Composite macromolecule water-absorbent resin containing nitrogen and potassium and preparation method of resin

A polymer water absorption, composite technology, applied in chemical instruments and methods, fertilizer mixtures, other chemical processes, etc., can solve the problems of easy mildew, low water absorption rate of resin, low water absorption rate, etc., and achieve good adhesion. Effect

Active Publication Date: 2019-05-31
SHANXI UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

(2) Graft copolymerization of starch with acrylic acid, acrylonitrile and other monomers. This kind of resin has good environmental protection. The disadvantage is that the resin has low water absorption and is easy to mildew
(3) Cellulose is copolymerized with monomers such as acrylic acid and acrylonitrile, which is easy to biodegrade, and the disadvantage is low water absorption

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] In a reaction vessel equipped with a condensing device and a stirring device, 300 g of reaction medium corn oil, 9 g of pentaerythritol tetraisostearate and 3 g of calcium carbonate were added, and the temperature was raised to 70° C. for mixing. Take another 30g of N-tert-octyl acrylamide, 10g of 3-propyl methacrylate potassium salt, 0.009g of N,N'-ethylenebisstearamide and 0.15g of 2,2-azo(2- Methylpropylimidium) dihydrochloride was dissolved in 100 g of distilled water, then added to the reaction vessel, and polymerized at 70° C. for 4 hours. After the reaction, the product is filtered, washed and dried to obtain a composite polymer water-absorbent resin.

[0022] Water absorption test:

[0023] time / h

Embodiment 2

[0025] In a reaction vessel equipped with a condensing device and a stirring device, add 500 g of reaction medium corn oil, 25 g of pentaerythritol tetraisostearate and 5 g of calcium carbonate, heat up to 70° C. and mix well. Take another 30g of N-tert-octyl acrylamide, 10g of 3-sulfonic acid propyl potassium salt, 0.015g of N,N'-ethylenebisstearamide and 0.3g of 2,2-azo(2- Methylpropylimidium) dihydrochloride was dissolved in 100 g of distilled water, then added to the reaction vessel, and polymerized at 70° C. for 4 hours. After the reaction, the product is filtered, washed and dried to obtain a composite polymer water-absorbent resin.

[0026] Water absorption test:

[0027] time / h

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to view more

Abstract

The invention discloses a composite macromolecule water-absorbent resin containing nitrogen and potassium and a preparation method of the resin. The preparation method includes the steps: adding a certain quantity of reaction media, dispersing agents and calcium carbonate into a reaction vessel provided with a condensing unit and a stirring device; heating and uniformly mixing the materials. In addition, a certain quantity of nitric monomers and methacrylic 3-potassium propyl sulfonate salt, crosslinking agents and initiators are taken, dissolved in distilled water, added into the reaction vessel and polymerized for several hours. After reaction, products are filtered, washed and dried to obtain the macromolecule water-absorbent resin. The macromolecule water-absorbent resin is simple in preparation technology and suitable for industrial production. The prepared macromolecule water-absorbent resin is high in water absorption and long in water retention time, and contains nitrogen and potassium needed by plant growth. The macromolecule water-absorbent resin has a good application prospect in aspects of land desertification controlling, soil water retention, vegetation transplantation and the like.

Description

technical field [0001] The invention relates to a polymer water-absorbing material, in particular to a composite polymer water-absorbing resin containing nitrogen and potassium and a preparation method thereof. The water-absorbing resin has good application prospects in land desertification control, soil water conservation, vegetation transplantation and the like. Background technique [0002] Water-absorbing resin is a water-swellable polymer material that has emerged in recent years. It has special water-absorbing properties and is widely used in chemical engineering, sewage treatment, dust suppression and sand fixation, farmland and gardens, etc. As functional materials, water-absorbent resins are mostly prepared by monomer polymerization, and the monomers often have hydrophilic groups, such as sulfonic acid groups, carboxyl groups, hydroxyl groups, amino groups, etc. grid. Compared with traditional water-absorbing materials such as cotton, hemp, fiber, etc., it has inc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/54C08F220/38C08F2/44C08K3/26C09K17/20C09K105/00
Inventor 尚成新
Owner SHANXI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap