Low-temperature fast fired marble tile and preparation method thereof

A technology for marble and ceramic tiles, which is applied to the field of low-temperature fast-fired marble tiles and their preparation, can solve the problems of high price of flux raw materials, aggravate the global greenhouse effect, and insignificant cooling effect, and achieve low price, lower energy consumption, and lower eutectic point. effect of temperature

Inactive Publication Date: 2018-12-28
清远市简一陶瓷有限公司 +1
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the current production of marble tiles not only consumes a large amount of raw materials and fuel, but also has high production costs, and also emits a large amount of CO 2 Exhaust gas, thus exacerbating the global greenhouse effect, causing serious damage to the natural environment
In view of the above situation, most of the existing technologies use a large amount of one or two kinds of feldspar flux raw materials or waste glass to reduce the sintering temperature. Since the formula structure has not changed, the cooling effect is not obvious
In addition, flux raw materials are expensive, resources are scarce, and production costs are too high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature fast fired marble tile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] An embodiment of the low-temperature fast-fired marble tiles of the present invention, the low-temperature fast-fired marble tiles in this embodiment include the following raw materials in parts by weight: 30 parts of ultra-fine particle marble tile edging waste residue, 22 parts of potassium sodium feldspar, 25 parts of lithium porcelain stone, 18 parts of ultra-white ball clay, 1 part of boronite, 2 parts of wollastonite and 2 parts of talc; the ultrafine particle marble tile edging waste slag is the waste slag produced in the marble tile edging process section, so The particle size D of ultra-fine particle marble tile edging waste residue 50 10~18μm, D 90 It is 45-60 μm.

[0033] The preparation method of the ultra-low temperature sintered ceramic tile of the present embodiment comprises the following steps:

[0034] (1) Collection of ultra-fine marble tile edging residue:

[0035] (a), collect the waste water containing fine particles produced in the edging proce...

Embodiment 2

[0043] An embodiment of the low-temperature fast-fired marble tiles of the present invention, the low-temperature fast-fired marble tiles in this embodiment include the following raw materials in parts by weight: 35 parts of ultrafine particle marble tile edging waste residue, 12 parts of potassium sodium feldspar, 30 parts of lithium china stone, 17 parts of ultra-white ball clay, 1 part of boronite, 3 parts of wollastonite and 2 parts of talc; the ultrafine particle marble tile edging waste slag is the waste slag produced in the marble tile edging process section, so The particle size D of ultra-fine particle marble tile edging waste residue 50 10~18μm, D 90 It is 45-60 μm.

[0044] The preparation method of the ultra-low temperature sintered ceramic tile of the present embodiment comprises the following steps:

[0045] (1), the collection of superfine particle marble tile edging waste residue: with embodiment 1;

[0046] (2), mix raw materials, add in ball mill and carry...

Embodiment 3

[0051] An embodiment of the low-temperature fast-fired marble tiles of the present invention, the low-temperature fast-fired marble tiles in this embodiment include the following raw materials in parts by weight: 30 parts of ultra-fine particle marble tile edging waste residue, 15 parts of potassium sodium feldspar, 25 parts of lithium porcelain stone, 10 parts of low-temperature sand, 15 parts of Huadu Baini, 1 part of boron calcium stone, 2 parts of wollastonite and 2 parts of talc; the ultrafine grain marble tile edging waste residue is the marble tile edging process The waste slag produced in the section, the particle size D of the ultrafine particle marble tile edging waste slag 50 10~18μm, D 90 It is 45-60 μm.

[0052] The preparation method of the ultra-low temperature sintered ceramic tile of the present embodiment comprises the following steps:

[0053] (1), the collection of superfine particle marble tile edging waste residue: with embodiment 1;

[0054] (2), mix ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-temperature fast fired marble tile. The low-temperature fast fired marble tile comprises raw materials in parts by weight as follows: 15-35 parts of ultrafine-particle marble tile edging waste, 15-25 parts of kalialbite, 15-30 parts of lithium china stone, 0-25 parts of low-temperature sand, 16-25 parts of clay and 3-10 parts of an auxiliary, wherein the ultrafine-particle marble tile edging waste is the waste produced in a marble tile edging procedure. The raw materials of the tile are easily available, the cost is low, product performance indexes of the low-temperature fast fired marble tile can be guaranteed, and by full use of the characteristics of low melting temperature and fine powder particle of the polishing waste as the waste raw material, sinteringtemperature of the product and energy consumption can be reduced while the waste is used. The invention further discloses a preparation method of the low-temperature fast fired marble tile. The marble polishing waste is separated with a simple process, content of impurities in the polishing waste is reduced, components of the polishing waste are more stable, and industrial production is facilitated.

Description

technical field [0001] The invention relates to a ceramic, in particular to a low-temperature fast-fired marble tile and a preparation method thereof. Background technique [0002] The rapid growth of social economy has driven the development of the construction industry, and also made the construction ceramics industry in full swing, and the products are constantly being introduced. Marble tiles are a bright spot of new architectural ceramic products. It combines the advantages of polished tiles and antique tiles. It has rich patterns, thick and dazzling colors, and a good sense of hierarchy. At the same time, the body is dense and durable. Therefore, marble tiles have also rapidly developed into a pillar of today's ceramic tile products. [0003] Marble tiles are also a kind of porcelain tiles, with extremely low water absorption and good flatness of tiles. In order to meet these two performance requirements, at present, the production and preparation of this type of cer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/14C04B35/622C04B35/64
CPCC04B35/14C04B35/62204C04B35/64C04B2235/3201C04B2235/3203C04B2235/3206C04B2235/3208C04B2235/3217C04B2235/3272C04B2235/3409C04B2235/3472C04B2235/349C04B2235/5436C04B2235/96
Inventor 唐赋许林峰周新苗蒋小英
Owner 清远市简一陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com