Far infrared thermal-sensing physical therapy paste and preparing method thereof
A technology of far-infrared and physiotherapy stickers, which is applied in the field of medical biopolymer materials, can solve the problems of limitation, inability to continuously achieve the application of temperature-sensitive physiotherapy, heat-generating materials that easily burn the skin, etc., so as to facilitate control and improve the human blood circulation system , Promote the effect of transdermal absorption
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0033] A kind of far-infrared temperature-sensing physiotherapy paste, comprising non-woven fabric backing layer, gel layer and release layer, described release layer is CPP embossed film, and its position is positioned at the upper layer of gel layer, described non-woven The cloth backing layer is located in the lower layer of the gel layer, and the gel layer is composed of the following raw materials and their proportions in parts by weight: 10 parts of sodium polyacrylate, 8 parts of turpentine, 1 part of composite crosslinking agent, and 15 parts of moisturizing agent , 0.5 parts of thickener, 0.01 parts of preservative, 3 parts of tartaric acid, 20 parts of temperature-sensitive active materials, and 20 parts of deoxygenated deionized water. Wherein, the moisturizing agent is glycerin, the composite crosslinking agent is a mixture of aluminum glyoxate and dihydroxyaluminum aminoacetate in a weight ratio of 1:1, and the thickener is polyvinylpyrrolidone; Described preserva...
Embodiment 2
[0040] A kind of far-infrared temperature-sensing physiotherapy paste, comprising non-woven fabric backing layer, gel layer and release layer, described release layer is CPP embossed film, and its position is positioned at the upper layer of gel layer, described non-woven The cloth backing layer is located in the lower layer of the gel layer, and the gel layer is composed of the following raw materials and their proportions in parts by weight: 15 parts of sodium polyacrylate, 5 parts of turpentine, 2 parts of composite crosslinking agent, and 10 parts of moisturizing agent , 0.1 part of thickener, 0.05 part of preservative, 2 parts of tartaric acid, 10 parts of temperature-sensitive active material, and 10 parts of deoxygenated deionized water. Wherein, the moisturizing agent is glycerin, the composite crosslinking agent is a mixture of aluminum glycolate and dihydroxyaluminum aminoacetate in a weight ratio of 1:5, and the thickener is polyvinylpyrrolidone and Carboxymethylcel...
Embodiment 3
[0047] A kind of far-infrared temperature-sensing physiotherapy paste, comprising non-woven fabric backing layer, gel layer and release layer, described release layer is CPP embossed film, and its position is positioned at the upper layer of gel layer, described non-woven The cloth backing layer is located in the lower layer of the gel layer, and the gel layer is composed of the following raw materials and their proportions in parts by weight: 18 parts of sodium polyacrylate, 10 parts of turpentine, 2 parts of composite crosslinking agent, and 5 parts of moisturizing agent , 1 part of thickener, 0.5 part of preservative, 5 parts of tartaric acid, 15 parts of temperature-sensitive active material, and 18 parts of deoxygenated deionized water. Wherein, the moisturizing agent is glycerin, the composite crosslinking agent is a mixture of aluminum glycolate and dihydroxyaluminum aminoacetate in a weight ratio of 1:2, and the thickener is polysodium alginate ; The preservative is io...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com