Porous membrane for membrane distillation and operating method of module for membrane distillation

A membrane distillation and component technology, applied in chemical instruments and methods, membranes, pervaporation, etc., can solve the problem of unclear surface state, membrane distillation module or membrane distillation device water treatment capacity, time-dependent stable transportability, and handleability. Reduce and other problems to achieve the effect of improving water treatment capacity, inhibiting wetting and solute precipitation/residual phenomena, cost and high efficiency

Active Publication Date: 2022-06-24
ASAHI KASEI KK
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0022] In addition, in addition to wetting, the present inventors have also found the following problem: In membrane distillation, a solute (such as NaCl crystal) in an undissolved state is formed on the permeation side surface and inside (membrane thickness portion) of the porous membrane. The phenomenon of precipitation and residue (hereinafter referred to as "salt permeation") reduces the water treatment capacity, stability over time, transportability, handling properties, etc. of the membrane distillation module or membrane distillation device
The porous membrane described in Patent Document 3 does not mention its structure, especially its internal structure, and its surface state is also unclear, so there is room for improvement in terms of wetting and inhibition of salt permeation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Porous membrane for membrane distillation and operating method of module for membrane distillation
  • Porous membrane for membrane distillation and operating method of module for membrane distillation
  • Porous membrane for membrane distillation and operating method of module for membrane distillation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0691] Put 4,200 polyvinylidene fluoride hollow fiber membranes with an outer diameter of 1.22 mm, an inner diameter of 0.66 mm, and a film thickness of 280 μm in a cylindrical container made of polysulfone with an inner diameter of 128 mm, and bond the hollow fiber membranes to the cylinder with epoxy resin. The gap of the type container was fixed, and a membrane module for membrane distillation with an effective membrane length of 86mm was produced. In addition, 360 stainless steel tubes having an inner diameter of 1 mm, an outer diameter of 1.2 mm, and an effective length of 220 mm were housed in the same container as the above-mentioned cylindrical container to produce a condenser. like figure 1 As shown, the module for membrane distillation and the condenser were connected to each other at one side opening. At this time, the shortest distance between the outer surface of the hollow fiber membrane in the membrane distillation module and the outer surface of the stainless ...

Embodiment 2

[0697] Membrane distillation was performed in the same manner as in Example 1 except that 4400 hollow fiber membranes were used. The structural characteristics of the membrane distillation module used, the operating conditions of the membrane distillation, and the results are shown in Table 1 below. The flux is 14.6kg / m 2 / hr, the permeated water production efficiency was 2.7%, and the conductivity of the obtained permeated water varied in the range of 0.1 to 0.2 μS / cm.

Embodiment 3

[0699] Membrane distillation was performed in the same manner as in Example 1 except that 4600 hollow fiber membranes were used. The structural characteristics of the membrane distillation module used, the operating conditions of the membrane distillation, and the results are shown in Table 1 below. The flux is 13.4kg / m 2 / hr, the permeated water production efficiency was 2.6%, and the conductivity of the obtained permeated water varied in the range of 0.1 to 0.2 μS / cm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to view more

Abstract

A membrane distillation apparatus comprising: a module for membrane distillation comprising two or more hydrophobic porous hollow fiber membranes; and a condenser for condensing vapor taken out from the module, the porous The average pore diameter of the hollow hollow fiber is 0.01 μm to 1 μm, the filling rate of the porous hollow fiber of the membrane distillation module is 10% to 80%, and the pressure condition of the membrane distillation is 1 kPa or more and the temperature of the water to be treated below the saturated vapor pressure of water.

Description

technical field [0001] The present invention relates to a module for membrane distillation and a membrane distillation apparatus including the module for membrane distillation. More specifically, the present invention relates to a membrane distillation module containing two or more hydrophobic membranes having through holes in a cylindrical container and a membrane distillation apparatus using the membrane distillation module. In the bundle of porous hollow fiber membranes, the water to be treated is passed inside the hollow fiber membranes, and the water vapor coming out from the outside is cooled and condensed, and recovered as permeated water. Background technique [0002] The membrane distillation (Membrane Distillation (MD)) method is the following method: using a hydrophobic porous membrane that allows only water vapor in the water to be treated to pass through, the heated high-temperature water to be treated (hereinafter also referred to as raw water) The water vapor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01D69/02B01D61/36B01D65/02B01D65/06B01D69/08
CPCB01D61/364B01D63/02B01D69/12B01D2325/02B01D2325/38B01D67/0088B01D69/02B01D63/033B01D61/366B01D61/368B01D69/081B01D63/026B01D65/02B01D69/1213B01D71/261B01D71/262C02F1/447B01D2325/02833B01D2325/02834B01D2325/24B01D2325/20B01D2321/16B01D71/26
Inventor 桥本知孝新井裕之长田一人久保田昇竹泽浩气大豊武彦
Owner ASAHI KASEI KK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap