Zirconium metal-organic framework as crystal sponge and preparation method thereof

A technology of metal-organic frameworks and crystals, applied in material analysis using radiation diffraction, analyzing materials, and using wave/particle radiation for material analysis, etc., can solve problems such as unsuitable for single crystal testing and easy loss of crystallinity, and achieve improvement The performance, the preparation method is simple, the effect of strong Zr-O interaction

Active Publication Date: 2019-09-27
JIANGHAN UNIVERSITY
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main reason is that the MOFs matrix easily loses its crystallinity during the post-modification process in a pure organic environment, which is not suitable for single crystal testing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zirconium metal-organic framework as crystal sponge and preparation method thereof
  • Zirconium metal-organic framework as crystal sponge and preparation method thereof
  • Zirconium metal-organic framework as crystal sponge and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Preparation of zirconium metal-organic frameworks

[0044] The preparation method is as follows:

[0045]1. Preparation of 2'-amino-5'-cyano-[1,1':3',1″-terphenyl]-4,4″-dicarboxylic acid:

[0046] (1) Under a nitrogen atmosphere, 3,5-dibromoaminobenzonitrile (16.0mmol), 4-phenylboronic acid methyl formate (38.0mmol), potassium phosphate (93.0mmol), were added to 1,4-dioxane Tetrakis(triphenylphosphine)palladium (1.1mmol) was added into the ring (500mL) solvent, then the temperature was raised to 80°C, refluxed for 45 hours, and cooled to room temperature;

[0047] (2) After removing the organic solvent by rotary evaporation, dichloromethane (100 mL) and H 2 O (50mL), the organic phase was separated, then the aqueous phase was extracted three times with dichloromethane (60mL), the combined organic phases were washed with saturated brine for extraction, and washed with anhydrous MgSO 4 Dry to obtain solution A;

[0048] (3) Solution A was rotary evaporated to remove t...

Embodiment 2

[0055] Preparation of zirconium metal-organic frameworks

[0056] The preparation method is as follows:

[0057] 1. Preparation of 2'-amino-5'-cyano-[1,1':3',1″-terphenyl]-4,4″-dicarboxylic acid:

[0058] (1) Under a nitrogen atmosphere, 3,5-dibromoaminobenzonitrile (16.8mmol), 4-phenylboronic acid methyl formate (40.0mmol), potassium phosphate (95.0mmol), were added to 1,4-dioxane Tetrakis(triphenylphosphine)palladium (1.3mmol) was added to the ring (550mL) solvent, then the temperature was raised to 100°C, refluxed for 50 hours, and cooled to room temperature;

[0059] (2) After removing the organic solvent by rotary evaporation, dichloromethane (100 mL) and H 2 O (50mL), the organic phase was separated, then the aqueous phase was extracted three times with dichloromethane (60mL), the combined organic phases were washed with saturated brine for extraction, and washed with anhydrous MgSO 4 Dry to obtain solution A;

[0060] (3) Solution A was rotary evaporated to remove t...

Embodiment 3

[0067] Preparation of zirconium metal-organic frameworks

[0068] The preparation method is as follows:

[0069] 1. Preparation of 2'-amino-5'-cyano-[1,1':3',1″-terphenyl]-4,4″-dicarboxylic acid:

[0070] (1) Under a nitrogen atmosphere, 3,5-dibromoaminobenzonitrile (16.4mmol), 4-phenylboronic acid methyl formate (39.0mmol), potassium phosphate (94.0mmol), were added to 1,4-dioxane Add tetrakis(triphenylphosphine)palladium (1.2mmol) into the ring (530mL) solvent, then raise the temperature to 90°C, reflux for 48 hours, and cool to room temperature;

[0071] (2) After removing the organic solvent by rotary evaporation, dichloromethane (100 mL) and H 2 O (50mL), the organic phase was separated, then the aqueous phase was extracted three times with dichloromethane (60mL), the combined organic phases were washed with saturated brine for extraction, and washed with anhydrous MgSO 4 Dry to obtain solution A;

[0072] (3) Solution A was rotary evaporated to remove the organic sol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a zirconium metal-organic framework as crystal sponge and a preparation method thereof, and belongs to the field of metal-organic frameworks. The chemical formula of the zirconium metal-organic framework is [Zr6(u3-O)4(u3-OH)4(OH)2(H2O)2(HCOO)2(L)4]n, wherein L is 2'-amino-5'-cyano-[1,1':3',1''-terphenyl]-4,4''-dicarboxylic acid, and n is infinity. The overall framework structure is a quadruple intercalation metal organic framework, the zirconium metal-organic framework belongs to the trigonal system, the space group is R-3c, the unit cell parameter is alpha=beta=90 degrees, gamma=120 degrees, and the unit cell volume is the structure of iodine after the zirconium metal organic framework provided by the embodiment can be used as the crystal sponge to absorb iodine molecules and the adsorption is characterized by a single crystal X-ray diffraction technique. According to the invention, the application range of the metal-organic framework in characterizing guest molecules, especially for inorganic materials dissolved in non-pure organic solvents.

Description

technical field [0001] The invention relates to the field of metal organic framework materials, in particular to a zirconium metal organic framework material as crystal sponge and a preparation method thereof. Background technique [0002] Metal-organic frameworks (MOFs), as one of the current hot research materials, have unique application prospects in many fields due to their specific framework structure and channel effect. Metal-organic frameworks have a highly ordered spatial configuration, stable pore structure, excellent adsorption performance, and periodically repeated component arrangements, and can fully explore their structural differences at the atomic level by using single crystal diffraction techniques. Studies have begun to explore the use of MOFs as carriers to test the related research of guest molecules. This strategy is called crystal sponge. The advantage of this technique is that it can clearly characterize the relevant configuration and other structural...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G83/00G01N23/2055
CPCC08G83/008G01N23/20G01N23/2005G01N2223/056G01N2223/1016G01N2223/604
Inventor 余凡胡思前刘继延
Owner JIANGHAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com