Aerated concrete building block brick

A technology of aerated concrete and blocks, which is applied in the field of building materials, can solve the problems of difficulty in controlling the degree of static curing of block bricks, difficulty in controlling the degree of softness and hardness of block bricks, and difficulty in forming block bricks, so as to improve the effect of heat preservation and heat insulation , maintain smoothness, reduce the quality of the effect

Active Publication Date: 2019-04-23
广州市宏利新型建材有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the difficulty in controlling the degree of resting of the block bricks, the softness and hardness of the block bricks are difficult to control, so that the block bricks may collapse during the cutting process, causing the block bricks to be difficult to form. Therefore, there are still room for improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aerated concrete building block brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] An aerated concrete block brick, comprising the following components in parts by mass:

[0055] 45kg of water; 25.5kg of medium sand; 25.5kg of gypsum; 21kg of cement; 22.5kg of lime; 2.1kg of isinglass powder; 7.5kg of hollow glass beads.

[0056] In this embodiment, the calcium oxide content of the lime is 85%, and the fineness of the lime is 0.07mm.

[0057] In this embodiment, the silicon content of the medium sand is 68%.

[0058] In this embodiment, the particle size of the hollow glass microspheres is 10 μm.

[0059] The preparation method of aerated concrete block brick is as follows:

[0060] (1) Crush 25.5kg of medium sand and 25.5kg of gypsum and mix them into a ball mill to grind them into a mixture with a fineness of 200 mesh, then add the mixture and 25.5kg of water into the stirring tank, stir at a speed of 120r / min, stir Uniform, forming a slurry;

[0061] (2) Add the uniformly stirred slurry in (1), 22.5kg of lime, 21kg of cement, and 19.5kg of wate...

Embodiment 2

[0067] An aerated concrete block brick, comprising the following components in parts by mass:

[0068] 52.5kg of water; 30kg of medium sand; 30kg of gypsum; 21kg of cement; 24.5kg of lime; 2.4kg of isinglass powder; 8.7kg of hollow glass beads.

[0069] In this embodiment, the calcium oxide content of the lime is 90%, and the fineness of the lime is 0.08mm.

[0070] In this embodiment, the silicon content of the medium sand is 71.5%.

[0071] In this embodiment, the particle size of the hollow glass microspheres is 12 μm.

[0072] The preparation method of aerated concrete block brick is as follows:

[0073] (1) Crush 30kg of medium sand and 30kg of gypsum and mix them into a ball mill to grind them into a mixture with a fineness of 200 meshes, then add the mixture and 30kg of water into the stirring tank, stir at a speed of 120r / min, and stir evenly to form slurry;

[0074] (2) Add the uniformly stirred slurry in (1), 24.5kg of lime, 21kg of cement, and 22.5kg of water wh...

Embodiment 3

[0080] An aerated concrete block brick, comprising the following components in parts by mass:

[0081] 60kg of water; 34kg of medium sand; 34kg of gypsum; 28kg of cement; 30kg of lime; 2.8kg of isinglass powder; 10kg of hollow glass beads.

[0082] In this embodiment, the calcium oxide content of the lime is 95%, and the fineness of the lime is 0.09mm.

[0083] In this embodiment, the silicon content of the medium sand is 75%.

[0084] In this embodiment, the particle size of the hollow glass microspheres is 15 μm.

[0085] The preparation method of aerated concrete block brick is as follows:

[0086] (1) Crush 34kg of medium sand and 34kg of gypsum and mix them into a ball mill to grind them into a mixture with a fineness of 200 meshes, then add the mixture and 34kg of water into the stirring tank, stir at a speed of 120r / min, stir evenly, and form slurry;

[0087] (2) Add the uniformly stirred slurry in (1), 30kg of lime, 28kg of cement, and 26kg of water while stirring,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Particle sizeaaaaaaaaaa
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of building materials, and provides an aerated concrete building block brick specific to the problem that the building block brick is difficult to cut and form. Theaerated concrete building block brick is prepared from the following ingredients in parts by mass: 45-60 parts of water, 25.5-34 parts of medium sand, 25.5-34 parts of gypsum, 21-28 parts of cement, 22.5-30 parts of lime, 2.1-2.8 parts of fish gelatin powder and 7.5-10 parts of hollow glass beads. By adding the fish gelatin powder, the fish gelatin powder has good affinity and water-retaining property, can form a skin membrane and is conducive to forming a protective film on the outer surface of the concrete building block brick, meanwhile, the thickness of concrete is increased, the concretebuilding block brick is conducive to forming a gelatinization shape in the recuperation process and takes on a jelly-like state in the cutting process, therefore, the elasticity and strength of the concrete building block is conducive to being improved, and the concrete building block is difficult to collapse in the cutting process and convenient to cut and form.

Description

technical field [0001] The invention relates to the field of building materials, more specifically, it relates to an aerated concrete block brick. Background technique [0002] Air-entrained concrete block brick is a new type of building material that is lightweight, porous, thermally insulated, good in fire resistance, nailable, sawable, planable, and has a certain degree of earthquake resistance. [0003] Aerated concrete block bricks are generally bricks with a certain strength formed by crushing, ball milling, measuring, pulping, mixing, pouring, resting, cutting, and steaming at high temperature and high pressure. However, due to the difficulty in controlling the degree of resting of the block bricks, the softness and hardness of the block bricks are difficult to control, so that the block bricks may collapse during the cutting process, causing the block bricks to be difficult to form. Therefore, there are still room for improvement. Contents of the invention [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/14C04B38/08C04B38/02
CPCC04B28/14C04B38/085C04B2201/50C04B7/02C04B22/002C04B14/06C04B22/064C04B24/14C04B14/22C04B38/02C04B22/04
Inventor 黄增贵
Owner 广州市宏利新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap