Fabricated building sleeve connecting grouting material based on phosphorus and magnesium materials and construction method of grouting material

A sleeve connection and grouting material technology, which is applied in the direction of construction, building components, building structures, etc., to achieve the effects of improving work performance, reducing consumption, increasing bulk density and compressive strength

Inactive Publication Date: 2018-12-07
GUIZHOU PHOSPHORUS MAGNESIUM MATERIAL CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are no relevant literature reports on the application of magnesium phosphate cement on the prefabricated building sleeve connection grouting material and how to construct it. In order to solve the above problems, the inventor has carried out further research on magnesium phosphate cement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fabricated building sleeve connecting grouting material based on phosphorus and magnesium materials and construction method of grouting material
  • Fabricated building sleeve connecting grouting material based on phosphorus and magnesium materials and construction method of grouting material
  • Fabricated building sleeve connecting grouting material based on phosphorus and magnesium materials and construction method of grouting material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A prefabricated construction sleeve connection grouting material based on phosphorus and magnesium materials is prepared from the following raw materials in parts by weight: 80 parts of magnesium phosphate cement, 3 parts of admixture, 10 parts of admixture, and 1 part of aggregate.

[0047] Further, the magnesium phosphate cement is a mixture of dead-burned magnesia and monoammonium phosphate, and the ratio of dead-burned magnesia and monoammonium phosphate is 4:1; It is obtained by grinding after calcining, its magnesium oxide content is 88%, and its fineness is 60 mesh; the fineness of the monoammonium phosphate is 60 mesh, and its nutrient content is 72%; The mixture of water reducer and water reducer; the defoamer is a silicone powder defoamer; The fineness is 60 mesh; the admixture is a mixture of fly ash and metakaolin; the fineness of the fly ash is 300 mesh; the metakaolin has been calcined above 800°C, and the fineness is 800 mesh; The above-mentioned aggrega...

Embodiment 2

[0055] A prefabricated construction sleeve connection grouting material based on phosphorus and magnesium materials is made of the following raw materials in parts by weight: 120 parts of magnesium phosphate cement, 16 parts of admixture, 25 parts of admixture, and 130 parts of aggregate.

[0056] Further, the magnesium phosphate cement is a mixture of dead-burned magnesia and monoammonium phosphate, and the ratio of dead-burned magnesia and monoammonium phosphate is 1:1; It is obtained by grinding after calcining, its magnesium oxide content is 95%, and its fineness is 400 mesh; the fineness of the monoammonium phosphate is 400 mesh, and its nutrient content is 60%; The mixture of water reducer and water reducer; the defoamer is a silicone powder defoamer; the retarder is borax, and the purity of the retarder is not less than 95%, fine The fineness is 400 mesh; the admixture is a mixture of fly ash and metakaolin; the fineness of the fly ash is 2000 mesh; the metakaolin has b...

Embodiment 3

[0064] A prefabricated building sleeve connection grouting material based on phosphorus magnesium material is made of the following raw materials in parts by weight: 90 parts of magnesium phosphate cement, 6 parts of admixture, 13 parts of admixture, and 10 parts of aggregate.

[0065] Further, the magnesium phosphate cement is a mixture of dead-burned magnesia and monoammonium phosphate, and the ratio of dead-burned magnesia and monoammonium phosphate is 3.5:1; It is obtained by grinding after calcining, its magnesium oxide content is 89%, and its fineness is 100 mesh; the fineness of the monoammonium phosphate is 100 mesh, and its nutrient content is 60%; The mixture of water reducer and water reducer; the defoamer is a silicone powder defoamer; the retarder is borax, and the purity of the retarder is not less than 95%, fine The fineness is 100 mesh; the admixture is a mixture of fly ash and metakaolin; the fineness of the fly ash is 400 mesh; the metakaolin has been calcine...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
compressive strengthaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fabricated building sleeve connecting grouting material based on phosphorus and magnesium materials and a construction method of the grouting material. The grouting materialis prepared from the following raw materials in parts by weight: 80-120 parts of magnesium phosphate cement, 3-16 parts of an additive, 10-25 parts of an admixture and 0-130 parts of aggregates. The phosphorus-magnesium grouting material has good corrosion resistance and freeze thawing resistance, good durability and fluidity, low contractibility, good steel adhesion, strong self-compaction property and environment temperature adaptability, is easy for pouring and can be used for construction at any time; an oxide film can be formed on the surface of the grouting material, has very good associativity and high bonding strength and has good attachment property with sleeves and steel bars; the grouting material can be mixed on site and convenient to construct, the construction procedure is simplified, the grouting material can be condensed and hardened after 10-30 minutes of the grouting, the compressive strength of the phosphorus-magnesium grouting material can reach over 40MPa after 1.5hours of the grouting, and the phosphorus-magnesium grouting material basically does not need to be maintained, so that the construction efficiency is improved, the construction period is greatly shortened, and the cost is saved.

Description

technical field [0001] The invention belongs to the technical field of prefabricated building structures, and in particular relates to a prefabricated building sleeve connection grouting material based on phosphorus and magnesium materials and a construction method. Background technique [0002] With the continuous acceleration of the urbanization process in our country, in order to realize the sustainable and healthy development of urban and rural construction, it is proposed to change the mode of urban and rural construction, promote the transformation and upgrading of the construction industry, and vigorously promote "construction industrialization" as one of the top tasks. Moreover, urban land is becoming more and more tense, and construction sites are often very narrow, especially as people's awareness of environmental protection gradually increases, prefabricated buildings have gradually developed. [0003] Sleeve grouting connection is a steel bar connection method th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/34E04C5/16C04B111/70
CPCC04B28/34C04B2111/70C04B2201/50E04C5/162C04B14/304C04B22/16C04B24/42C04B22/0013C04B14/106C04B18/08C04B14/02C04B2103/302
Inventor 刘荣周永勤陈先勇邓玲夕杨庆锋刘俊才谭万燕
Owner GUIZHOU PHOSPHORUS MAGNESIUM MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com