PA/ABS composite material and preparation method thereof

A technology of composite materials and maleic anhydride, applied in the field of PA/ABS composite materials and its preparation, to achieve good thermal and electrical conductivity, excellent application prospects, and reduce production costs

Inactive Publication Date: 2019-01-18
惠州市沃特新材料有限公司
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a PA / ABS composite material with excellent thermal conductivity and electrical conductivity and its preparation method and application, aiming to solve the problem that existing plastic materials are difficult to simultaneously take into account better electrical conductivity and thermal conductivity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PA/ABS composite material and preparation method thereof
  • PA/ABS composite material and preparation method thereof
  • PA/ABS composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] Correspondingly, an embodiment of the present invention provides a method for preparing a PA / ABS composite material, comprising the following steps:

[0048] According to the formula of the PA / ABS composite material described in the embodiment of the present invention, each component is weighed; an internal mixer with a sealed structure and a twin-screw extruder provided with forced side feeding equipment are provided;

[0049] Mixing the ABS resin, PA resin, graphite filler, compatibilizer, antioxidant, lubricant, and toner to obtain a mixture;

[0050] Put the above mixture into the internal mixer for melting and banburying, until the materials are completely mixed and uniform, and then take out the semi-finished composite material;

[0051] Putting the conductive carbon black into the forced side feeding device of the twin-screw extruder;

[0052] While putting the semi-finished composite material into the twin-screw extruder for melt extrusion, the conductive carbo...

Embodiment 1-6

[0080] A kind of PA / ABS composite material, comprises each component of content shown in Table 1 embodiment 1-6.

[0081] The preparation method of the PA / ABS composite material is as follows: after weighing the ingredients, mix the formula components except the conductive carbon black for 3 minutes with a high mixer to obtain a uniform mixture; put the above mixture into the internal mixer for melting and kneading , and then melted and extruded together with conductive carbon black in a twin-screw extruder, and pelletized.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a PA / ABS composite material. The PA / ABS composite material comprises the following components in parts by weight: 25-40 parts of ABS resin, 25-40 parts of nylon 6 resin, 30-60 parts of graphite fillers, 5-10 parts of conductive carbon black, 1-5 parts of a compatibilizer, 0.1-1 part of an antioxidant and 0.1-3 parts of a lubricant.

Description

technical field [0001] The invention belongs to the technical field of conductive composite materials, and in particular relates to a PA / ABS composite material and a preparation method thereof. Background technique [0002] Graphite is an excellent natural material. According to incomplete statistics, the world's natural graphite reserves are about 2 billion tons, of which crystalline graphite is about 800 million tons. China's natural graphite reserves rank first in the world, and the total reserves of crystalline graphite mines are 473 million tons. China has now formed a comprehensive natural graphite industry for mining, beneficiation, processing, purification and product series. China is the world's largest producer of natural graphite. In 2009, the production of natural graphite reached 1.7556 million tons. China's production accounts for about 55% of the world's total output, ranking first in the world. Developed countries reserve their own graphite resources as str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L55/02C08L77/02C08L39/06C08L91/06C08K13/04C08K7/24C08K7/00C08K3/04C08K5/134C08K5/526
CPCC08K2201/001C08K2201/011C08L55/02C08L77/02C08L2201/02C08L2203/206C08L2205/035C08L39/06C08L91/06C08K13/04C08K7/24C08K7/00C08K3/04C08K5/1345C08K5/526
Inventor 周小舟管静何征张尊昌
Owner 惠州市沃特新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com