Preparation method of high-fireproof composite color steel tile

A color steel tile, refractory technology, applied in fireproof coatings, devices for coating liquid on the surface, coatings, etc., can solve the problems of color steel tile deformation, steel plate deformation, etc., to avoid deformation problems, good fire resistance and heat insulation effect of effect

Active Publication Date: 2018-12-04
安徽成龙塑业科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Based on the applicant's research on the heat resistance of color steel tiles in this case, when the color steel tiles are heated, due to excessive heat transfer to the color steel tile body, that is, the steel plate, the steel plate is deformed; Brushing to form a layer of heat insulation and fire prevention cannot effectively solve the problem of deformation of color steel tiles that have been baked at high temperatures for a long time during a fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-fireproof composite color steel tile
  • Preparation method of high-fireproof composite color steel tile

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] The invention provides a method for preparing a composite color steel tile with high fire resistance, which comprises the following steps:

[0018] (1) Preliminary treatment of the color steel tile body, that is, cold-rolled steel plate or galvanized steel plate, including removing oil, dust and debris;

[0019] (2) Preparation of thermal conductive layer paint: Weigh the raw materials according to the formula, disperse graphene oxide powder and alumina powder into the high temperature resistant adhesive, stir evenly and spray on the color steel tile body of step (1), and then dry it. After drying, a heat-conducting layer is formed, and the two sides of the color steel tile body are respectively processed to obtain a semi-finished product A with heat-conducting layers on both sides;

[0020] Open through holes on the semi-finished product A, the diameter of the through holes is 0.8-1.5cm; the spacing of the through holes is 2-5cm; and then use a forming machine to form corruga...

Embodiment 1

[0046] A composite color steel tile, comprising a color steel tile body and a heat-conducting layer arranged on both sides of the color steel tile body, the outer side of the heat-conducting layer is provided with a refractory layer, and the outer side of the refractory layer is provided with a topcoat layer;

[0047] The refractory layer comprises the following raw materials prepared by weight: 55 parts of clay, 4 parts of corundum powder, 3 parts of alumina powder, 15 parts of silica powder, 20 parts of yellow dextrin, and 110 parts of water; the thickness of the refractory layer is 5mm ;

[0048] The particle size of the clay and silica powder is below 3mm;

[0049] The particle size of the corundum powder and alumina powder are both below 2mm;

[0050] The heat-conducting layer includes the following raw materials prepared in parts by weight: 60 parts of high-temperature resistant adhesive, 5 parts of graphene oxide powder, and 3 parts of alumina powder; the thickness of the heat-...

Embodiment 2

[0060] This embodiment is according to the preparation method of the composite color steel tile of embodiment 1, the difference is:

[0061] The refractory layer is prepared with the following raw materials in parts by weight: 50 parts of clay, 3 parts of corundum powder, 2 parts of alumina powder, 13 parts of silica powder, 15 parts of yellow dextrin, and 100 parts of water; the rest remain unchanged to obtain a composite color Steel tile.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of processing of color steel tiles and particularly relates to a preparation method of a high-fireproof composite color steel tile. The method includes (1)pretreating a color steel tile body; (2) preparing a heat conductive layer coating, and coating the color steel tile body with the coating to obtain a semi-product A, and forming through holes in andshaping corrugated structures on the semi-product A; (3) forming fireproof layers to prepare a semi-product B; (4) forming a surface paint layer to produce the composite color steel tile. By arranging the heat conductive layers on two sides of the color steel tile and the fireproof layers on outer sides of the heat conductive layers, when fire hazard breaks out, fireproof layers have great fireproof and heat-insulation effect during use. In addition, the heat transmitted to the color steel tile body can be dissipated via the heat conductive layers in order to prevent deformation due to concentrated heat.

Description

Technical field [0001] The invention belongs to the technical field of color steel tile processing, and specifically relates to a method for preparing a composite color steel tile with high fire resistance. Background technique [0002] Color steel tile, also known as color profiled tile, is a profiled plate that uses color coated steel plate and is rolled into various wave shapes. The color coated steel sheet used to manufacture color steel tiles is usually cold rolled steel sheet or galvanized steel sheet, which is made by applying organic film such as roll coating or compounding PVC on the surface of the steel sheet after chemical treatment and baking and curing Into steel products. Color coated steel plate not only has the properties of high mechanical strength and easy forming of steel materials, but also has good decoration and corrosion resistance of coating materials. It is suitable for roofing, wall and interior and exterior wall decoration of industrial and civil buil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D201/00C09D7/61C09D5/18C09D103/02C09D133/00B05D3/00B05D1/02B05D3/02B05D7/24
CPCB05D1/02B05D3/002B05D3/0254B05D7/24C08K2003/2227C08K2003/2241C08K2201/014C09D5/18C09D103/02C09D133/00C09D201/00C09D7/61C08K3/042C08K3/22C08K3/346C08K3/36
Inventor 靳南南
Owner 安徽成龙塑业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap