PVC separation wall composite board and preparation method thereof

A composite board and stone-plastic technology, which is applied in the field of building wall panels, can solve the problems of rubber damage and reduce the heat insulation effect, and achieve the effects of strong acid and alkali resistance, resource saving, and easy processing and molding.

Inactive Publication Date: 2018-11-13
浙江雄冉装饰材料有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the addition of neoprene and nitrile rubber to the above-mentioned stone-plastic board will cause damage to the rubber during the rolling process of the stone-plastic board at 140 ° C. At the same time, rubber as the main component will reduce its heat insulation effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] Corresponding to the formula of the above-mentioned stone-plastic partition wall composite board, the preparation method of the composite board is adjusted, and the preparation method comprises the following steps:

[0027] S1. Put PVC resin, nano-calcium, and heavy calcium powder into the mixer according to the formula ratio, control the stirring speed at 800-1400r / min, control the time at 4-8min, and control the temperature at 60-80°C;

[0028] S2, then import the mixture obtained in step S1 into the internal mixer, and simultaneously put the anti-shock agent, calcium zinc stabilizer, paraffin, and stearic acid into the internal mixer, and control the temperature of the internal mixer at 140-150°C;

[0029] S3, then import the mixture obtained in step S2 into the screw extruder, and then enter the die head with the specification of the composite plate after passing through the screw feeding section, the melting section and the homogenizing section successively, wherein...

Embodiment 1

[0032] The formula of the stone-plastic partition wall composite board includes at least the following ingredients: PVC resin, nano-calcium, heavy calcium powder, ACR, calcium-zinc stabilizer, paraffin, stearic acid, and the weight ratio of the above-mentioned ingredients is 70:40:20 according to the formula: 4:2.5:1:2.

[0033] Corresponding to the formula of the above-mentioned stone-plastic partition wall composite board, the preparation method of the composite board is adjusted, and the preparation method comprises the following steps:

[0034] S1. Put PVC resin, nano-calcium, and heavy calcium powder into the mixer according to the formula ratio, control the stirring speed at 1400r / min, control the time at 6min, and control the temperature at 60°C;

[0035] S2, then import the mixture obtained in the S1 step into the internal mixer, and simultaneously enter the anti-impact agent, calcium zinc stabilizer, paraffin, and stearic acid into the internal mixer, and the temperat...

Embodiment 2

[0039] The formula of stone-plastic partition wall composite board includes at least the following ingredients: PVC resin, nano-calcium, heavy calcium powder, ACR, CPE, calcium-zinc stabilizer, paraffin, stearic acid, and the weight ratio of the above-mentioned ingredients is 30:60 according to the formula: 0:4:2:2.5:1:2.

[0040] Corresponding to the formula of the above-mentioned stone-plastic partition wall composite board, the preparation method of the composite board is adjusted, and the preparation method comprises the following steps:

[0041] S1. Put PVC resin, nano-calcium, and heavy calcium powder into the mixer according to the formula ratio, control the stirring speed at 1300r / min, control the time at 7min, and control the temperature at 75°C;

[0042] S2, then import the mixture obtained in the S1 step into the internal mixer, and simultaneously enter the anti-impact agent, calcium zinc stabilizer, paraffin, and stearic acid into the internal mixer, and the temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Bending strengthaaaaaaaaaa
Tear strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a formula of a PVC separation wall composite board which comprises at least following ingredients: PVC resin, nano-calcium, calcium carbonate, an impact modifier, a calcium-zinc stabilizer, paraffin and stearic acid, and the weight ratio of the ingredients according to the formula is (30-70):(0-70):(0-70):(3-9):(1-5):(1-2):(1-6). According to the PVC separation wall composite board, the PVC main raw material is used, the material is easy to process and shape, the manufacturing cost is low, at the same time, the nano-calcium and / or calcium carbonate are / is added in the PVC main raw material, not only is the product volume increased, but also the cost is reduced; meanwhile, the impact modifier, the calcium-zinc stabilizer, the paraffin and the stearic acid are added to regulate the performance of the composite board, and the mechanical performance, the stability and the demolding effect of the composite board are enhanced; the preparation method of the composite board and the formula are in mutual combination in the production process, the production processes are regulated, no environment pollution is produced while the production efficiency is improved, andthe product yield is controlled.

Description

technical field [0001] The invention relates to the field of building wallboards, in particular to a stone-plastic partition wall composite board and a preparation method thereof. Background technique [0002] At present, the traditional red brick is still used as the main wall structure in the construction industry, but due to policy reasons, the red brick will withdraw from the construction market. Therefore, new wall material technologies continue to emerge to meet the new needs of the construction market. At present, in addition to clay bricks, there are also industrial waste slag block bricks, silicate and sulphoaluminate cement wallboards, etc. for building wall materials. The traditional clay solid brick, because of its serious waste of land resources, serious energy consumption, and serious pollution of the environment, at the same time, the construction project is not energy-saving, the construction labor intensity is high, the construction cost is high, the speed i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L91/06C08L33/04C08L23/28C08K3/26C08K5/09C08K13/02B29C47/92B29C48/92
CPCC08K2003/265C08K2201/011C08K2201/014C08L27/06C08L2205/03C08L91/06C08L33/04C08L23/286C08K3/26C08K5/09C08K13/02
Inventor 徐江娥
Owner 浙江雄冉装饰材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com