A kind of airgel fireproof heat insulation coating and preparation method thereof

A technology for thermal insulation coatings and aerogels, applied in fire-resistant coatings, epoxy resin coatings, polyurea/polyurethane coatings, etc., can solve problems such as poor adhesion, instability, and structural damage, reduce heat loss, improve The effect of fire resistance and heat insulation improvement

Active Publication Date: 2020-11-27
河南爱彼爱和新材料有限公司
View PDF14 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention patent titled "Aerogel Water-Based Thermal Insulation and Fireproof Coating and Its Preparation Method" uses a surfactant to modify the airgel first to be hydrophobic and then hydrophilic. The surfactant and the aerogel form a non-chemical bond. Combination, the binding force is poor, the surfactant is attached to the surface of the airgel with two layers, the structure is easily destroyed, and it is extremely unstable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of airgel fireproof heat insulation coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] An aerogel fireproof and heat-insulating coating, comprising the following raw materials in parts by weight: water-based polyurethane emulsion 20, water-based epoxy resin emulsion 15, graphene aerogel 25, 2-hydroxybenzophenone derivatives 2. Piperidine derivatives 2, sodium hexametaphosphate 3, ethylene glycol 3, ammonium borate 4, amino resin 5, zirconia ceramic powder 18, hydroxyethyl cellulose 4, tributyl phosphate 2.5, sodium benzoate 2 , Silicone series leveling agent 4, titanium dioxide 2, silicone defoamer 2.5, deionized water 30.

[0042] The preparation method of the aerogel fireproof and thermal insulation coating of the present embodiment comprises the following steps:

[0043] (1) Preparation of modified aerogel slurry:

[0044] a. Heating the aerogel powder for 30min-2h at a heating temperature of 200-500℃ for surface hydrophilic modification, without destroying its three-dimensional network structure, modify the surface of the aerogel powder into Hydroph...

Embodiment 2

[0051] An aerogel fireproof and heat-insulating coating is prepared from the following raw materials in parts by weight: water-based polyurethane emulsion 40, LiO aerogel 24, 2-hydroxybenzophenones 3, fatty alcohol polyoxyethylene ether 2, Glycerol 2, Pentaerythritol 2, Ammonium Phosphate 7, Silica Ceramic Powder 12, Sodium Carboxymethyl Cellulose 2, Aluminum Hydroxide 0.5, Expanded Graphite 0.5, Sodium Benzoate 1.5, Acrylate Leveling Agent 0.5, Fluorine Modification Leveling agent 0.5, titanium dioxide 2, zinc oxide 2, silicone defoamer 3, deionized water 20.

[0052] The preparation method of the aerogel fireproof and thermal insulation coating of the present embodiment comprises the following steps:

[0053] (1) Preparation of modified aerogel slurry:

[0054] a. Heating the aerogel powder for 30min-2h at a heating temperature of 200-500℃ for surface hydrophilic modification, without destroying its three-dimensional network structure, modify the surface of the aerogel powd...

Embodiment 3

[0057] An aerogel fire-proof and heat-insulating coating, comprising the following raw materials in parts by weight: water-based epoxy resin emulsion 45, TiO 2 Aerogel powder 15, imidazolidinone derivatives 1, fatty alcohol polyoxyethylene ether 1.5, ethylene glycol 2, ammonium borate 6, zirconia ceramic powder 14, lithium bentonite 1.5, expanded graphite 3, sodium citrate 3.5 , acrylate leveling agent 3, zinc oxide 1.5, silicone defoamer 1, deionized water 40.

[0058] The preparation method of the aerogel fireproof and thermal insulation coating of the present embodiment comprises the following steps:

[0059] (1) Preparation of modified aerogel slurry:

[0060] a. Heating the aerogel powder for 30min-2h at a heating temperature of 200-500℃ for surface hydrophilic modification, without destroying its three-dimensional network structure, modify the surface of the aerogel powder into Hydrophilic to obtain aerogel powder with surface hydrophilic modification;

[0061] Other ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aerogel waterproof and heat-insulating coating as well as a preparation method thereof. The coating with fireproof and heat-insulating properties is prepared by adding aerogel powder and ceramic powder which are subjected to hydrophilic modification as well as adding aids and fillers according to different formula proportions, and the coating is prepared by utilizing theproperty characteristic of a three-dimensional network structure of the aerogel, so that the defect that the existing coating is only fireproof and is not heat-insulating is solved and the coating has the heat-insulating characteristic. Meanwhile, nanometer ceramic powder is added in the coating, the nanometer ceramic powder in the coating is heated to be ceramic, one expanded ceramic film is formed on the surface of a base material, one air layer is arranged between the film and the base material, contact between flame and the surface of a vehicle metal material product is isolated, and heatis prevented from being transmitted to the surface of the metal by depending on the low heat-conducting coefficient characteristic of the aerogel in the coating. Through fireproof and heat-insulatingsynergistic effect, good barrier effect on heat and flame is guaranteed to be achieved no matter normal use of the metal part in the vehicle or occurrence of extreme fire accidents, and the fireproofproperty of the coating is enhanced.

Description

technical field [0001] The invention belongs to the field of vehicle fire-proof and heat-insulation, and in particular relates to an aerogel fire-proof and heat-insulation coating and a preparation method thereof. Background technique [0002] With the continuous progress of science and technology, the development of railway and highway construction in China is growing, and people's requirements for material life are increasing. High-speed and comfortable modern air-conditioned passenger / train will become the development direction and mainstream of road / rail passenger car The safety and comfort of the environment will become an important indicator for the design of passenger cars. [0003] In the vehicle structure, although the metal parts such as the skin, the roof and the keel are non-combustible materials, the thermal conductivity of the metal material is very high. In winter, these metal parts will form thermal bridges to accelerate the heat dissipation in the vehicle; i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D163/00C09D133/04C09D5/18C09D7/61C09D7/63C09D7/65
CPCC08K2003/2227C08K2003/2241C08K2003/322C08K2201/014C08L2201/02C08L2205/035C09D5/185C09D7/61C09D7/63C09D7/65C09D133/04C09D163/00C09D175/04C08L63/00C08L1/284C08L61/20C08K13/06C08K7/24C08K3/32C08K5/053C08K5/521C08L71/02C08L1/286C08K3/22C08K7/26C08K3/346
Inventor 张光明晁华鑫张爽杨浩侯志国罗肖宁
Owner 河南爱彼爱和新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com