Composite waterproof structure and preparation method thereof

A technology of structure and waterproof membrane layer, applied in the direction of building structure, chemical instruments and methods, building components, etc., can solve the problems of delamination of paint and membrane, difficulty in ensuring waterproof quality, etc., and achieve the effect of improving compatibility

Active Publication Date: 2018-11-23
四川省威盾新材料有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the above-mentioned problems that delamination of the coating and the coiled material will occur and it is difficult to ensure the waterproof quality, the present invention proposes a composite waterproof structure and a preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite waterproof structure and preparation method thereof
  • Composite waterproof structure and preparation method thereof
  • Composite waterproof structure and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Such as figure 1 and figure 2As shown, a composite waterproof structure, from top to bottom is a waterproof coiled material layer 1, a reactive polymer elastic coating layer 2 and a waterproof base layer 3; the waterproof coiled material layer 1 is an upper surface layer from top to bottom 11 and a self-adhesive material layer 12, the upper surface layer 11 is a strong cross film layer formed by two layers of high-strength PE film crossed at an angle of 45 degrees, the self-adhesive layer 12 is a self-adhesive polymer modified asphalt, the The self-adhesive polymer modified asphalt comprises the following raw materials in parts by weight: 1 part of SBS modifier, 1 part of SBR modifier, 20 parts of naphthenic oil, and 100 parts of asphalt prepolymer;

[0036] The reactive polymer elastic coating includes component A and component B, the weight ratio of component A and component B is 1:1, and the component A includes the following raw materials in parts by weight: polye...

Embodiment 2

[0046] A composite waterproof structure, from top to bottom is a waterproof coiled material layer, a reactive polymer elastic coating layer and a waterproof base layer; the waterproof coiled material layer is an upper surface layer and a self-adhesive material layer from top to bottom, so The upper surface layer is a strong cross film layer formed by two layers of high-strength PE film obliquely crossing at 45 degrees. The self-adhesive layer is a self-adhesive polymer modified asphalt, and the self-adhesive polymer modified asphalt includes the following parts by weight The number of raw materials: 1 part of SBS modifier, 2 parts of SBR modifier, 10 parts of naphthenic oil, 90 parts of asphalt prepolymer;

[0047] The reactive polymer elastic coating includes component A and component B, the weight ratio of component A and component B is 1:2, and the component A includes the following raw materials in parts by weight: polyether 2000 50 Parts, 50 parts of asphalt prepolymer, 2...

Embodiment 3

[0056] A composite waterproof structure, from top to bottom is a waterproof coiled material layer, a reactive polymer elastic coating layer and a waterproof base layer; the waterproof coiled material layer is an upper surface layer and a self-adhesive material layer from top to bottom, so The upper surface layer is a strong cross film layer formed by two layers of high-strength PE film obliquely crossing at 45 degrees. The self-adhesive layer is a self-adhesive polymer modified asphalt, and the self-adhesive polymer modified asphalt includes the following parts by weight The number of raw materials: 2 parts of SBS modifier, 1 part of SBR modifier, 15 parts of naphthenic oil, 95 parts of asphalt prepolymer;

[0057] The reactive polymer elastic coating includes component A and component B, the weight ratio of component A and component B is 1:1.5, and the component A includes the following raw materials in parts by weight: polyether 2000 40 40 parts of asphalt prepolymer, 17 par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
penetrationaaaaaaaaaa
Functional group degreeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite waterproof structure and a preparation method thereof, and belongs to the field of building waterproof materials. The composite waterproof structure is prepared from a waterproof coil layer, a reaction type macromolecular elastic coating layer and a waterproof base layer in turn from top to bottom, wherein the waterproof coil layer is prepared from an upper surface layer and a self-sticking material layer in turn from top to bottom; the self-sticking layer is self-sticking polymer modified asphalt. According to the composite waterproof structure and the preparation method thereof disclosed by the invention, separation between the coating and the coil is avoided, and the waterproof effect is perfect.

Description

technical field [0001] The invention belongs to the field of building waterproof materials, and in particular relates to a composite waterproof structure and a preparation method. Background technique [0002] With the development and progress of modern society, waterproofing occupies an increasingly important position in the modern construction industry and has become an important factor affecting people's work and life. In order to solve the problems and defects caused by using waterproof coatings or coils alone, people began to combine coatings and coils to form a composite waterproof system. Nowadays, the more popular non-curing composite waterproof system will delaminate from the coating and the membrane as time goes by, making it difficult to guarantee the waterproof quality. Contents of the invention [0003] In order to solve the above-mentioned problems of delamination of the paint and the coiled material and difficulty in ensuring waterproof quality, the present...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/06B32B27/32B32B7/10B32B11/04B32B33/00B32B37/00B32B37/24C08L95/00C08L53/02C08L9/06C08L91/00C09D175/08C09D195/00C09D7/61C09D7/63C09D7/65
CPCB32B7/10B32B11/04B32B11/046B32B27/08B32B27/32B32B33/00B32B37/00B32B37/24B32B2037/243B32B2255/20B32B2255/24B32B2255/26B32B2307/308B32B2307/5825B32B2307/7265B32B2307/734C08L95/00C08L2205/035C09D7/61C09D7/63C09D7/65C09D175/08C09D195/00C08L53/02C08L9/06C08L91/00C08L91/06C08K13/02C08K3/34C08K5/12C08L75/08
Inventor 李雷刘勇樊军金永峰胡蔚儒丁海涛刘亚妮郑伦李尚臻
Owner 四川省威盾新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com