. Background technique [0002] Foaming sponge is like foaming bread. It can be foamed by mechanical equipment, or it can be artificially surrounded by wooden boards. The foamed cotton is like a large square bread. Use a slicer to go through the slicing process. The cutting thickness is required, and the softness and hardness of the foamed cotton can also be adjusted. Seat cotton generally adopts 25-8kg / m3 density, and others use 20-22kg / m3 density. Although the softness and hardness of the sponge are directly related to the density, they are also related to different additive formulas. Therefore, the industry is divided into high elasticity, gray Ultra, black gray ultra, soft cotton. When designing and using the product, it should be rationally and scientifically matched according to different shapes and structures. Generally, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08L7/02C08L89/00C08K13/02C08K5/09C08K3/22C08K5/39C08K3/34C08J9/04
CPCC08J9/0023C08J9/0033C08J9/0061C08J9/0066C08J9/04C08J2323/06C08J2407/02C08J2423/08C08J2489/00C08K3/34C08K5/09C08K5/39C08K13/02C08K2003/2296
Inventor 秦伯军张君秦天德刘远斌翟必赢曹鑫
Owner 亚罗斯建材(江苏)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap