Elastic knitted fabric and preparation method thereof

A knitted fabric and elastic technology, applied in knitting, weft knitting, warp knitting, etc., can solve the problems of increasing fabric processing procedures and processing costs, loss of fabric elasticity, and easy aging of spandex, so as to maintain permanence and save processing Cost, not easy to aging effect

Active Publication Date: 2019-05-24
WUXI HANUO TEXTILE TECH
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the addition of spandex in the existing elastic knitted fabric, the spandex is easy to age after repeated stretching, resulting in a great loss of fabric elasticity, and the need to obtain a plush structure through napping treatment, which increases the fabric processing process and processing costs. Problem, the present invention provides an elastic knitted fabric, the elasticity of which will not be lost even after being stretched many times, and has its own fluff structure, which does not require napping treatment. At the same time, the present invention also provides this elastic knitted fabric preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A method for preparing an elastic knitted fabric, comprising the following steps: rough weaving→width cutting→presetting→dyeing→dehydration→finished product shaping→packaging. In the rough weaving step, high F-number yarns and elastic shrinkage yarns are selected as raw materials, wherein, 50D / 72F polyester yarn and 75D / 48F polyester yarn are used for high F-number yarn, the elastic shrinkage yarn is 100D / 48F PTT / PET blended filament, and when threading on the loom, the elastic shrinkage yarn has a high line length ratio The thread length of F number yarn is increased by 10%, and then weaves double-sided fabric, the inner layer is woven with 50D / 72F polyester yarn, and the outer layer is woven with 75D / 48F polyester yarn and 100D / 48F PTT / PET blended filament Weaving; the cutting width adopts conventional technology; in the pre-setting step, the setting temperature is 150°C, and the frame width of the pre-setting machine is set to 90% of the width of the blank of the fabr...

Embodiment 2

[0023] A method for preparing an elastic knitted fabric, comprising the following steps: rough weaving→width cutting→presetting→dyeing→dehydration→finished product shaping→packaging, in the rough weaving step, high F-number yarns, ordinary yarns and elastic shrinkage yarns are selected as Raw materials, among them, the high F number yarn is made of 50D / 48F polyester yarn, the ordinary yarn is made of 75D / 36F nylon yarn, and the elastic shrinkage yarn is 100D / 48F PBT / PET blended filament, and when threading on the loom, The line length of the elastic shrinkage yarn is 20% longer than the line length of the high F number yarn, and the line length of the ordinary yarn is equal to the line length of the high F number yarn, and then weaves a double-sided fabric, and the inner layer is made of 50D / 48F polyester yarn The outer layer is woven with 75D / 36F nylon yarn and 100D / 48F PBT / PET blended filament; the cutting width adopts the conventional process; in the pre-setting step, the se...

Embodiment 3

[0025] A method for preparing an elastic knitted fabric, comprising the following steps: rough weaving→width cutting→presetting→dyeing→dehydration→finished product shaping→packaging. In the rough weaving step, high F-number yarns and elastic shrinkage yarns are selected as raw materials, wherein, 75D / 48F polyester yarn and 100D / 96F polyester yarn are used for high F-number yarn, and the elastic shrinkage yarn is 150D / 72F PBT / PET blended filament, and when threading on the loom, the elastic shrinkage yarn has a high line length ratio The thread length of the F number yarn is increased by 30%, and then weaves double-sided fabric, the inner layer is made of 75D / 48F polyester yarn, the outer layer is woven with 100D / 96F polyester yarn and 150D / 72F PBT / PET blended filament ;The cutting width adopts the conventional process; in the pre-setting step, the setting temperature is 160°C, and the frame width of the pre-setting machine is set to 95% of the width of the blank of the fabric; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
shrinkageaaaaaaaaaa
Login to view more

Abstract

The invention provides elastic knitted fabric, and solves problems in existing elastic knitted fabric that spandex is easily aged after multiple times of stretching because the spandex is added, so that fabric elasticity is greatly lost, and a plush structure can be obtained only through napping raising treatment, fabric processing procedures and processing cost are increased. A fabric rough blankof the fabric is formed by interweaving a high F-number yarn and an elastic shrinking yarn, or formed by co-interweaving the high F-number yarn, a common yarn and the elastic shrinking yarn. The highF-number yarn is a yarn of which a D/F range is within 0.5-1.6. The elastic shrinking yarn is a PTT/PET blending filament or a PBT/PET blending filament. The fabric rough blank is shrunk on the surface of an inner layer after dyed so as to form naps. In addition, the invention further provides a preparation method for the fabric.

Description

technical field [0001] The invention relates to the field of knitted fabrics, in particular to an elastic knitted fabric and a preparation method thereof. Background technique [0002] Spandex has excellent elastic properties, so most of the existing elastic knitted fabrics are added with spandex, but because the fabric is often subjected to stretching force during use, spandex is easy to age after repeated stretching, resulting in a great loss of fabric elasticity. Seriously affect the use of fabrics, and if you want to form a plush structure on the surface of the fabric to improve the skin-friendly and thermal performance of the fabric, you also need to dye the fabric, set the shape and then perform napping treatment, which increases the fabric processing and processing costs. Contents of the invention [0003] Aiming at the addition of spandex in the existing elastic knitted fabric, the spandex is easy to age after repeated stretching, resulting in a great loss of fabri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/14D04B1/16D04B1/18D04B1/04D04B21/04D06C7/02
Inventor 姚馨馨赵衡过志良冯培生
Owner WUXI HANUO TEXTILE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products