Heat-resisting liquid silicon rubber with improved strength and interface bonding performance

A liquid silicone rubber and interface bonding technology, which is applied in the field of heat-resistant liquid silicone rubber materials to achieve the effects of easy processing, broad market application prospects and high heat resistance.

Pending Publication Date: 2018-12-11
SICHUAN UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Modification of silicone rubber with other polymers can improve the above shortcomings. At present, there is no report on the use of bisphenol A epoxy resin for modifying liquid silicone rubber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-resisting liquid silicon rubber with improved strength and interface bonding performance
  • Heat-resisting liquid silicon rubber with improved strength and interface bonding performance
  • Heat-resisting liquid silicon rubber with improved strength and interface bonding performance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1, the preparation of the liquid silicone rubber of epoxy resin modification of the present invention

[0026] One, the preparation method of the liquid silicone rubber of epoxy resin modification of the present invention

[0027] 1 Experimental raw materials

[0028]

[0029] 2 Preparation of bisphenol A type epoxy resin-silane coupling agent prepolymer

[0030]

[0031] To a three-necked flask equipped with a thermometer, a mechanical stirrer and a reflux condenser device, an epoxy resin (E44, 50 g) and a silane coupling agent (SCA-L, 13.04 g) were sequentially added in a molar ratio of 1:1 to feed an inert Exhaust the air in the device, raise the temperature to 100°C and keep it constant, start stirring to make the mixture evenly mixed. By changing the time of the prepolymerization reaction and the amount of catalyst (tetraisopropyl titanate) (see Table 1), 9 groups of different primary products were prepared respectively, and the primary products ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides heat-resisting liquid silicon rubber with improved strength and interface bonding performance and in particular relates to a heat-resisting type liquid silicon rubber material with strength and interface bonding performance, which can be improved through introducing an epoxy functional group. The heat-resisting liquid silicon rubber is prepared from the following raw materials in parts by weight: 100 parts of liquid silicon rubber, 10 parts of a bisphenol A type epoxy resin-silane coupling agent pre-polymer, 3 parts of a curing agent and 0.2 part of a catalyst A. Starting from a molecular structure design, the epoxy functional group is introduced into a silicon rubber material matrix, so that the strength of the silicon rubber (the tensile strength is improved to reach 0.83MPa and is improved by 162 percent when being compared with that of a pure sample, and the bonding performance is 0.81MPa and is improved by 160 percent when being compared with that of the pure sample) , and elongation at break (the elongation at break reaches 268 percent and is improved by about two times when being compared with that of the pure sample) are greatly improved under the condition that the adding amount is extremely low; the rigidity and toughness of a composite material are improved at the same time, an application field of the silicon rubber is extremely widened and the service life of the silicon rubber is prolonged.

Description

technical field [0001] The invention relates to a modified heat-resistant liquid silicone rubber, in particular to a heat-resistant liquid silicone rubber material with epoxy-improved strength and interface bonding performance. Background technique [0002] Silicone rubber is a linear type in which the main chain is composed of silicon-oxygen bonds (Si-O) alternately, and organic groups (such as methyl, ethyl, vinyl, phenyl, trifluoropropyl, etc.) form its side groups. polyorganosiloxane. Due to the particularity of structure and composition, silicone rubber materials combine the characteristics and functions of inorganic and organic substances, and have excellent properties that many other materials cannot have at the same time, such as excellent high and low temperature resistance, excellent oil resistance, solvent resistance, UV resistance, radiation resistance, good aging resistance, excellent electrical insulation and chemical stability and physiological inertness, etc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L83/07C08L63/00C08L83/05
CPCC08L83/04C08L2201/08C08L2205/025C08L2205/03C08L63/00
Inventor 邹华维张斌陈洋梁梅
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com