Multifunctional clothing material and preparation method thereof

A multi-functional, clothing technology, applied in the field of clothing materials, can solve the problems of complex production process, high production difficulty, low yield, etc., and achieve the effects of increasing specific surface area, good mechanical properties, and convenient operation.

Active Publication Date: 2019-10-01
HAIYAN SHUOCHUANG CLOTHING RES INST
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But this method can only be applied to chemical fiber textiles, and the production process is complicated, the production difficulty is high, the yield is low, and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional clothing material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021]A preparation method of a multi-functional clothing material. The cotton fiber base is arranged in an aqueous solution of N-methylmorpholine-N-oxide containing nano-antibacterial agents, guanidine phosphate and lithium sulfate for heat treatment. After the end, it is sequentially cured and Self-cleaning finishing, i.e. a multifunctional garment material. After the N-methylmorpholine-N-oxide aqueous solution is first formed into a film shape on the fabric, it is placed in a coagulation bath of pure deionized water. The NMMO molecules on the surface of the film form hydrogen bonds with water molecules, and the two interact with each other. Interdiffusion occurs, the concentration of NMMO solvent in the membrane liquid decreases, the ability to dissolve fibers is lost, and the fiber plastic film is solidified and formed. This phase transformation gradually penetrates into the interior of the fiber membrane, and finally completes the complete transformation to form a membrane...

Embodiment 2

[0028] A preparation method of a multifunctional clothing material, comprising the steps of:

[0029] 1) Preparation of nano-antibacterial agent: add 9mM silver nitrate solution to the chitosan solution with a concentration of 1.6% according to the volume ratio of 1:1.4, stir evenly and add 0.11M silver nitrate solution dropwise to the mixed solution at a speed of 2 drops / second Sodium borohydride, namely nano antibacterial agent;

[0030] 2) The preparation method of the nano self-cleaning agent is: slowly add n-butyl titanate dropwise into the vigorously stirred acetic acid solution, stir until clarified, and then add a betaine solution with a concentration of 3.0%, wherein n-butyl titanate, acetic acid The volume ratio of betaine solution and betaine solution is 1:8:0.04. After mixing evenly, add it dropwise to vigorously stirred deionized water with a pH of 2. The volume ratio of deionized water to the mixed solution is 1.5:1. Stir until it becomes clear, and seal it for 2...

Embodiment 3

[0035] A preparation method of a multifunctional clothing material, comprising the steps of:

[0036] 1) Preparation of nano-antibacterial agent: add 10mM silver nitrate solution to the chitosan solution with a concentration of 1.8% according to the volume ratio of 1:1.5, stir evenly and add 0.12M silver nitrate solution dropwise to the mixed solution at a speed of 3 drops / second Sodium borohydride, namely nano antibacterial agent;

[0037] 2) The preparation method of the nanometer self-cleaning agent is: slowly drop n-butyl titanate into the vigorously stirred acetic acid solution, stir until clarified, and then add a betaine solution with a concentration of 3.5%, wherein n-tetrabutyl titanate, acetic acid The volume ratio of betaine and betaine solution is 1:10:0.05. After mixing evenly, add it dropwise to vigorously stirred deionized water with a pH of 3. The volume ratio of deionized water to the mixed solution is 2:1. Stir until clear, and seal it for 24 hours. Obtain n...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a multifunctional clothing material and a preparation method thereof, and belongs to the technical field of clothing materials. The multifunctional clothing material is preparedby the steps: placing a cotton fiber base fabric into N-methylmorpholine-N-oxide water solution containing nano-antibacterial agents, guanidine phosphate and lithium sulfate; performing heating treatment and then sequentially performing curing and self-cleaning finishing to obtain the multifunctional clothing material. According to the preparation method of the multifunctional clothing material,cotton fibers can be transformed into regenerated cellulose fibers, formed regenerated cellulose tends to be more uniformly distributed on the surface of a fabric, binding firmness of antibacterial agents and cellulose molecules of the base fabric is enhanced, a prepared nano self-cleaning agent is lasting in effect, the acquired multifunctional clothing material has better mechanical properties,softness, breathability, antibacterial stability, durability and self-cleaning stability.

Description

technical field [0001] The invention belongs to the technical field of clothing materials, and in particular relates to a multifunctional clothing material and a preparation method thereof. Background technique [0002] With the acceleration of the pace of life and the pursuit of high-quality life, people's growing wearing high standards and multiple requirements put forward more and newer clothing requirements for knitted clothing. The development and application of functional knitted fabrics is the current knitting industry. A research hotspot. For example, knitted thermal underwear in winter is mostly thick and difficult to clean, and repeated cleaning will cause loss of wearing performance, and underwear is easy to breed bacteria when worn next to the body, causing degradation and discoloration of the fabric, and endangering human health. Therefore, it has become an important research direction to select composite functional finishing agents to impart antibacterial and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M11/83D06M11/56D06M13/432D06M15/03D06M13/355D06M101/06
CPCD06M11/56D06M11/83D06M13/355D06M13/432D06M15/03D06M16/00D06M2101/06D06M2200/50
Inventor 王硕
Owner HAIYAN SHUOCHUANG CLOTHING RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com