A salt-storage slow-release snow-melting and deicing agent and preparation method thereof

A slow-release, deicing agent technology, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of limited release and long release time of snow-melting agents, and achieve the effect of prolonging the release time and good ice-melting effect.

Active Publication Date: 2021-02-26
CHONGQING JIAOTONG UNIVERSITY +1
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the above-mentioned deficiencies in the prior art, the object of the present invention is to provide a salt-storage slow-release snow-melting and de-icing agent that is not limited by temperature-controlled molecules, has a long release time, and improves the amount of ice-melting and its preparation method, which solves the problem of The problem that the release of existing deicing agents is limited by temperature-controlled molecules

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A salt-storage slow-release snow-melting and deicing agent and preparation method thereof
  • A salt-storage slow-release snow-melting and deicing agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A salt-storage slow-release snowmelting and deicing agent, comprising the following ingredients: 128g of slow-release inorganic salts, 33g of isopropanol and 40g of polymer monomers in the encapsulating polymer; Calcium chloride saturated solution 120g, 8g diatomaceous earth, 0.8g nano silicon dioxide, 3.8g OP-10 and 180mL absolute ethanol; the encapsulation polymer includes 1g acrylic acid, 18g methyl acrylate, 14g butyl acrylate, 7g styrene , 1gKH570, 0.8gAIBN, 2g isopropanol, 2g triethylamine and 5g water.

[0027] The preparation method of the salt-storage slow-release snow melting and deicing agent comprises the following steps:

[0028] (1) prepare 120g antifreezing calcium chloride saturated solution;

[0029] (2) Dissolve 8g of diatomite, 0.8g of nano-silica, and 3.8g of OP-10 in a flask previously filled with 180mL of absolute ethanol, and place the flask in a 60°C water bath with a polytetrafluoroethylene stirring rod Stir evenly to obtain a diatomite suspen...

Embodiment 2

[0034]A salt-storage slow-release snow-melting and deicing agent, comprising the following ingredients: 175g of slow-release inorganic salts, 65g of propylene glycol methyl ether and 50g of polymer monomers in the encapsulating polymer; Sodium chloride saturated solution 136g, 10g diatomaceous earth, 1.2g nano silicon dioxide, 4.3gOP-10 and 220mL absolute ethanol; The said wrapping polymer comprises 1.5g acrylic acid, 22g methyl acrylate, 18g butyl acrylate, 8.5g Styrene, 2g KH570, 1.3g AIBN, 65g propylene glycol methyl ether, 3g triethylamine and 10g water.

[0035] The preparation method of the salt-storage slow-release snow melting and deicing agent comprises the following steps:

[0036] (1) prepare 136g antifreezing sodium chloride saturated solution;

[0037] (2) Dissolve 10g of diatomite, 1.2g of nano-silica, and 4.3g of OP-10 in a flask previously filled with 220mL of absolute ethanol, and place the flask in a 60°C water bath with a Teflon stirring rod Stir evenly to...

Embodiment 3

[0042] A salt-storage slow-release snowmelting and deicing agent, comprising the following ingredients: 158.2g of slow-release inorganic salts, 45.2g of isopropanol and 45.2g of polymer monomers in the encapsulating polymer; the slow-release inorganic salts include anti- 110g of frozen magnesium chloride saturated solution, 9g of diatomaceous earth, 1g of nano-silica, 4g of OP-13 and 200mL of absolute ethanol; , 1.5g KH570, 0.9g AIBN, 2.5g isopropanol, 2.5g triethylamine and 7.5g water.

[0043] The preparation method of the salt-storage slow-release snow melting and deicing agent comprises the following steps:

[0044] (1) prepare 110g antifreeze magnesium chloride saturated solution;

[0045] (2) Dissolve 9g of diatomite, 1g of nano-silica, and 4g of OP-13 in a flask previously filled with 200mL of absolute ethanol, and place the flask in a 60°C water bath and stir evenly with a Teflon stirring rod , to obtain a diatomite suspension modified by nano-silica;

[0046] (3) t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a salt-storage slow-release snow-melting and deicing agent and a preparation method thereof, comprising the following steps: firstly preparing a saturated solution of anti-coagulation glacial chloride salt and a suspension of diatomite modified by nano-silica, and then adding the anti-freeze The saturated solution of glacial chloride salt is added dropwise to the diatomite suspension modified by nano-silica, stirred, vacuum filtered, dried, and pulverized to obtain a slow-release inorganic salt; the polymer monomer solution is then prepared, and finally the slow-release Release inorganic salt, isopropanol or propylene glycol methyl ether solution into the flask, put the flask in an oil bath and stir evenly, then add the mixed solution of polymer monomer solution, KH570 and gAIBN to it, continue stirring, and lower the temperature , and then add triethylamine into the flask, stir, and then add water to obtain the salt-storage slow-release snow-melting and deicing agent. The snow-melting substance in the salt-storage slow-release snow-melting and deicing agent prepared by the invention is not limited by temperature-controlling molecules, and the snow-melting substance releases for a long time and has a high melting ice amount.

Description

technical field [0001] The invention belongs to the technical field of road materials, in particular to a salt-storage slow-release snow-melting and deicing agent and a preparation method thereof. Background technique [0002] my country's road network is huge, most of which are located in snow-prone areas. The snow and ice on the road surface in winter greatly reduces the adhesion coefficient of the road surface, which seriously affects the smooth flow of the road and causes traffic safety accidents. The traditional methods of snow melting and deicing include manual mechanical removal method and spraying deicing agent method. However, the artificial mechanical removal method is expensive to remove snow and ice, and the deicing rate is low; the method of spreading deicing agent will cause serious pollution to the environment and corrode the road. . Therefore, the adoption of active, long-term, safe and environmentally friendly snow and ice removal technology will become an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K3/18
CPCC09K3/185
Inventor 郭鹏冯云霞李正强孟建玮魏琳王一村陈秀谨王成符世辉孙易男尹红飞肖振涛杨俊芳高云
Owner CHONGQING JIAOTONG UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com