Manufacturing method of grouting material for building wall

A technology for building walls and manufacturing methods, which is applied in the field of building walls, can solve the problems of complex operation, easy settlement and shrinkage, and short construction time, and achieve the effects of simple process, guaranteed service life, and easy operation

Inactive Publication Date: 2019-04-23
陈辉
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problems of complex operation, short construction time and easy occurrence of settlement and shrinkage in the construction process of grouting materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of grouting material for building wall

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A method for manufacturing grout for building walls, comprising the following steps:

[0022] First, after mixing 9 parts by weight of dodecyl primary amine, 2 parts of glutamic acid, 1.5 parts of alkyl glycoside and 40 parts of n-butanol, put it into an autoclave, pressurize to 0.15MPa, and control the temperature at 90°C. Keep constant pressure and temperature for 30 minutes, then release the pressure and cool down, add 7 parts of methyl oleate, re-pressurize to 0.2MPa, raise the temperature to 100°C, keep it for 20 minutes, drop the oil alcohol polyoxyethylene after reducing the pressure and temperature 3 parts of the mixed solution of ether and isooctyl alcohol, the temperature of the mixed solution is controlled at 40°C, the dropwise addition is completed in 30 minutes, and after the dropwise addition, it is kept at 40°C for 50 minutes to obtain the anti-settling agent, in which oleyl alcohol polyoxygen The molar ratio of vinyl ether to isooctyl alcohol is 1:2.5, ...

Embodiment 2

[0028] A method for manufacturing grout for building walls, comprising the following steps:

[0029] First, 5-10 parts by weight of dodecyl primary amine, firstly mix 8 parts by weight of dodecyl primary amine, 3 parts of glutamic acid, 1 part of alkyl glycoside and 35 parts of n-butanol, and then pack Autoclave, pressurize to 0.2MPa, control the temperature at 85°C, keep constant pressure and temperature for 20 minutes, then release the pressure and cool down, add 6 parts of methyl oleate, repressurize to 0.25MPa, and raise the temperature to 100-110 ℃, keep it for 15 minutes, after reducing the pressure and temperature, drop 2.5 parts of the mixed solution of oleyl alcohol polyoxyethylene ether and isooctyl alcohol, the temperature of the mixed solution is controlled at 45 ℃, and the dropwise addition is completed in 25 minutes ℃ for 50 minutes to obtain the anti-settling agent, wherein the molar ratio of oleyl alcohol polyoxyethylene ether to isooctyl alcohol is: 1: 3,

[...

Embodiment 3

[0035] A method for manufacturing grout for building walls, comprising the following steps:

[0036] First, after mixing 10 parts by weight of dodecyl primary amine, 3 parts of glutamic acid, 1 part of alkyl glycoside and 38 parts of n-butanol, put it into an autoclave, pressurize to 0.25 MPa, and control the temperature at 90 ° C. Keep constant pressure and temperature for 25 minutes, then release the pressure and cool down, add 7 parts of methyl oleate, re-pressurize to 0.3 MPa, raise the temperature to 110°C, keep it for 15 minutes, drop the oil alcohol polyoxyethylene after reducing the pressure and cooling down 2.5 parts of a mixed solution of ether and isooctyl alcohol, the temperature of the mixed solution is controlled at 40-50°C, the dropwise addition is completed in 20 minutes, and after the dropwise addition is completed, it is kept at 40-50°C for 45 minutes to obtain the anti-settling agent, wherein The molar ratio of oleyl alcohol polyoxyethylene ether to isooctyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A manufacturing method of a grouting material for a building wall includes the steps: firstly, uniformly mixing, by weight, 5-10 parts of dodecylamine, 2-3 parts of glutamic acid, 1-1.5 parts of alkylglycoside and 35-40 parts of n-butyl alcohol; placing mixture into an autoclave; pressurizing the autoclave to reach 0.15-0.25MPa; controlling temperature to range from 80 DEG C to 90 DEG C; keepingconstant pressure and constant temperature for 15-30 minutes; adding 4-8 parts of methyl oleate after reducing the pressure and the temperature; pressurizing the autoclave again to reach 0.2-0.3MPa; keeping the temperature increased to 100-110 DEG C for 10-20 minutes; dropping 2-3 parts of mixed liquid of oleic alcohol polyoxyethylene ether and isooctyl alcohol after reducing the pressure and thetemperature. By adding anti-shrinking agents, a solidified body of the grouting material cannot shrink after hydration reaction of the grouting material, the anti-shrinking agents can be uniformly distributed in the solidified body under the action of anti-settling agents, local shrinkage of the solidified body is avoided, and the service life of the wall is ensured.

Description

technical field [0001] The invention relates to a method for manufacturing a grouting material for building walls, and belongs to the technical field of building walls. Background technique [0002] The grouting material is mainly used for building reinforcement, enlarging the section of beams and columns, thickening the wall structure and repairing leakage and seepage, grouting for the collapse of various foundation projects and various emergency repair projects, etc. After reinforcement, the strength, stiffness, crack resistance, stability and durability of the structure should meet the requirements. In the prior art, the grouting material will shrink during the curing process, which makes the target volume of the required grouting body different, and it takes a certain time to solidify during grouting so that the solid fillers and additives will settle, and this settlement The phenomenon leads to unstable performance of the grouting material, and it is more prone to shri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B111/70
CPCC04B28/06C04B2111/70C04B2201/50C04B22/066C04B14/06C04B14/28C04B18/144C04B24/06C04B24/121C04B24/123C04B24/10C04B24/026C04B24/085C04B24/32C04B24/2676
Inventor 陈辉
Owner 陈辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com