Novel lightweight wall tile

A light-weight technology for wall bricks, applied in floors, buildings, building structures, etc., can solve the problems of difficult to find the location of water seepage, strict requirements for pasting procedures, poor construction technology, etc., to overcome the problems of easy aging, cracking and Easy to break, wide range of use, cost reduction effect

Inactive Publication Date: 2018-12-18
倪和芬
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the initial investment cost of exterior wall tiles is relatively high, the sticking procedures are strict, and the construction is difficult. If the construction technology is not strong, it is easy to cause falling off and hurting people. High-quality waterproof materials must also be used to solve the waterproof problem.
Because once a leak occurs on the exterior wall of the ceramic tile, it will be difficult to find the location of the water seepage, and it is very difficult to repair

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] This embodiment provides a new type of lightweight wall tile, which includes glass fiber tires, modified asphalt coatings formed on the front and back sides of the glass fiber tires, and cladding materials respectively coated on the modified asphalt coatings. layers and isolation material layers.

[0043] The modified asphalt coating raw material formula is as follows: 10# petroleum asphalt 40%; 90# road asphalt 3%; Oxidized polyethylene modifier (Honeywell Comprehensive Technology Co., Ltd., 8903) 2%; Magnesium hydroxide (particle size 2-3 microns) 20%; desulfurized reclaimed rubber powder (60 mesh) 12%; calcium carbonate 23%.

[0044] The raw material formula of the cladding material is as follows: hollow ceramic microspheres (30-50 microns in particle size) 35%; colored sand (20-30 mesh) 63%; powdered styrene-butadiene rubber (QL-6) 2%.

[0045] The performance parameters of the new lightweight wall brick obtained in this example are as follows: water absorption rat...

Embodiment 2

[0047] This embodiment provides a new type of lightweight wall tile, the structure of which is the same as that of Embodiment 1, except that the raw material formula of the modified asphalt coating and the raw material formula of the cladding material are different, as follows.

[0048] The raw material formula of modified asphalt coating is as follows: 10# petroleum asphalt 46%; 90# road asphalt 4%; Maleic anhydride modified polyethylene modifier (Honeywell Comprehensive Technology Co., Ltd., 8822) 3%; Magnesium (particle size 1-2 microns) 18%; desulfurized reclaimed rubber powder (50 mesh) 9%; talcum powder 20%.

[0049] The raw material formula of the cladding material is as follows: hollow ceramic microspheres (50-60 microns in particle size) 40%; colored sand (30-40 mesh) 57%; powdered styrene-butadiene rubber (GS-1A) 3%.

[0050]The performance parameters of the new lightweight wall brick obtained in this example are as follows: water absorption rate 0.4%, no cracks when...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a novel lightweight wall tile. The wall tile includes a glass fiber blank, a modified asphalt coating and a facing material layer. The modified asphalt coating is prepared from, by weight, 40-60% of 10# petroleum asphalt, 3-5% of 90# pavement asphalt, 1-3% of polyolefin processing modifier, 13-23% of magnesium hydroxide, 8-14% of desulfurized reclaimed rubber and the balance fillers. The facing material is prepared from 30-40% of hollow ceramic microbeads, 2-5% of powdery butadiene styrene rubber and the balance colored sand. The wall tile has excellent corrosion resistance, water resistance and aging resistance and is high in tensile strength, excellent in trimming and processing performance, simple in construction, attractive, elegant and especially superior in thermal insulation and flame retardation performance, and an environment-friendly, energy-saving, safe and reliable external wall decoration material is obtained.

Description

technical field [0001] The invention relates to a light wall brick. Background technique [0002] As an easy-to-construct building exterior wall decoration material, lightweight wall bricks not only have good decorative and aesthetic effects, but are also mainly used to protect the wall from external erosion and damage, and the comprehensive cost is low, and the later maintenance is convenient. Many are applied to modern architecture. [0003] In recent years, due to changes in architectural design and the use of new building components, higher and higher requirements have been placed on facade materials. On September 25, 2009, the Ministry of Public Security and the Ministry of Housing and Urban-Rural Development jointly issued the "Interim Regulations on Fire Protection of Civil Building External Thermal Insulation Systems and Exterior Wall Decoration", which requires that the building's exterior facades must reach the fire rating of B1, and high-rise buildings are restri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F13/075C04B26/26C04B30/00
CPCE04F13/0875C04B26/26C04B30/00C04B2111/28C04B2201/50E04F2290/04E04F2290/045C04B24/2611C04B22/066C04B18/22C04B14/106C04B14/042C04B14/28C04B18/146C04B14/06C04B14/24C04B24/26
Inventor 倪和芬
Owner 倪和芬
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com