A kind of inorganic mineral plate and coating method thereof

A technology of inorganic minerals and coating methods, which is applied to special decorative structures, devices for coating liquid on the surface, and coatings. The effect of simple method and simple production equipment

Active Publication Date: 2020-04-24
FOSHAN YIKEJU NEW MATERIAL CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The first technical problem to be solved by the present invention is to provide a coating method for inorganic mineral plates, the method is simple, the process is controllable, and powder coatings can be used to perform various decorative effects on the surface of inorganic mineral plates, solving the problem of powder coatings and inorganic mineral plates. Mineral plates are difficult to match

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of inorganic mineral plate and coating method thereof
  • A kind of inorganic mineral plate and coating method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example

[0073] As a preferred embodiment of the present invention, the raw materials of the ultra-low temperature powder coating include: polyester resin, epoxy resin and auxiliary agent, and the auxiliary agent includes one or more of a catalyst, an anti-sticking agent and a defoaming agent .

[0074] Wherein, the main material of the ultra-low temperature powder coating is the main polyester resin containing carboxyl group, the glass transition temperature is 40-60°C, the acid value is 10-75mgKOH / g, and the curing temperature is 90-130°C. Then use low-temperature curing (80-90 ℃) liquid or low-viscosity solid epoxy resin, and use high-efficiency catalyst to carry out low-temperature ring-opening reaction on epoxy resin, add a new type of defoamer for degassing and defoaming, and add a new type of anti-foaming agent. Adhesive to better solve sticking and clumping problems.

[0075] Specifically, the catalyst can be selected from 2-methylimidazole, 2-phenylimidazoline, tertiary amine...

Embodiment 1

[0113] (1) Select calcium silicate fiberboard, and carry out dust removal and cleaning treatment;

[0114] (2) Carry out sticker sealing treatment on the silicon-calcium fiberboard after dust removal and cleaning;

[0115] (3) Carry out preheating treatment on the surface of calcium silicate fiberboard after sealing treatment to improve the surface conductivity of calcium silicate fiberboard, wherein the temperature of preheating treatment is 60°C, and the preheating time is 10 minutes;

[0116] (4) Apply commercially available ultra-low temperature powder paint to the surface of the preheated calcium-silicon fiberboard for one or more times to form a powder coating, wherein the spray particle size of the ultra-low temperature powder paint is 5-25 μm, and the D90 is less than 25μm, the glass transition temperature is 40°C, the gelation time is 50s at 110°C, the curing temperature is 95°C, and the curing time is 4min;

[0117] (5) Curing the powder coating on the surface of ca...

Embodiment 2

[0121] (1) Select gypsum fiberboard and carry out dust removal and cleaning treatment;

[0122] (2) Sealing the gypsum fiberboard coated with ultraviolet radiation curing paint after dust removal and cleaning;

[0123] (3) Perform preheating treatment on the surface of the gypsum fiberboard after sealing treatment to increase the surface conductivity of the gypsum fiberboard, wherein the temperature of the preheating treatment is 70°C, and the preheating time is 3 minutes;

[0124] (4) The preheated gypsum fiberboard surface is coated with commercially available ultra-low temperature powder coating one or more times to form a powder coating, wherein the ultra-low temperature powder coating has a spray particle size of 5-25 μm and a D90 of less than 25 μm , the glass transition temperature is 50°C, the gelling time is 100s at 110°C, the curing temperature is 110°C, and the curing time is 5min;

[0125] (5) Curing the powder coating on the surface of the gypsum fiberboard;

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
acid valueaaaaaaaaaa
cure temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a coating method of an inorganic mineral plate. The coating method comprises the following steps of (1) selecting the inorganic mineral plate and carrying out dust removal and cleaning treatment, (2) sealing the inorganic mineral plates, (3) preheating the surface of the inorganic mineral plate to improve the surface conductivity of the inorganic mineral plate, (4) coating the surface of the inorganic mineral plate with ultra-low temperature powder paint for one or more times to form a powder coating, (5) curing the powder coating on the surface of the inorganic mineral plate, (6) decorating the inorganic mineral plate, and (7) carrying out quality inspection and packaging on the inorganic mineral plate to obtain a finished product. The invention further provides an inorganic mineral plate prepared by the coating method. With the adoption of the coating method, the method is simple, the process is controllable, various decorative effects can be achieved on the surface of the inorganic mineral plate by using the powder coating, and the problem that the powder coating and the inorganic mineral plate are difficult to match is solved.

Description

technical field [0001] The invention relates to the technical field of printed boards, in particular to an inorganic mineral board and a coating method thereof. Background technique [0002] Panels are flat, rectangular panels of building material in preset sizes, used in the construction industry as elements for walls, ceilings or floors. [0003] Boards include organic boards and inorganic boards. At present, the mainstream inorganic boards include calcium silicate fiberboard, gypsum fiberboard, calcium silicate board and magnesia board. Compared with organic boards, inorganic boards have the following outstanding features: 1. Class A non-combustible: traditional MDF with fireproof leather veneer can reach Class B flame retardant, while inorganic boards have the characteristics of Class A non-combustible, and the thickness of 10mm can be easily Reach the flame retardant limit of 3 hours. 2. Waterproof and moisture-proof: The material of the inorganic board is characteriz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B05D7/24B05D1/12B05D3/02B05D3/04B05D7/00C09D167/00C09D163/00C09D5/03C09D7/61C04B41/52C04B41/00B44C5/04B44C1/24
CPCB05D1/12B05D3/0218B05D3/0263B05D3/0413B05D7/24B05D7/536B05D2203/30B05D2401/32B05D2504/00B05D2508/00B44C1/24B44C5/04C04B41/0072C04B41/4545C04B41/52C04B2111/27C08K2003/2227C08K2201/011C08L2205/03C09D5/033C09D163/00C09D167/00B05D2420/01C08L63/00C08K3/36C08K3/22C08L67/00
Inventor 伍明
Owner FOSHAN YIKEJU NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap