A finishing agent for preventing fluffing of embroidery and its preparation method and application method

Abstract

The invention discloses a finishing agent for preventing fluffing of embroidery and its preparation method and application method. The finishing agent comprises the following proportions by weight: 2-5 parts of polyvinyl alcohol, 2-5 parts of polyacrylic acid, cross-linked 0.2-0.5 part of agent borax, 0.2-0.5 part of colorless water-soluble penetrating agent, 0.2-0.5 part of colorless water-soluble softener, add deionized water and be made into the solution of 100 parts of total amount; The preparation method of the agent comprises the steps of: weighing 2-5 parts of polyvinyl alcohol according to the ratio of parts by weight, and placing an appropriate amount of deionized water to swell, and then heating and dissolving to obtain an aqueous solution of polyvinyl alcohol; The preparation method of the finishing agent for preventing fluffing of embroidery is simple, and at the same time, the finishing agent for preventing fluffing of embroidery is convenient to use, has strong operability, good controllability, and no pollution; the finishing agent for preventing fluffing of embroidery The anti-pilling effect is obvious. At the same time, the color difference of embroidery after treatment is small, and its inherent color and pattern texture, layering and soft feel are retained.

Description

technical field [0001] The invention relates to the improvement of an embroidery anti-fluffing technology, in particular to a preventive embroidery which can effectively prevent the surface of the embroidery from fluffing after long-term use, has a simple synthesis method, and does not affect the quality of the embroidery on the embroidery after spraying. A fluffed finish and methods of making and using the same. Background technique [0002] Due to the loose structure of the embroidery pattern in the embroidery and floating on the surface of the embroidery, the embroidery will be subject to more friction and damage during use, resulting in fluffing, which greatly affects the beauty and durability of the embroidery; In the prior art, Chinese patent CN201611121791.9 discloses an embroidery anti-hair finishing agent and its use method. The main components of the finishing agent are methacrylamide monomer, methacrylate monomer, butyl acrylate Copolymer formed by monomer and 2-...

AI Technical Summary

Problems solved by technology

[0002] Due to the loose structure of the embroidery pattern in the embroidery and floating on the surface of the embroidery, the embroidery will be subject to more friction and damage during use, resulting in fluffing, which greatly affects the beauty and durability of the embroidery; In the prior art, Chinese patent CN201611121791.9 discloses an embroidery anti-hair finishing agent and its use method. The main components of the finishing agent are methacrylamide monomer, methacrylate monomer, butyl acrylate Copolymer formed by monomer and 2-hydroxyethyl acrylate monomer, the finishing method is to use a brush to dip an appropriate amount of finishing agent to smear, and then heat and cure in an oven; however, the synthetic monomer components of this finishing agent are complex and the composition is difficult to control. The water solubility is not ideal, which not only affects the smearing effect and the quality of embroidery after smearing, but also the method of application is cumbersome and difficult to control

Images