A yarn and linear density technology, applied in the field of textile manufacturing, can solve problems such as unsuitability for large-scale production, complicated process processing, and excessive additives in the production process

Inactive Publication Date: 2019-06-07
YIBIN HUIMEI WORSTED TECH
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this technical scheme, wool fiber, bamboo charcoal polyester fiber and polylactic acid fiber are used as raw materials, and the anti-pilling, anti-pilling and Soft, smooth and plump, but the production process has too many additives, complicated process, and has requirements for raw materials, so it is not suitable for large-scale production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Yarn and preparing method
  • Yarn and preparing method
  • Yarn and preparing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0103] A yarn, prepared by air spinning, comprising:

[0104] 40 pieces, evenness CV% is 12.5~16.5%, -50% detail is 4~50 pcs / 1000m, +50% thick place is 12~70 pcs / 1000m, +200% nep is 10~68 pcs / 1000m , +280% neps are 3-25 / 1000m; hairiness index is 2.0-2.5, pilling resistance is 2.0-3.5, coefficient of variation of dry breaking strength is 7-12%, dry breaking strength is 11-16 CN / tex, the dry elongation at break is 6.0-13.2%, and the average linear density is 14.68-14.83tex.

Embodiment 2

[0106] A yarn, prepared by air spinning, comprising:

[0107] 40 pieces, evenness CV% is 12.5~16.5%, -50% detail is 4~50 pcs / 1000m, +50% thick place is 12~70 pcs / 1000m, +200% nep is 10~68 pcs / 1000m , +280% neps are 3-25 / 1000m; hairiness index is 2.0-2.5, pilling resistance is 2.0-3.5, coefficient of variation of dry breaking strength is 7-12%, dry breaking strength is 11-16 CN / tex, the dry elongation at break is 6.0-13.2%, and the average linear density is 14.68-14.83tex.

Embodiment 3

[0109] A yarn, prepared by air spinning, comprising:

[0110] 40 pieces, evenness CV% is 12.5~16.5%, -50% detail is 4~50 pcs / 1000m, +50% thick place is 12~70 pcs / 1000m, +200% nep is 10~68 pcs / 1000m , +280% neps are 3-25 / 1000m; hairiness index is 2.0-2.5, pilling resistance is 2.0-3.5, coefficient of variation of dry breaking strength is 7-12%, dry breaking strength is 11-16 CN / tex, the dry elongation at break is 6.0-13.2%, and the average linear density is 14.68-14.83tex.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Dry breaking strengthaaaaaaaaaa
Breaking strengthaaaaaaaaaa
Linear densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a yarn and a preparing method, and belongs to the technical field of textile manufacturing. According to the preparing method, viscose staple fibers serve as raw materials, andviscose staple fiber card slivers are obtained through opening and carding into slivers; then two or more viscose staple fiber card slivers are subjected to primary drawing and secondary drawing, andthen rotor spinning or vortex spinning or ring spinning is conducted to prepare the yarn. According to the indexes of the finished yarn product, the hairness index is 2.0-4.0, the pilling resistancereaches the level 2.5-4, the breaking strength variation coefficient is 5.8-12%, the dry breaking strength is 10.7-16 CN / tex, the dry elongation at break is 6-13%, and the linear density is 9.84-84.96tex. The yarn has the advantages of high strength, low elongation, good softness, good pilling resistance and the like, the market requirement is met, and the living standard of people is improved.

Description

technical field [0001] The invention relates to a yarn and a preparation method, in particular to a yarn with high-strength elongation viscose staple fiber as a raw material and a preparation method, belonging to the technical field of textile manufacturing. Background technique [0002] High-strength and low-elongation viscose staple fiber (product name: Yacel) is made of 100% natural bio-based materials. It is a kind of strength and elongation index similar to Modal fiber. It has good water absorption, air permeability, and skin-friendly Sexual new textile fiber raw materials. It has high strength and low elongation fiber characteristics, and its dry breaking strength and wet breaking strength are about 40% higher than ordinary bio-based short fibers. It can be widely used in vortex spinning, siro spinning and siro compact spinning 80S In the above high-count yarn field, the product price is 5,000 yuan per ton lower than that of modal fiber, which has a very high cost per...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D02G3/02
Inventor 黄政张洪卫赵聪杨玉兰
Owner YIBIN HUIMEI WORSTED TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap