Ultra-thin glass fiber sunshade fabric and preparation method thereof

A fabric and glass fiber technology, applied in the field of textile fabrics, can solve the problems of mildew and low anti-ultraviolet performance of sunshade fabrics, and achieve the effect of solving mildew, not easy to interfere with external factors, and feeling comfortable.

Pending Publication Date: 2019-11-05
句容市恒鑫遮阳科技有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the deficiencies of the prior art, the present invention provides an ultra-thin glass fiber sunshade fabric and its preparation method, which has the advantages of anti-ultraviolet and mildew resistance, and solves the problem of low ultraviolet resistance of the sunshade fabric in the prior art, and the use of After a long time, the sunshade fabric will have the problem of mildew

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The invention provides an ultra-thin glass fiber sunshade fabric, which includes a fabric and a coating coated on the surface of the fabric. The coating includes the following raw materials in proportions by weight: 2 parts of antibacterial agent, 5 parts of anti-ultraviolet dispersion liquid, 3 parts of Water-based polyurethane emulsion, 2 parts of polyvinyl alcohol, 1 part of tributyl phosphate, 0.5 parts of coupling agent, 1 part of triethanolamine, 10 parts of glass fiber, 6 parts of filler, 0.1 part of defoamer, 3 parts of ammonium phosphate and 4 parts Dispersant.

[0029] Among them, the fabric is interwoven with high-strength and low-shrinkage polyester filaments; the antibacterial agent is nano-silver-loaded antibacterial finishing agent; the anti-ultraviolet dispersion liquid is a mixture of nano-titanium dioxide, part starch and surfactant The mass ratio of the three is 2:1:1; the filler is a mixture of sepiolite, asbestos fiber powder, diatomaceous earth, so...

Embodiment 2

[0038] The invention provides an ultra-thin glass fiber sunshade fabric, which includes a fabric and a coating coated on the surface of the fabric. The coating includes the following raw materials in proportions by weight: 3 parts of antibacterial agent, 7 parts of anti-ultraviolet dispersion liquid, 4 parts of Water-based polyurethane emulsion, 2.5 parts of polyvinyl alcohol, 2 parts of tributyl phosphate, 1.2 parts of coupling agent, 1.5 parts of triethanolamine, 13 parts of glass fiber, 7 parts of filler, 1 part of defoamer, 5 parts of ammonium phosphate and 6 parts Dispersant.

[0039] Among them, the fabric is interwoven with high-strength and low-shrinkage polyester filaments; the antibacterial agent is nano-silver-loaded antibacterial finishing agent; the anti-ultraviolet dispersion liquid is a mixture of nano-titanium dioxide, part starch and surfactant The mass ratio of the three is 2:1:1; the filler is a mixture of sepiolite, asbestos fiber powder, diatomaceous earth...

Embodiment 3

[0048]The invention provides an ultra-thin glass fiber sunshade fabric, which includes a fabric and a coating coated on the surface of the fabric. The coating comprises the following raw materials in proportions by weight: 4 parts of antibacterial agent, 9 parts of anti-ultraviolet dispersion liquid, 5 parts of Water-based polyurethane emulsion, 3 parts of polyvinyl alcohol, 3 parts of tributyl phosphate, 2 parts of coupling agent, 2 parts of triethanolamine, 15 parts of glass fiber, 9 parts of filler, 2 parts of defoamer, 7 parts of ammonium phosphate and 9 parts Dispersant.

[0049] Among them, the fabric is interwoven with high-strength and low-shrinkage polyester filaments; the antibacterial agent is nano-silver-loaded antibacterial finishing agent; the anti-ultraviolet dispersion liquid is a mixture of nano-titanium dioxide, part starch and surfactant The mass ratio of the three is 2:1:1; the filler is a mixture of sepiolite, asbestos fiber powder, diatomaceous earth, sod...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an ultra-thin glass fiber sunshade fabric. The fabric comprises a fabric body and a coating applied to the fabric surface; the coating is prepared from, by weight, 2-4 parts ofan antibacterial agent, 5-9 parts of an uvioresistant dispersing agent, 3-5 parts of an aqueous polyurethane emulsion, 2-3 parts of polyvinyl alcohol, 1-3 parts of tributyl phosphate, 0.5-2 parts ofa coupling agent, 1-2 parts of triethanolamine, 10-15 parts of glass fiber, 6-9 parts of a filler, 0.1-2 parts of a defoamer, 3-7 parts of ammonium phosphate and 4-9 parts of a dispersing agent. Accordingly, by making the antibacterial agent dispersed on the surface of the fabric, the antibacterial performance of the fabric is more stable, the sunshade fabric has the good mildewproof, anti-moth and antibacterial properties, the problem that the sunshade fabric mildews is solved, and nanometer titania in the uvioresistant dispersing agent not only can absorb ultraviolet rays but also can reflect and scatter the ultraviolet rays, can also be pervious to visible light and avoid harm brought by the ultraviolet rays, and is an ultraviolet protecting agent excellent in performance.

Description

technical field [0001] The invention relates to the technical field of textile fabrics, in particular to an ultra-thin glass fiber sunshade fabric and a preparation method thereof. Background technique [0002] In recent years, with the continuous improvement of people's living standards, and the establishment and continuous improvement of fire protection regulations and textile flame-retardant standards, the number of decorative textiles and industrial textiles that need flame-retardant finishing has continued to increase. The fire safety issues of building interior decoration materials and so on are increasingly concerned by the government and the public. In home textiles, curtains account for a large proportion, of which polyester fibers are the most used. [0003] Sunshade fabrics are fabrics used to block the sun's glare and harmful light from intruding. It has some functions that other fabrics do not have, such as adjusting indoor temperature, adjusting natural light...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/00D06N3/14
CPCD06N3/0059D06N3/0061D06N3/0063D06N3/0077D06N3/142D06N2209/065D06N2209/067D06N2209/1671D06N2209/1678
Inventor 王岳来王姝颖
Owner 句容市恒鑫遮阳科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap