A high heat input gas-electric vertical welding gas-shielded flux-cored wire based on grain refinement mechanism

A flux-cored wire, high heat input technology, applied in welding equipment, manufacturing tools, welding media, etc., can solve the problem of limited welding heat input range, increasing the hardening tendency of weld metal, and increasing the degree of burning of beneficial alloying elements. Advanced problems, to achieve the effect of improving welding process performance, ensuring comprehensive mechanical properties, and ensuring the quality of weld forming

Active Publication Date: 2021-06-15
BAOSHAN IRON & STEEL CO LTD
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] First, prolonging the high temperature residence time increases the degree of burning of beneficial alloying elements and weakens the alloying effect of the weld;
[0005] Second, the extension of the high temperature residence time increases the tendency of the original columnar grains to grow. This irreversible process cannot be effectively refined in the subsequent cooling process, and the coarsening of the grains is likely to cause various embrittlements of the welded joints;
[0006] Third, after the cooling rate is reduced, high-temperature solid-state phase transformation is prone to occur, and pro-eutectoid massive ferrite or Widmanstatten structure with coarse grains is formed
Due to the high alloy content of the flux-cored wire, the weld metal cold crack sensitivity index P cm The value can reach 0.22. High Cr and Mo content increase the hardening tendency of the weld metal, and various precipitates of alloying elements hinder dislocation movement and also cause a decrease in the elongation of the welded joint.
Chinese patent application number CN201611163806.8 and other patents combine the advantages of good welding process performance of acidic slag system and low hydrogen type slag system, with good process performance and joint mechanical properties, but the applicable welding heat input range is limited
Chinese patent application number CN201510350945.0 discloses a gas-shielded flux-cored wire for gas-electric vertical welding with large heat input, which adopts the joint action of Ti, B and rare earth to strengthen and toughen the mechanism, and adopts a higher carbon content configuration , when the welding heat input is too high, there is a risk of weld embrittlement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high heat input gas-electric vertical welding gas-shielded flux-cored wire based on grain refinement mechanism
  • A high heat input gas-electric vertical welding gas-shielded flux-cored wire based on grain refinement mechanism
  • A high heat input gas-electric vertical welding gas-shielded flux-cored wire based on grain refinement mechanism

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0072] The present invention will be further described below in conjunction with embodiment.

[0073] See Table 1 for the chemical composition of the flux-cored welding wire steel strip of the present invention. Table 2 shows the composition of the flux-cored wire powder of the present invention, the balance of which is reduced iron powder.

[0074] Table 3 shows the chemical composition of the cladding metal in the examples of flux-cored wires designed with five different compositions.

[0075] In the embodiment of the present invention, EH40 grade shipbuilding steel with a wall thickness of 35 mm was selected to conduct a gas-electric vertical welding test with a heat input of about 230 kJ / cm. The welding current is 390-430A, the welding voltage is 40-42V, and the welding speed is 4.2-4.6mm / min. Welding adopts V-shaped groove without blunt edge, the groove angle is 30°±2°, the pair gap is 5-8mm, and the corresponding front opening width is 23-26mm. During the welding proces...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

A high heat input gas-electric vertical welding gas-shielded flux-cored wire based on a grain refinement mechanism, including a flux-cored wire sheath and its inner drug powder, wherein the flux-cored wire sheath is made of low-carbon steel cold-rolled steel strip, which The mass percentage of the composition is: C<0.06%, Si<0.3%, Mn<0.8%, P<0.02%, S<0.01%, and the balance is Fe and unavoidable impurities; the mass percentage of the composition of the powder is: titanium dioxide Or one or both of rutile: 1-5%, quartz sand: 2-6%, feldspar: 3-8%, magnetite: 1-5%, lithium oxide, sodium oxide or potassium oxide One or more: 2-5%, low-carbon ferromanganese: 10-15%, aluminum powder: 3-8%, titanium iron: 3-8%, nickel powder: 2-6%, rare earth silicon: 2- 6%, magnesium powder: 1-3%, and the rest is reduced iron powder; and the powder accounts for 15-20% of the total mass of the flux-cored wire. The welding wire of the invention can be used for gas-electric vertical welding of thick steel plate with large heat input of 100kJ / cm-300kJ / cm.

Description

technical field [0001] The invention relates to a gas-shielded flux-cored welding wire, in particular to a gas-shielded flux-cored wire for gas-electric vertical welding with large heat input based on a grain refinement mechanism. Background technique [0002] At present, with the development of modern manufacturing industry's demand for various large-scale steel structures, the quality and efficiency of steel structure welding have attracted more and more attention. In order to improve the construction welding efficiency of the steel structure manufacturing site and reduce the construction cost, the large heat input gas-electric vertical welding technology has been more and more applied. Gas electric vertical welding is a special vertical upward welding technology developed on the basis of melting electrode gas shielded welding, generally using CO 2 Gas protection, using water-cooled copper sliders or slides to force the molten metal in the molten pool to form, while preve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/30B23K35/368
CPCB23K35/0266B23K35/3073B23K35/3602B23K35/3607B23K35/368
Inventor 刘硕翁思源钱伟方曹能
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products