A kind of preparation method of oil-water separation membrane based on superhydrophobic superoleophilic oil-water separation membrane modified by tannic acid

A technology for separating omentum and tannic acid from oil and water, which is applied in the direction of separation methods, liquid separation, semipermeable membrane separation, etc., can solve the problems of cumbersome preparation process, high cost, unsuitable for industrial production and application, and achieve simple preparation process, Easy to operate and avoid the effect of surface microstructure construction process

Active Publication Date: 2021-11-16
刘云晖
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the field of oil-water separation, there have been many literature and patent reports on superhydrophobic and superoleophilic functional surfaces based on dopamine surface modification, but there are still problems such as cumbersome preparation process, high cost, and unsuitability for industrial production and application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of oil-water separation membrane based on superhydrophobic superoleophilic oil-water separation membrane modified by tannic acid
  • A kind of preparation method of oil-water separation membrane based on superhydrophobic superoleophilic oil-water separation membrane modified by tannic acid
  • A kind of preparation method of oil-water separation membrane based on superhydrophobic superoleophilic oil-water separation membrane modified by tannic acid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) Clean the 400-mesh stainless steel mesh and dry it for later use.

[0029] (2) Dissolving tannic acid in water, adjusting the pH to 8.5 to obtain a tannic acid solution with a mass percentage of tannic acid of 5%; dissolving ferric chloride in water to obtain a mass percentage of iron ions Be 1% iron ion solution; Cetylamine is dissolved in ethanol to obtain a long-chain alkylamine solution whose mass percentage of cetylamine is 8%;

[0030] (3) Soak the dried stainless steel mesh in the tannic acid solution, soak for 1 hour, take it out and dry it; then soak it in the iron ion solution, soak it for 10 seconds, take it out and dry it; repeat this process twice; After taking it out, it was dried in a drying oven at 60° C. for 2 hours to obtain a tannic acid-modified fabric web.

[0031] (4) Soak the tannic acid-modified fabric net obtained in step (3) in the long-chain alkylamine solution, react at 60°C for 12 hours, take it out, and dry it in a drying oven at 80°C ...

Embodiment 2

[0034] (1) Clean the 300-mesh PET non-woven net and dry it for later use.

[0035] (2) Dissolving tannic acid in water, adjusting the pH to 8.3 to obtain a tannic acid solution with a mass percentage of tannic acid of 10%; dissolving ferric chloride in ethanol to obtain a mass percentage of iron ions Content is the iron ion solution of 1%; Cetylamine is dissolved in ethanol, and the mass percentage composition that obtains cetylamine is the long-chain alkylamine solution of 5%;

[0036] (3) Soak the dried PET non-woven fabric in the tannic acid solution, soak for 30 seconds, take it out and dry it; then soak it in the iron ion solution, soak it for 30 seconds, take it out and dry it; repeat the process 4 times; take it out and dry it in a drying oven at 60° C. for 8 hours to obtain a tannic acid modified fabric net.

[0037] (4) Soak the tannic acid modified fabric net obtained in step (3) in the long-chain alkylamine solution, react at 60°C for 30 hours, take it out, and dry...

Embodiment 3

[0039] (1) Clean the 350-mesh copper mesh and dry it for later use.

[0040] (2) Dissolve tannic acid in water and adjust the pH to 9.0 to obtain a tannic acid solution with a mass percentage of tannic acid of 3%; dissolve ferric chloride in ethanol to obtain a mass percentage of iron ions Content is the iron ion solution of 2%; Cetylamine is dissolved in ethanol, and the mass percent composition that obtains cetylamine is the long-chain alkylamine solution of 8%;

[0041] (3) Soak the dried copper mesh in the tannic acid solution, soak for 30 seconds, take it out and dry it; then soak it in the iron ion solution, soak it for 1 second, take it out and dry it; this process is repeated 5 times; After taking it out, it was dried in a drying oven at 80° C. for 8 hours to obtain a tannic acid-modified fabric web.

[0042] (4) Soak the tannic acid-modified fabric net obtained in step (3) in the long-chain alkylamine solution, react at 70°C for 20 hours, take it out, and dry it in a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a superhydrophobic superlipophilic oil-water separation omentum modified by tannic acid. The invention uses natural polyphenol tannic acid and long-chain alkylamine to modify the surface of the omentum material, and at the same time realizes the "micro-nano structure" and "low surface energy" of the material surface, and prepares a super-hydrophobic The super-oleophilic oil-water separation membrane avoids additional surface microstructure construction process. The raw materials of the invention are easy to obtain, have wide sources, and the preparation process is simple. The prepared super-hydrophobic and super-oleophilic oil-water separation mesh has good selective permeation to oil substances, low processing cost, simple and convenient operation, and can be recycled and used for many times.

Description

technical field [0001] The invention relates to a preparation method of an oil-water separation omentum, in particular to a preparation method of an oil-water separation omentum based on a tannic acid-modified super-hydrophobic and super-oleophilic oil-water separation omentum. Background technique [0002] With the massive discharge of oily sewage in production and life and the frequent occurrence of oil spill accidents at sea, oil pollution in water has become a major problem that endangers human health and environmental safety. In order to maintain a good ecological environment and human health, and protect limited water resources, the effective separation of oily sewage has become an urgent problem to be solved. At present, there are many ways to control water pollution caused by toxic organic solvents or leakage of petroleum products. Traditional oil-water separation methods include gravity separation, oil skimming, centrifugation, and flotation, etc., which have a good...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D71/06B01D69/02B01D67/00B01D17/022
CPCB01D17/085B01D67/0079B01D69/02B01D71/06B01D2325/38
Inventor 彭新艳刘云鸿刘云晖
Owner 刘云晖
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com