Novel multifunctional three-dimensional conduction fabric, preparation method thereof and application of fabric

A conductive fabric, multi-functional technology, applied in the field of textiles, to achieve the effect of reducing transmittance, good space mesh overall effect, and reducing re-pollution

Inactive Publication Date: 2019-04-19
NINGBO GRAPHENE INNOVATION CENT CO LTD
View PDF15 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this patent, an adhesive is used for compounding, which will cause the above-mentioned defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel multifunctional three-dimensional conduction fabric, preparation method thereof and application of fabric
  • Novel multifunctional three-dimensional conduction fabric, preparation method thereof and application of fabric
  • Novel multifunctional three-dimensional conduction fabric, preparation method thereof and application of fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0073] figure 1 As shown, a new multifunctional three-dimensional conductive fabric, from top to bottom is the appearance layer 1, the functional conductive layer 2 and the fabric protection layer 3, and the above three layers are formed by interweaving warp yarns and weft yarns or binding yarns. made. The appearance layer 1 is a fabric composed of one or more layers of warp yarns and one or more layers of weft yarns. The functional conductive layer 2 is a fabric composed of weft yarns and warp yarns, and the number of layers is adjusted according to application requirements. The fabric protection layer 3 is made of one or more layers of warp yarns and one or more layers of weft yarns.

[0074] The above-mentioned three layers are formed by laying the warp system in the thickness direction at a certain buckling change angle into the vertically arranged weft system, tying and weaving them into one body, or by binding and connecting the warp system and the weft system through...

Embodiment 2

[0086] A new multi-functional three-dimensional conductive fabric, from top to bottom is an appearance layer 1, a functional conductive layer 2 and a fabric protection layer 3, and the above three layers are formed by interweaving warp yarns and weft yarns or bundling yarns. The appearance layer 1 is a fabric composed of multiple layers of warp yarns and multiple layers of weft yarns. The functional conductive layer 2 is a fabric composed of weft yarns and warp yarns, and the number of layers is adjusted according to application requirements. The fabric protection layer 3 is made of multiple layers of warp yarns and multiple layers of weft yarns.

[0087] The above-mentioned three layers are formed by laying the warp system in the thickness direction at a certain buckling change angle into the vertically arranged weft system, tying and weaving them into one body, or by binding and connecting the warp system and the weft system through the binding yarn passing through the thick...

Embodiment 3

[0093] A new multi-functional three-dimensional conductive fabric, from top to bottom is an appearance layer 1, a functional conductive layer 2 and a fabric protection layer 3, and the above three layers are formed by interweaving warp yarns and weft yarns or bundling yarns. The appearance layer 1 is a fabric composed of multiple layers of warp yarns and multiple layers of weft yarns. The functional conductive layer 2 is a fabric composed of weft yarns and warp yarns, and the number of layers is adjusted according to application requirements. The fabric protection layer 3 is made of multiple layers of warp yarns and multiple layers of weft yarns.

[0094] The above-mentioned three layers are formed by laying the warp system in the thickness direction at a certain buckling change angle into the vertically arranged weft system, tying and weaving them into one body, or by binding and connecting the warp system and the weft system through the binding yarn passing through the thick...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a novel multifunctional three-dimensional conduction fabric, a preparation method thereof and an application of the fabric. The three-dimensional conduction fabric sequentially comprises an appearance layer, a functional conduction layer and a fabric protection layer from top to bottom, and the appearance layer, the functional conduction layer and the fabric protection layer are interwoven through stitching warps and stitching wefts or integrally bundled by bundling yarns. The three-dimensional conduction fabric is designable in height, simple in preparation process, high in weaving efficiency and suitable for industrial production, application field of the conduction fabric is widened, and the conduction fabric has wide application prospects in the fields of smartclothing, heating, electronic sensing and electromagnetic shielding.

Description

technical field [0001] The invention relates to the field of textiles, in particular to a novel multifunctional three-dimensional conductive fabric. Background technique [0002] As a functional fabric, conductive fabric has a wide range of applications in the fields of antistatic, heat generation, electromagnetic shielding, and smart wearable textiles. The traditional way of preparing conductive fabric is to use metal conductive fibers such as copper wire, stainless steel wire, and carbon fiber as raw materials. to weave. Patent CN 105256389 B provides an antistatic double-sided fabric and its production method. Cotton fiber and stainless steel fiber are blended to obtain cotton / stainless steel staple fiber blended yarn; stainless steel filament is prepared by Siro core spinning as core yarn 1. Cotton / stainless steel monofilament core-spun yarn with cotton fiber as the outsourcing fiber; use two stainless steel filaments as the core yarn, cotton fiber as the outsourcing fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D25/00D03D15/00D03D1/00D02G3/04D02G3/36D02G3/44A41D31/02H05B3/12H05B3/10D03D15/217D03D15/225D03D15/283D03D15/292D03D15/30D03D15/50D03D15/513D03D15/533
CPCA41D31/02H05B3/10H05B3/12D02G3/04D02G3/36D02G3/441D03D1/0088D03D15/00D03D25/005D10B2321/02D10B2321/022D10B2331/02D10B2331/04D10B2331/10D10B2321/041D10B2321/06D10B2321/08D10B2101/00D10B2101/12D10B2401/16D03D15/47
Inventor 赵玉芬赖垂林汪海映刘兆平
Owner NINGBO GRAPHENE INNOVATION CENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com