Method for preparing monodisperse microspheres by ultrasonic-induced raft precipitation polymerization

A monodisperse microsphere, precipitation polymerization technology, applied in the preparation of microspheres, microcapsule preparations, etc., can solve the problems of low mechanical properties, lack of functional groups, large internal stress of monodisperse microspheres, etc., to achieve wide application prospects, polymerization rate quick effect

Active Publication Date: 2020-07-24
HUAIYIN INSTITUTE OF TECHNOLOGY
View PDF17 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the uneven internal structure of the monodisperse microspheres prepared by the precipitation polymerization of the conventional ordinary free radical polymerization mechanism leads to large internal stress and low mechanical properties; more importantly, the surface of this type of microspheres lacks further functions. oxidized functional groups, limiting its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach 1

[0022] Add 0.4 g of methyl methacrylate, 0.4 g of ethylene glycol dimethacrylate, and 20 mg of CPADB into a transparent reaction vessel, and add a mixture of 7 g of ethanol and 3 g of water as a solvent, and bubble with high-purity argon After deoxygenation, it was placed under a 50w ultrasonic triggering device with a frequency of 450kHz. The ultrasonic mode was ultrasonic 2s, intermittent 2s, and polymerized for 50 minutes. After the polymerization, the reaction vessel was unsealed and centrifuged to obtain a white powder. *20 ml of ethanol was washed and centrifuged, and the resulting solid was o C dried overnight in a vacuum oven to obtain monodisperse polymer microspheres.

Embodiment approach 2

[0024] Add 0.5 g of hydroxyethyl methacrylate, 0.5 g of trimethylolpropane trimethacrylate, and 25 mg of RAFT reagent DDMAT into a transparent reaction vessel, and add a mixture of 6.5 g of ethanol and 3.5 g of water to make Solvent, after bubbling high-purity argon to remove oxygen, place it under a 50w, frequency 450kHz ultrasonic triggering device, the ultrasonic mode is ultrasonic 2s intermittent 2s, polymerization 60 minutes; powder, the white powder was washed with 3*20 ml ethanol and centrifuged, and the resulting solid was o C dried overnight in a vacuum oven to obtain monodisperse polymer microspheres.

Embodiment approach 3

[0026] Add 0.4 g of styrene, 0.6 g of p-divinylbenzene, and 25 mg of CPDN into a transparent reaction vessel, and add a mixture of 7.5 g of ethanol and 5.5 g of water as a solvent. It is placed under a 50w ultrasonic triggering device with a frequency of 450kHz, the ultrasonic mode is ultrasonic 2s intermittent 2s, and polymerized for 80 minutes; after the polymerization is completed, the reaction vessel is unsealed and centrifuged to obtain a white powder, which is washed with 3*20 ml ethanol Wash and centrifuge the resulting solid at 35 o C dried overnight in a vacuum oven to obtain monodisperse polymer microspheres.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of chemical industry, and discloses a method for preparing monodisperse microspheres by ultrasonic-induced RAFT precipitation polymerization, comprising the following steps: adding monofunctional vinyl monomers, multifunctional vinyl monomers, and RAFT reagents into a reaction vessel, And add an appropriate amount of ethanol-water mixture to it as a solvent, and place it under ultrasonic waves to initiate polymerization after bubbling high-purity argon to deoxygenate; after the polymerization is completed, unseal the reaction vessel, centrifuge and wash the white powder with ethanol several times , to obtain monodisperse microsphere samples. The invention creatively introduces ultrasound into RAFT precipitation polymerization to prepare monodisperse active microspheres, the polymerization rate is fast, the spherical rate is high and the microspheres have strong monodispersity, and the prepared microspheres have dithioester functional groups on the surface, It is convenient for further functionalization, and has broad application prospects in the fields of adsorption separation, biomedicine and so on.

Description

technical field [0001] The invention relates to the technical field of controllable radical polymerization, in particular to a method for preparing monodisperse microspheres by ultrasonic-induced RAFT precipitation polymerization. Background technique [0002] At present, highly cross-linked monodisperse microspheres are widely used in many fields such as standard metrology, intelligence information, catalyst carrier, biomedicine and chromatographic separation due to their advantages of large specific surface area, strong adsorption and uniform size. However, the uneven internal structure of the monodisperse microspheres prepared by the precipitation polymerization of the conventional ordinary free radical polymerization mechanism leads to large internal stress and low mechanical properties; more importantly, the surface of this type of microspheres lacks further functions. functionalized groups, limiting its application. Contents of the invention [0003] Purpose of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/14C08F222/14C08F212/36C08F220/20B01J13/18
CPCC08F220/14C08F222/1006C08F212/36C08F220/20B01J13/185C08F2438/03C08F222/103C08F222/102C08F212/08
Inventor 姜孝武夏鑫杨路史建倪伶俐
Owner HUAIYIN INSTITUTE OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap