TMCP delivery economical HIC-resistance pipeline steel plate X65MS and manufacturing method thereof

A manufacturing method and an economical technology, applied in the field of metallurgy, can solve the problems of high manufacturing cost of HIC-resistant pipeline steel and unstable HIC performance, and achieve the effects of good HIC-resistant performance, prolonging heating time, and increasing heating temperature

Active Publication Date: 2018-12-21
JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] For the anti-HIC pipeline steel plate X65MS delivered by TMCP, the use of precious alloy elements is saved through reasonable composition design to improve economy, and at the same time, the heating, rolling and cooling processes are precisely set to ensure the strength and HIC resistance of the steel plate. Focus on solving the technical problems of high manufacturing cost and unstable HIC performance of the HIC-resistant pipeline steel delivered by TMCP

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • TMCP delivery economical HIC-resistance pipeline steel plate X65MS and manufacturing method thereof
  • TMCP delivery economical HIC-resistance pipeline steel plate X65MS and manufacturing method thereof
  • TMCP delivery economical HIC-resistance pipeline steel plate X65MS and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1 and 2

[0029] According to the scope of chemical composition and manufacturing method of the present invention, pretreatment of molten iron by KR—converter smelting—LF refining—RH vacuum degassing—continuous casting—continuous casting slab covered and slow cooling—continuous casting slab inspection and cleaning—slab heating—high pressure Water descaling—controlled rolling and controlled cooling—straightening—slow cooling of steel plate piles and other process steps to manufacture X65MS economical HIC-resistant pipeline steel with a thickness of 21mm (Example 1 and 2).

[0030] The continuous casting slab meets, P≤0.008; S≤0.0008; [N]≤0.002, [O]≤0.0010, [H]≤0.0001, the sum of the four types of inclusions A, B, C, and D is less than or equal to level 2, using continuous The segregation of the billet is controlled by light reduction and electromagnetic stirring technology, and the segregation of the billet meets the Mannesmann standard rating M1; the continuous casting billet is slowly c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a TMCP delivery economical HIC-resistance pipeline steel plate X65MS and a manufacturing method thereof. The TMCP delivery economical HIC-resistance pipeline steel plate X65MScomprises chemical components including 0.06-0.10% of C, 0.3-0.4% of Si, less than or equal to 1.0% of Mn, less than or equal to 0.08% of Nb+Ti+V, 0.1-0.3% of Cr, less than or equal to 0.008% of P, less than or equal to 0.0008% of S, less than or equal to 0.002% of [N], less than or equal to 0.0010% of [O], less than or equal to 0.0001% of [H], and the balance Fe and inevitable impurities. A uniform polygonal ferritic structure is obtained. The preparation method comprises the technological steps of KR molten iron pretreatment, converter smelting, LF refining, RH vacuum degassing, continuous casting, continuous casting billet covering slow-cooling, continuous casting billet inspection and cleaning, casting billet heating, high-pressure water descaling, controlled rolling and controlled cooling, straightening and steel plate pile slow-cooling. Through the preparation method, production of the HIC-resistance pipeline steel plate X65MS with the economical components and HIC resistance isrealized.

Description

technical field [0001] The invention belongs to the technical field of metallurgy and relates to a pipeline steel plate X65MS delivered by TMCP with more economical composition and HIC resistance and a manufacturing method thereof. Background technique [0002] At present, with the continuous exploitation of resources, there are more and more oil and gas resources containing corrosive media such as hydrogen sulfide, which are corrosive to the pipeline during the transportation process. If the conventional pipeline steel plate design is adopted, the safety of the pipeline will be seriously affected sex. In order to prevent cracking caused by hydrogen sulfide corrosion, HIC-resistant steel plates that can resist hydrogen sulfide gas corrosion are mostly used in the design. At present, the main steel grade used is BMS-X65MS, and the highest steel grade is X70MS. The higher the steel grade, the higher the strength , the greater the sensitivity of HIC, the steel type involved in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22D11/115C21C1/02C21C5/35C21C7/064C21C7/10C21D1/84C21D3/06C21D6/00C21D8/02C21D9/46C22C33/04C22C38/02C22C38/04C22C38/24C22C38/26C22C38/28B21B37/74
CPCB21B37/74B22D11/115C21C1/02C21C5/35C21C7/064C21C7/10C21D1/84C21D3/06C21D6/002C21D6/005C21D6/008C21D8/0221C21D9/46C21D2211/005C22C33/04C22C38/001C22C38/002C22C38/02C22C38/04C22C38/24C22C38/26C22C38/28
Inventor 孙宪进许晓红白云李经涛苗丕峰林涛宁康康石艾来许峰
Owner JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com