Composite rubber material and preparation method thereof

A composite material and rubber technology, applied in the field of rubber composite materials, can solve problems such as the inability to effectively meet the noise reduction requirements of reactors, poor mechanical properties and damping properties of nitrile rubber, and achieve the purpose of reducing noise and vibration, improving mechanical properties, The effect of meeting the needs of noise reduction

Inactive Publication Date: 2019-09-10
GLOBAL ENERGY INTERCONNECTION RES INST CO LTD +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the problems of poor mechanical properties and damping properties of nitrile rubber in the prior art, and can not effectively meet the noise reduction requirements of reactors, thereby providing a rubber composite material and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite rubber material and preparation method thereof
  • Composite rubber material and preparation method thereof
  • Composite rubber material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] This embodiment provides an oil-resistant damping sound-insulating rubber composite material for the inner wall of the reactor oil tank, including the following raw materials:

[0038]

[0039] The preparation method of above-mentioned rubber composite material: comprise the steps:

[0040] 1) The nitrile rubber is masticated by the open mill, and the masticated nitrile rubber is coated on the roller, and the active agent, the accelerator, the anti-aging agent, and the reinforcing filler are added to the masticated nitrile rubber in sequence and vulcanizing agent are mixed to obtain rubber compound;

[0041]2) Put the mixed rubber obtained in step 1) for 24 hours, and then use a flat vulcanizer to perform vulcanization and compression molding at a vulcanization temperature of 165° C., a vulcanization pressure of 15 MPa, and a vulcanization time of 20 minutes to obtain the rubber composite material.

Embodiment 2

[0043] This embodiment provides an oil-resistant damping sound-insulating rubber composite material for the inner wall of the reactor oil tank, including the following raw materials:

[0044]

[0045] The preparation method of above-mentioned rubber composite material: comprise the steps:

[0046] 1) The nitrile rubber is masticated by the open mill, and the masticated nitrile rubber is coated on the roller, and the active agent, the accelerator, the anti-aging agent, and the reinforcing filler are added to the masticated nitrile rubber in sequence and vulcanizing agent are mixed to obtain rubber compound;

[0047] 2) Put the mixed rubber obtained in step 1) for 24 hours, and then use a flat vulcanizer to perform vulcanization and compression molding at a vulcanization temperature of 165° C., a vulcanization pressure of 15 MPa, and a vulcanization time of 20 minutes to obtain the rubber composite material.

Embodiment 3

[0049] This embodiment provides an oil-resistant damping sound-insulating rubber composite material for the inner wall of the reactor oil tank, including the following raw materials:

[0050]

[0051]

[0052] The preparation method of above-mentioned rubber composite material: comprise the steps:

[0053] 1) The nitrile rubber is masticated by the open mill, and the masticated nitrile rubber is coated on the roller, and the active agent, the accelerator, the anti-aging agent, and the reinforcing filler are added to the masticated nitrile rubber in sequence and vulcanizing agent are mixed to obtain rubber compound;

[0054] 2) Put the mixed rubber obtained in step 1) for 24 hours, and then use a flat vulcanizer to perform vulcanization and compression molding at a vulcanization temperature of 165° C., a vulcanization pressure of 15 MPa, and a vulcanization time of 20 minutes to obtain the rubber composite material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of composite rubber materials and in particular relates to a composite rubber material and a preparation method thereof. The composite rubber material provided by the invention comprises the following raw materials in parts by weight: 100 parts of butadiene-acrylonitrile rubber, 3-5 parts of a vulcanizing agent, 2-8 parts of an active agent, 0.5-2 partsof an accelerant, 1-2 parts of an anti-aging agent and 5-10 parts of montmorillonite. A montmorillonite reinforcing filler is added to be matched with the butadiene-acrylonitrile rubber so as to forma nano composite material with an intercalated structure, so that the mechanical property, oil resistance, damping capacity and sound insulation property of the butadiene-acrylonitrile rubber composite material can be effectively improved, and noise reduction requirements of electric reactors are effectively met. The prepared composite rubber material is an excellent-performance oil-resistant damping sound-insulation composite material for inner walls of electric reactor tanks.

Description

technical field [0001] The invention relates to the technical field of rubber composite materials, in particular to a rubber composite material and a preparation method thereof, and further relates to an oil-resistant damping sound-insulating rubber composite material for the inner wall of a reactor oil tank and a preparation method thereof. Background technique [0002] With the continuous increase of power demand, the noise problem of substations is becoming more and more obvious. At present, auxiliary noise control measures are often used for noise control of substations, such as the use of a large number of sound-absorbing materials, sound insulation components, and noise reduction devices to block noise transmission. Approach; In order to effectively block the noise passage, people will also adopt measures such as sound insulation cover and large sound insulation room, but this will bring problems such as poor heat dissipation, high cost, and difficult maintenance. Afte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L9/02C08K13/06C08K3/22C08K5/09C08K5/14C08K9/04C08K3/34B29C35/02
CPCB29C35/02C08K3/22C08K3/346C08K5/09C08K5/14C08K9/04C08K13/06C08K2003/2296C08K2201/014C08L9/02
Inventor 侯东聂京凯邱宁王广克韩钰陈新樊超田一刘晓圣何强
Owner GLOBAL ENERGY INTERCONNECTION RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap