Method of detecting silver ions and serine based on mercaptosuccinic acid-modified CdTe quantum dot paper core sheet
A technology of mercaptosuccinic acid and quantum dots, which is applied in the field of paper chip sensing, can solve the problems of cumbersome operation procedures, complicated and precise instruments, insufficient to meet the fast field detection of silver ions, etc., and achieves high sensitivity and selectivity. The effect of fast and fast on-site inspection
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0045] The preparation method of the paper chip of CdTe quantum dots modified with mercaptosuccinic acid includes the steps:
[0046] (1) Preparation of CdTe quantum dots (TMA-capped CdTe) modified with mercaptosuccinic acid
[0047] Dissolve cadmium dichloride (0.1142g, 12.5mM) and mercaptosuccinic acid (0.0901g, 15mM) in 40mL ultrapure water, adjust the pH of the solution to 11, and then stir in an ice bath with nitrogen for 20 minutes, and add tellurium Sodium (0.0216g, 2.5mM), stir for 15 minutes, then add sodium borohydride (0.0113g, 7.5mM), stir for 15 minutes to obtain a mixed solution, and finally put the mixed solution into the reaction kettle, in an oven at 200℃ React for 50 minutes and cool to room temperature to obtain 7.10×10 -5 CdTe quantum dots modified with mol / L mercaptosuccinic acid. Use a transmission electron microscope to observe, such as figure 2 As shown, the transmission electron microscope characterizes the particle size of 3~5nm.
[0048] (2) Preparation ...
Embodiment 2
[0051] The method for detecting silver ions based on the CdTe quantum dot paper chip modified by mercaptosuccinic acid includes the steps:
[0052] (1) Preparation of CdTe quantum dots (TMA-capped CdTe) modified with mercaptosuccinic acid
[0053] Dissolve cadmium dichloride (0.1142g, 12.5mM) and mercaptosuccinic acid (0.0901g, 15mM) in 40mL ultrapure water, adjust the pH of the solution to 11, and then stir in an ice bath with nitrogen for 20 minutes, and add tellurium Sodium (0.0216g, 2.5mM), stir for 15 minutes, then add sodium borohydride (0.0113g, 7.5mM), stir for 15 minutes to obtain a mixed solution, and finally put the mixed solution into the reaction kettle, in an oven at 200℃ React for 50 minutes and cool to room temperature to obtain 7.10×10 -5 CdTe quantum dots modified with mol / L mercaptosuccinic acid. Use a transmission electron microscope to observe, such as figure 2 As shown, the transmission electron microscope characterizes the particle size of 3~5nm.
[0054] (2...
Embodiment 3
[0065] The method for detecting serine based on the CdTe quantum dot paper chip modified by mercaptosuccinic acid includes the steps:
[0066] (1) Preparation of CdTe quantum dots (TMA-capped CdTe) modified with mercaptosuccinic acid
[0067] Dissolve cadmium dichloride (0.1142g, 12.5mM) and mercaptosuccinic acid (0.0901g, 15mM) in 40mL ultrapure water, adjust the pH of the solution to 11, and then stir in an ice bath with nitrogen for 20 minutes, and add tellurium Sodium (0.0216g, 2.5mM), stir for 15 minutes, then add sodium borohydride (0.0113g, 7.5mM), stir for 15 minutes to obtain a mixed solution, and finally put the mixed solution into the reaction kettle, in an oven at 200℃ React for 50 minutes and cool to room temperature to obtain 7.10×10 -5 CdTe quantum dots modified with mol / L mercaptosuccinic acid. Based on transmission electron microscope observation, such as figure 2 As shown, the transmission electron microscope characterizes the particle size of 3~5nm.
[0068] (2)...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
emission peak | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com